冷却速率对M2高速工具钢铸锭凝固组织的影响

特殊钢 ›› 2014, Vol. 35 ›› Issue (3): 45-48.

冷却速率对M2高速工具钢铸锭凝固组织的影响

赵志刚^1,2，颜慧成²，仇圣桃²，朱荣¹

1北京科技大学冶金与生态工程学院，北京100083 ；
2钢铁研究总院连铸技术国家工程研究中心，北京100081

收稿日期:2013-12-04 出版日期:2014-06-01 发布日期:2022-08-30
作者简介:赵志刚(1985-),男，博士研究生(钢铁研究总院),2009年昆明理工大学(本科)毕业,工模具钢连铸研究。

Effect of Cooling Rate on Solidification Structure of M2 High Speed Tool Steel Ingot

Zhao Zhigang^1,2, Yan Huicheng², Qiu Shengtao²，Zhurong¹

1 School of Metallurgical and Ecological Engineering, University of Science and Technology, Beijing 100083 ；
2 National Engineering Research Center of Continuous Casting Technology, Central Iron and Steel Research Institute, Beijing 100081

Received:2013-12-04 Published:2014-06-01 Online:2022-08-30

摘要/Abstract

摘要： 试验M2钢(/%:0.81C,0.31Si,0.33Mn,4.01Cr,4.57Mo,5.71W,1.77V)由实验室25 kg高频真空感应炉熔炼,并浇铸成横截面50 mm×100 mm钢锭。研究了水冷铜模和铸铁模浇铸的M2钢的低倍组织、晶粒尺寸和碳化物分布。结果表明,快速冷却可有效控制和消除M2钢铸锭中的柱状晶,随着冷却速率增大,M2钢铸锭部分气泡上浮不完全,但中心缩孔显著减小,晶粒更细小且分布更均匀,碳化物更加弥散且细小;铸铁模锭边缘和中心部分的晶粒尺寸分别为40~57μm用和55~62μm,而水冷铜模锭边缘和中心部分的晶粒尺寸分别为30~40μm和50μm。

关键词: M2高速工具钢, 冷却速率, 凝固, 低倍, 晶粒尺寸, 碳化物

Abstract: The test M2 steel (/%: 0. 81C, 0. 31 Si, 0. 33Mn, 4. 01 Cr, 4.57Mo, 5. 71W, 1. 77V) is melted by a 25 kg high-frequency induction furnace and cast to cross section 50 mm X 100 mm ingots in laboratory. The macro-structure, grain size and distribution of carbides of M2 steel ingot casting by water-cooling copper mould and cast-iron mould are studied. Results show that higher cooling rate is available to control and eliminate the columnar crystal in ingot of M2 steel; with increasing the cooling rate the partial bubbles in M2 steel ingot float off incompletely but the central shrinkage of ingot decreases significantly, the grains are fine and uniform distribution, and the carbides in steel are more dispersed and fine ； the grain size at edge and center of ingot with cast iron mould process are respectively 40 ~ 57 μm and 55 ~ 62 μm and that with water-cooling copper mould process are respectively 30-40 μm and 50 μm.

赵志刚, 颜慧成, 仇圣桃, 朱荣. 冷却速率对M2高速工具钢铸锭凝固组织的影响[J]. 特殊钢, 2014, 35(3): 45-48.

Zhao Zhigang, Yan Huicheng, Qiu Shengtao, Zhurong. Effect of Cooling Rate on Solidification Structure of M2 High Speed Tool Steel Ingot[J]. Special Steel, 2014, 35(3): 45-48.

