连续退火温度对390 MPa级IF钢组织、织构和力学性能的影响

特殊钢 ›› 2014, Vol. 35 ›› Issue (3): 53-55.

连续退火温度对390 MPa级IF钢组织、织构和力学性能的影响

程晓杰¹，李振¹，蔡阿云¹，乔建军¹，孙建华¹，赵爱民²

1首钢冷轧薄板有限公司，北京101304；
2北京科技大学冶金工程研究院，北京100083

收稿日期:2013-12-08 出版日期:2014-06-01 发布日期:2022-09-01
作者简介:程晓杰(1983-),男，博士(北京科技大学)，工程师,2007年北京科技大学(本科)毕业，冷轧汽车板研发。
基金资助:
北京科技计划项目“首钢高品质板材的开发及其产业化"(D07010300700701)

Effect of Continuous Annealing Temperature on Structure Texture and Mechanical Properties 390 MPa IF Steel

Cheng Xioajie¹, Li Zhen¹, Cai Ayun¹, Qiao Jianjun¹, Sun Jianhua¹ ，Zhao Aimin²

1 Shougang Cold Rolling Co Ltd, Beijing 101304；
2 Metallurgical Engineering Research Institute,University of Science and Technology, Beijing 100083

Received:2013-12-08 Published:2014-06-01 Online:2022-09-01

摘要/Abstract

摘要： 试验用390 MPa级IF钢(/%:0.005C,0.04Si,0.35Mn,0.095P,0.005S,0.030Nb,0.016Ti,0.036Alt)0.8 mm冷轧板由4 mm热轧板冷轧生产。研究了连续退火温度780~820℃对该IF钢组织、织构和力学性能的影响。结果表明,当连续退火温度由780℃提高至820℃时,IF钢的屈服和抗拉强度分别由282 MPa和432 MPa降至249 MPa和405 MPa,伸长率A₅₀和塑性应变比r_m分别从37.2%和1.45提高到41.7%和1.84,具有较好的深冲性能;但随退火温度升高,平面各向异性指数△r由0.44提高到0.65,铁素体晶粒尺寸增大,组织均匀变差,同时变形织构{112}<110>变弱,有利织构{111}<110>增强,{001}<110>变弱,综合考虑退火温度控制在820℃左右为宜。

关键词: IF钢, 连续退火温度, 力学性能, 组织, 织构

Abstract: Test 0. 8 mm cold rolled sheet of 390 MPa IF steel (/%: 0. 005C, 0.04Si, 0. 35Mn, 0. 095P, 0. 005S, 0. 030Nb, 0. 016Ti, 0. 036Alt) is cold rolled by 4 mm hot rolled plate. The effect of continuous annealing temperature 780 ~ 820 °C on structure, texture and mechanical properties of the IF steel has been studied. Results show that as continuous annealing temperature increases from 780 ℃ to 820 ℃, the yield and tensile strength of the IF steel decrease respectively from 282 MPa and 432 MPa to 249 MPa and 405 MPa, and the elongation A₅₀ and plastic strain ratio r_m increase respectively from 37. 2% and 1.45 to 41. 7% and 1. 84, it has better deep drawing property while with increasing annealing temperature the plane anisotropic index △r increases from 0. 44 to 0. 65, grain size of ferrite increases， and structure homogeneity becomes poor, and deformation texture {112} < 110 > is weaker, favorable texture {111} < 110 > is enhanced, texture {001}<110> weakens, comprehensively considering, the suitable annealing temperature is about 820 ℃.

程晓杰, 李振, 蔡阿云, 乔建军, 孙建华, 赵爱民. 连续退火温度对390 MPa级IF钢组织、织构和力学性能的影响[J]. 特殊钢, 2014, 35(3): 53-55.

Cheng Xioajie, Li Zhen, Cai Ayun, Qiao Jianjun, Sun Jianhua, Zhao Aimin. Effect of Continuous Annealing Temperature on Structure Texture and Mechanical Properties 390 MPa IF Steel[J]. Special Steel, 2014, 35(3): 53-55.

