600 MPa低硅Nb-Ti微合金化优质3.5 mm热轧双相钢板的开发

特殊钢 ›› 2014, Vol. 35 ›› Issue (5): 47-49.

600 MPa低硅Nb-Ti微合金化优质3.5 mm热轧双相钢板的开发

殷胜¹，蔡晓辉²，朱红丹³

1. 宝钢梅山钢铁股份有限公司技术中心，南京210039；
2. 东北大学连轧自动化国家重点实验室，沈阳110819；
3. 宝钢梅山钢铁股份有限公司检测中心，南京210039；

收稿日期:2014-04-16 出版日期:2014-10-01 发布日期:2022-09-01
作者简介:殷胜(1980-)，男，硕士研究生，工程师，2004年南京理工大学(本科)毕业，热轧汽车钢产品开发。

Development of 600 MPa Low Silicon and Nb-Ti Microalloying High Quality 3.5 mm Hot-Rolled Dual Phase Steel Plate

Yin Sheng¹ , Cai Xiaohui² , Zhu Hongdan³

1. Technology Center, Meishan Iron and Steel Co Ltd, Baosteel, Nanjing 210039 ；
2. State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819 ;
3. Testing Center, Meishan Iron and Steel Co Ltd, Baosteel, Nanjing 210039 ;

Received:2014-04-16 Published:2014-10-01 Online:2022-09-01

摘要/Abstract

摘要： 通过真空感应炉熔炼和浇铸的50 kg锭锻成40 mm×150 mm坯和热轧成10 mm板以及热模拟试验研究了开发的低硅Nb-Ti微合金化双相钢(/%:0.082C，0.15Si，1.20Mn，0.010P，0.002S，0.020Nb，0.015Ti，0.045Al，0.0035N)静态和动态连续冷却转变(CCT)曲线、组织(11%马氏体+89%铁素体)和力学性能(抗拉强度682 MPa)。并通过铁水脱硫-260 t BOF-LF-RH-230 mm×1300 mm连铸-热轧工艺试制了低硅双相钢(/%:0.075C，0.15Si，1.16Mn，0.012P，0.003S，0.016Nb，0.015Ti，0.033Al，0.0043N)3.5mm板。结果表明，精轧出口温度810℃，水冷至700℃，空冷4.5 s，卷取温度150℃时，该钢的组织为15%马氏体+85%铁素体,晶粒度12~12.5级，抗拉强度672~692 MPa，伸长率24.0%~28.5%，屈强比0.65~0.67，钢板冲压成塑性能优良，制造的轿车轮辐弯曲疲劳性能15×10⁴次。

关键词: 600 MPa低硅Nb-Ti微合金化双相钢, 3.5 mm板, 开发

Abstract: The static and dynamic continuous cooling transformation (CCT) curves, structure (11% martensite + 89% feiTite) and mechanical properties (tensile strength 682 MPa) of developed low silicon and Nb-Ti Microalloying dual phase steel (/% : 0.082C, 0.15Si, 1.20Mn, 0.010P, 0.002S, 0.020Nb, 0.015Ti, 0.045Al, 0.0035N) have been tested and studied by melting in a vacuum induction furnace, casting 50 kg ingot, forging to 40 mm x 150 mm slab and hot rolling to 10 mm plate and thermal simulation testing. And 3.5 mm low silicon dual phase steel plate (/% : 0.075C, 0.15Si, 1.16Mn, 0.012P, 0.003S, 0.016Nb, 0.015Ti, 0.033Al, 0.0043N) has been pilot-produced by hot metal desulphurization-260 t BOF-LF-RH-230 mm x 1300 mm slab concasting-hot rolling process. Results show that with finished rolling 810 °C , water cooling to 700 ℃, air cooling for 4.5 s and coiling at 150 °C , the structure of steel is 15% +85% ferrite with gain size rating 12-12.5, the tensile strength of steel is 672-692 MPa with yield-ultimate strength ratio 0. 65 ~0. 67, and the yield of steel is 24.0%-28.5% . The steel plate has nice stamping performance and the bending fatigue life of manufactured wheel rib of car is 15 x 10⁴.

Key words: 600 MPa Low Silicon and Nb-Ti Microalloying Dual Phase Steel, 3.5 mm Plate, Development

殷胜, 蔡晓辉, 朱红丹. 600 MPa低硅Nb-Ti微合金化优质3.5 mm热轧双相钢板的开发[J]. 特殊钢, 2014, 35(5): 47-49.

Yin Sheng , Cai Xiaohui , Zhu Hongdan. Development of 600 MPa Low Silicon and Nb-Ti Microalloying High Quality 3.5 mm Hot-Rolled Dual Phase Steel Plate[J]. Special Steel, 2014, 35(5): 47-49.

[1]	刘福斌, 姜周华, 李花兵, 冯浩, 董君伟, 张取一, 郑淮北. 加压电渣重熔装备与工艺技术开发[J]. 特殊钢, 2024, 45(4): 26-33.
[2]	赵满堂, 陈永峰, 陶群南, 林作津, 史杨. 低合金高强度30CrMnTi盘条钢的开发实践[J]. 特殊钢, 2021, 42(1): 29-31.
[3]	殷胜, 朱红丹. 屈服强度750 MPa低合金钢高强度集装箱用钢的开发[J]. 特殊钢, 2019, 40(1): 16-18.
[4]	孟传峰, 王一德, 卫英慧, 崔天燮, 王育田. 工程机械用TQ960E微合金化低碳高强度钢的开发[J]. 特殊钢, 2018, 39(6): 66-70.
[5]	梁娜. 汽车轴头用低合金高强度钢Q460D的开发和性能[J]. 特殊钢, 2018, 39(3): 66-69.
[6]	刘年富. 窄淬透性带20CrMnTiH齿轮钢的开发[J]. 特殊钢, 2018, 39(1): 41-43.
[7]	万长杰, 申丽娟, 刘梅, 赵天力. 高碳微合金非调质钢C70S6的开发和工艺实践[J]. 特殊钢, 2017, 38(5): 31-33.
[8]	陈振业, 孙力, 王晓书, 韦明, 张海军. 建筑抗震用低屈服点钢LY225的开发[J]. 特殊钢, 2017, 38(2): 37-39.
[9]	邓通武, 柯晓涛, 胡峰荣. 含钒非调质预硬型塑料模具钢48MnV的开发[J]. 特殊钢, 2016, 37(5): 55-58.
[10]	邢娜, 黄宝, 何立波, 赵婷婷. 酸性环境用油气专用无缝钢管的研发现状[J]. 特殊钢, 2016, 37(3): 20-24.
[11]	朱敏, 徐光, 张昌强, 吉玉. 980 MPa耐蚀钢轨U68CuCr的开发和应用[J]. 特殊钢, 2016, 37(2): 58-61.
[12]	邢娜, 黄宝, 何立波. 超临界超超临界锅炉管品种的开发现状[J]. 特殊钢, 2016, 37(1): 17-21.
[13]	孔凡庆, 程晓杰, 贾松, 乔建军, 李勇, 段晓东. 无铬钝化热镀锌耐指纹板的开发[J]. 特殊钢, 2014, 35(3): 33-35.
[14]	周志伟, 俞杰. C90-1级耐腐蚀石油套管用钢25CrMoTi的开发[J]. 特殊钢, 2012, 33(4): 39-41.
[15]	殷胜, 万兰凤. 600 MPa级Nb-Ti微合金高强度钢的开发[J]. 特殊钢, 2012, 33(3): 29-31.