参考文献

[1]邓玉昆，陈景荣,王世章.高速工具钢[M].北京:冶金工业出版社,2002:156.
[2]李正邦.发展我国高速钢的战略分析[J].特殊钢,2006,27(1) ：1-6.
[3]赵建政，贾志琦.国内外高速钢发展现状[J].科技情报开发与经济,1997(1):13-15.
[4]郭耕三.高速钢及其热处理[M].北京:机械工业出版社,1985： 265.
[5] Leskovsek V, Vie B. Improved Vacuum Heat-treatment for Fine-blanking Tools from High-speed Steel M2 [J]. Materials Processing Technology, 1998,82 ： 89-94.
[6] Bergman F, Hedenqvist P, Hogmark S. The Influence of Primary Carbides and Test Parameters on Abrasive and Erosive Wear of Selected PM High Speed Steels [J]. Tribology International, 1997 r 30(3):183-191.
[7] Shaikh Q A, Coleman D S, Bates J, et al. Wear and Microstructural Studies of Alloy Sintered Steels [J]. Journal of Materials Science & Technology, 1991,7：728-738.
[8] Dunlop G L, Wang Rong. Development of Microstructure during Heat Treatment of High-Speed Steels[Z]. Leoben: Proceeding First International HSS Conference, 1990 ： 33-40.
[9] EI-Rakayby A M,Mi Us B. On the Microstructure and Mechanical Properties of High-Speed Steels [J]. Journal of Materials Science & Technology, 1988 ：23 ：4340-4344.
[10]Ghomaschi M R,Sellar C M. Microstructural Changes in as-cast M2 Grad High Speed Steel during High Temperature Treatment [M]. Metal Science, 1984,18(1) ：44-48.
[11] Lenta E J, Twentyman M E, Pesci H. Transformation of the Primary Carbide Networks in High-speed Steels by Heat Treatment at High Temperatures[J]. Metallography, 1983,16 ：387-401.
[12]Kheirandish Sh, Mirdamadi Sh, Kharrazi Y H K. Effect of Titanium on Cast Structure of High-Speed Steels [J]. Materials Science and Technology, 1998(14) ：312-316.
[13]赵玉谦，姜启川,赵宇光，等.铝复合变质处理M2铸造高速钢的影响[J].吉林工业大学学报,1997,27(2) ：28-32.

[1]	杨文彬, 刘中秋, 王芳, 黄雪驰, 郎宇平, 李宝宽. 熔速对高填充比06Cr18Ni11Ti电渣重熔铸锭凝固过程的影响[J]. 特殊钢, 2024, 45(6): 28-36.
[2]	谢康, 莫金强, 张威, 王丽君. 稀土Ce对441铁素体不锈钢碳氮化物析出的影响与控制[J]. 特殊钢, 2024, 45(6): 1-7.
[3]	唐远寿, 张十庆, 李方, 何钦生, 赵振, 王宏, 邹兴政, 王建桥, 黄雅丽. 淬火温度对M₆C强化2 200 MPa级超高强度钢力学性能的影响[J]. 特殊钢, 2024, 45(5): 108-112.
[4]	张明. 显微组织对薄壁X65M管线钢落锤试验性能的影响[J]. 特殊钢, 2024, 45(5): 123-126.
[5]	孙佳怡, 董龙沛, 赵云松, 王恩会, 侯新梅. 镍基单晶涡轮叶片定向凝固过程温度场数值模拟研究进展[J]. 特殊钢, 2024, 45(4): 34-40.
[6]	曹玉龙, 张赛康, 汪秀秀, 马崇圣, 李光强. 加热温度对高钒高速钢中M₂C碳化物分解转变行为的影响[J]. 特殊钢, 2024, 45(4): 146-152.
[7]	孙中豪, 李强, 张明亮, 马程款, 夏志斌, 钟云波. 磁控电渣重熔对M2高速钢凝固组织及力学性能的影响[J]. 特殊钢, 2024, 45(4): 68-76.
[8]	李亚强, 李莹莹, 李川, 韩宝臣, 施进卿. 12Cr1MoV珠光体耐热钢连续冷却相变研究[J]. 特殊钢, 2024, 45(3): 85-90.
[9]	陈德, 张广军, 刘吉刚. GCr15轴承钢方坯连铸轻压下工艺优化与实践[J]. 特殊钢, 2024, 45(2): 50-55.
[10]	徐乐钱, 李朋, 刘宇, 庞于思, 罗胜平. Cr8扁钢轧制模拟与工艺优化[J]. 特殊钢, 2024, 45(2): 101-104.
[11]	杨亚倩, 邢炜伟, 丁磊磊, 马颖澈. S对铸造高温合金K417G凝固行为的影响[J]. 特殊钢, 2024, 45(2): 30-38.
[12]	郑冰, 徐东, 王怡群, 王学玺, 赵红阳, 巨东英. 34CrNi3MoV钢奥氏体晶粒长大模型验证与应用[J]. 特殊钢, 2023, 44(6): 101-106.
[13]	苏学虎. 铸造镍基合金CW12MW与CW6MC平衡凝固及析出热力学模拟[J]. 特殊钢, 2023, 44(6): 31-38.
[14]	张剑桥, 李筱, 孙铭山, 付金柱. 冷却速率对60Cr13马氏体不锈钢微观组织影响规律[J]. 特殊钢, 2023, 44(6): 112-116.
[15]	苏学虎. 铸造双相不锈钢CD3MWCuN凝固与析出热力学模拟[J]. 特殊钢, 2023, 44(4): 28-34.