耐候钢S355J2W的研发和工艺实践

特殊钢 ›› 2014, Vol. 35 ›› Issue (1): 43-45.

耐候钢S355J2W的研发和工艺实践

栾文林¹，刘志远¹，赵定国²

1河北钢铁集团唐钢中厚板公司，唐山063000；
2河北联合大学冶金与能源学院，唐山063009

收稿日期:2013-09-04 出版日期:2014-02-01 发布日期:2022-09-06
作者简介:栾文林(1982-)，男，硕士(河北理工大学)，工程师,2005年河北理工大学(本科)毕业，炼钢新技术研究。
基金资助:
河北省自然科学基金项目资助(E2013209113)

Development and Process Practice of Weathering Steel S355J2W

Lu an Wenlin¹ , Liu Zhiyuan¹ ，Zhao Dingguo²

1 Tangshan Heavy Plate Co Ltd, Hebei iron and Steel Group, Tangshan 063000；
2 College of Metallurgy and Energy, Hebei United University, Tangshan 063009

Received:2013-09-04 Published:2014-02-01 Online:2022-09-06

摘要/Abstract

摘要： 研发的耐候钢S355J2W(/%:0.06~0.10C,0.20~0.40Si,1.00~1.30Mn,≤0.008S,≤0.020P,0.25~0.40Cu,0.30~0.55Cr,0.10~0.30Ni,0.020~0.040Nb,0.020~0.050Alt)的试生产流程为铁水-120 t顶底复吹转炉-LF-250 mm×2 000 mm板坯连铸-轧制≤16 mm板。通过采取控制转炉终点[C]≤0.05%,[P]≤0.015%,精炼时(FeO)+(MnO)≤1.5%,(SiO2)≤15%,精炼渣碱度≥3.0,[Al]s≥0.025%,按Ca/Al=0.06~0.12,喂入钙线,连铸时采用耐候钢专用保护渣[主要成分/%:34.0CaO,28.0SiO₂,4.6Al₂O₃,≤6(Li₂O+B₂O₃)],控制开坯温度1 010~1 060℃等工艺措施,≤16 mm耐候钢S355J2W成品板铝含量为0.025%~0.035%,钢中平均氧含量为21×10^-6,平均氮含量为31×10^-6,钢中非金属夹杂物的尺寸基本≤14μm,各项冶金质量指标合乎要求。

关键词: 耐候钢S355J2W, 120 t BOF-LF-板坯CC流程, 研发, 工艺实践

Abstract: The pilot production flow sheet for developed weathering steel S355J2W (/% : 0.06 ~ 0. 10C, 0.20 ~ 0.40Si, 1.00-1. 30Mn, ≤0.008S, ≤0.020P, 0.25 〜0.40Cu, 0.30 ~ 0. 55Cr, 0.10 〜0. 30Ni, 0. 020 ~ 0. 040Nb, 0. 020 ~ 0. 050Alt) is hot metal-120 t top and bottom combined blown converter-LF-250 mm x2 000 mm slab CC-≤16 mm plate rolling process. With using the process measures including controlling converter end [ C] ≤0.05% and [P] ≤0. 015%, in refining ( FeO) + ( MnO)≤1. 5%, ( SiO₂) ≤15%, refining slag basicity ≥3. 0, [Al]s ≥0.025% and feeding calcium wire according to Ca/Al = 0. 06 〜0. 12, in casting using special-purpose mold shielding flux for weathering steel [main ingredient/%: 34.0CaO, 28.0SiO₂, 4.6Al₂O₃, ≤6 ( Li₂O+ B₂O₃)], controlling breakdown temperature 1 010 ~ 1 060℃, the aluminium content in ≤16 mm finished plate of weathering steel is 0. 025% ~0. 035%, the average oxygen content in steel is 21 x 10^-6 and the average nitrogen content in steel is 31 x 10^-6, the size of nonmetallic inclusions in steel normally ≤14μm, and each metallurgy quality index meets the requirement of standard.

栾文林, 刘志远, 赵定国. 耐候钢S355J2W的研发和工艺实践[J]. 特殊钢, 2014, 35(1): 43-45.

Lu an Wenlin , Liu Zhiyuan, Zhao Dingguo. Development and Process Practice of Weathering Steel S355J2W[J]. Special Steel, 2014, 35(1): 43-45.

[1]	韩常海, 王志利, 施进卿. 胀断连杆用非调质钢C70S6BY产品研发[J]. 特殊钢, 2021, 42(6): 55-57.
[2]	郭键, 和红杰, 韩清连, 卢登攀. 中间包双挡渣墙对冷镦钢Q10B21-C夹杂物去除工艺实践[J]. 特殊钢, 2020, 41(5): 34-37.
[3]	王春梅, 黄永建, 李双江. 300 mm x360 mm连铸坯生产Φ80 mm非调质钢38MnVS6工艺实践[J]. 特殊钢, 2019, 40(5): 21-23.
[4]	王之香, 高建兵, 王玉玲, 王育田, 张锦文. 时速350 km中国标准动车组车轴用钢DZ2的生产工艺实践[J]. 特殊钢, 2019, 40(1): 19-22.
[5]	高菊, 丁志军, 李辉. 提高齿轮钢8620RH( K)末端淬火内控符合率的工艺实践[J]. 特殊钢, 2018, 39(5): 28-31.
[6]	丰年. 120t BOF-LF-VD-CC流程生产磨球钢B2的工艺实践[J]. 特殊钢, 2018, 39(2): 17-20.
[7]	宋延成, 刘吉刚. 150t转炉脱磷炉渣控制工艺的实践[J]. 特殊钢, 2018, 39(1): 44-47.
[8]	陈均, 江南红, 龚洪君, 张彦恒, 曾建华. 200t顶底复吹转炉半钢冶炼深脱磷工艺实践[J]. 特殊钢, 2017, 38(6): 40-44.
[9]	万长杰, 申丽娟, 刘梅, 赵天力. 高碳微合金非调质钢C70S6的开发和工艺实践[J]. 特殊钢, 2017, 38(5): 31-33.
[10]	冯文甫, 郭键, 叶凡新, 曹红波, 陈月光. 60t AOD兑脱磷铁水一步法冶炼0Crl2Mnl5NiCuN不锈钢的工艺实践[J]. 特殊钢, 2017, 38(4): 35-37.
[11]	祁庆花, 赵子文, 韩文科, 杨德生. 30t EAF-LF-VD-13t 铸锭流程生产14Cr1Mo钢的工艺实践[J]. 特殊钢, 2017, 38(2): 19-22.
[12]	叶凡新, 冯文甫, 郭志彬, 王晓亮, 曹红波, 吴广海. 60t AOD-LF-CCM 流程冶炼清洁球用超低[C+N]不锈钢0Cr13的工艺实践[J]. 特殊钢, 2017, 38(2): 23-25.
[13]	叶凡新, 冯文甫, 郭志彬, 王晓亮, 曹红波, 吴广海. 60 t AOD全铁水精炼400系不锈钢热补偿技术的工艺实践[J]. 特殊钢, 2016, 37(6): 44-46.
[14]	张振申, 程官江, 王新志, 王中岐, 夏志升. 超低碳钢150 t转炉冶炼过程超低硫的控制和工艺实践[J]. 特殊钢, 2016, 37(6): 47-51.
[15]	李永超, 陈继林, 郭明仪, . 高强度螺栓用QB30冷镦钢盘条的研发与生产[J]. 特殊钢, 2016, 37(4): 33-36.