参考文献

[1]康永林.现代汽车板工艺及成形理论与技术[M].北京:冶金工业出版社,2009.
[2]郭艳辉，王昭东,李守卫，等.IF钢与ELC钢织构及性能的对比[J].东北大学学报(自然科学版),2007,28(12):1713-1716.
[3] Ghosh P,Ghosh C,Ray R K,et al. Precipitation Behavior and Texture Formation at Different Stages of Processing in an Interstitial Free High Strength Steel [J]. Scripta Materialia,2008,59 ：276-278.
[4] Jeong W C. Effect of Hot-rolling Temperature on Microstructure and Texture of an Ultra-low Carbon Ti-interstitial-free Steel[J]. Materials Letters ,2008,62：91-94.
[5]李守华，李俊.汽车用高强度IF钢的研究进展[J].上海金属， 2007,29(5):66-70.
[6] Gupta A K,Kumar D R. Formability of Galvanized Interstitial-free Steel Sheets [J]. Journal of Materials Processing Technology, 2006, 172(2)：225-237.
[7] Debanshu B. Developments in Advanced High Strength Steels [J]. Iron & Steel Supplement,2005,40：69-75.
[8] Hutchinson B, Artymowicz D. Mechanisms and Modelling of Micro- structure/Texture Evolution in Interstitial Free Steel Sheets[J]. ISIJ International,2001,41 (6) ：533-537.
[9]吕庆功，陈光南,周家琮，等.深冲钢板的主要织构对塑性应变比的影响[J].钢铁研究,2000(5):40-43.
[10] Liu Y, Wang C, Jiang Q, et al. Individual Grain Orientation and Heterogeneous Deformation in Cold-deformed Interstitial-free Sheet Steel[J]. Journal of Materials Science and Technology,2007,23 (5):689-692.
[11]孙景宏.微碳深冲钢板组织演变规律和工艺优化的研究[D]. 北京:北京科技大学,2005.
[12] Wang Z,Zhang P,Guo Y,et al. Recrystallization Texture Characteristic and Drawability of a Warm Rolled and Cold Rolled Interstitial- free Steel [J]. Journal of Materials Engineering and Performance, 2006,15(6):646-650.

[1]	孟庆勇, 单庆林, 潘宏伟, 路博勋, 石晓伟, 温巨文. 高铬耐候钢Q350EW高温热塑性分析 [J]. 特殊钢, 2024, 45(6): 23-27.
[2]	张艳梅, 余海存, 仇秋玲. 固溶工艺对3Al-310S耐热钢组织和力学性能的影响[J]. 特殊钢, 2024, 45(6): 95-101.
[3]	赵广迪, 臧喜民, 刘志超, 井玉安. 淬火工艺对A514CrQ齿条钢显微组织演变及硬度的影响[J]. 特殊钢, 2024, 45(6): 73-82.
[4]	徐临超, 叶赛男, 王文权, 张新戈, 陆有, 郭威. 热处理工艺对锻造430F铁素体不锈钢组织和性能的影响[J]. 特殊钢, 2024, 45(6): 83-87.
[5]	袁麟, 胡小强, 刘洋, 李殿中, 谢晶, 陈伟. 稀土精炼与电渣重熔3%Cr轧辊钢对比分析[J]. 特殊钢, 2024, 45(5): 1-7.
[6]	唐远寿, 张十庆, 李方, 何钦生, 赵振, 王宏, 邹兴政, 王建桥, 黄雅丽. 淬火温度对M₆C强化2 200 MPa级超高强度钢力学性能的影响[J]. 特殊钢, 2024, 45(5): 108-112.
[7]	张明. 显微组织对薄壁X65M管线钢落锤试验性能的影响[J]. 特殊钢, 2024, 45(5): 123-126.
[8]	徐烨玲, 王冲, 侯翔益, 黄嘉良, 廉心桐, 黄烁. GH4706合金涡轮盘锻件不同部位的组织及高温力学性能[J]. 特殊钢, 2024, 45(5): 102-107.
[9]	李晴. 固溶温度对GH4163合金显微组织及拉伸性能的影响[J]. 特殊钢, 2024, 45(5): 97-101.
[10]	李阳, 赵广迪, 臧喜民, 姜昊源, 王兆宇. B对Fe-Cr-B-C合金热处理后显微组织和强韧性的影响[J]. 特殊钢, 2024, 45(5): 25-33.
[11]	李建平, 唐正友, 张翰文, 邓通武. Si对缆索钢丝绳用热轧盘条组织和力学性能的影响[J]. 特殊钢, 2024, 45(5): 19-24.
[12]	袁志钟, 陈露, 张伯承, 刘海明, 牛宗冉, 王致远, 鞠玉琳, 程晓农. LB/M复相热处理工艺对冷作模具钢DC53组织和力学性能的影响[J]. 特殊钢, 2024, 45(4): 153-160.
[13]	孙中豪, 李强, 张明亮, 马程款, 夏志斌, 钟云波. 磁控电渣重熔对M2高速钢凝固组织及力学性能的影响[J]. 特殊钢, 2024, 45(4): 68-76.
[14]	张宏, 李旭, 陈华, 唐琴, 李林森, 王立, 高首磊. 热处理工艺对140 ksi等级In718合金组织与性能的影响[J]. 特殊钢, 2024, 45(4): 139-145.
[15]	范晓烁, 刘玉峰, 袁华. 粉末处理对FGH95氧含量、微观组织及力学性能的影响[J]. 特殊钢, 2024, 45(4): 124-130.