含银高氮无镍抗菌不锈钢HNSAg的冷作硬化和耐磨蚀性能

特殊钢 ›› 2015, Vol. 36 ›› Issue (6): 59-62.

• 组织和性能 • 上一篇

含银高氮无镍抗菌不锈钢HNSAg的冷作硬化和耐磨蚀性能

袁军平，王昶，陈绍兴，卢焕洵，申柯娅，黄宇亨

广州番禺职业技术学院珠宝学院，广州511483

收稿日期:2015-06-23 出版日期:2015-12-01 发布日期:2022-08-16
作者简介:袁军平(1969-)，男，博士(2009年暨南大学)，教授级高级工程师,1992年北京科技大学(本科)毕业，金属材料和成型工艺研究。
基金资助:
广东高校珠宝首饰工程技术开发中心建设项目资助 (粤教科函【2012】131号)

Cold-Work Hardening and Wear-Corrosion Resistance of Silver-Containing High-Nitrogen Nickel-Free Antibacterial Stainless Steel HNSAg

Yuan Junping, Wang Chang, Chen Shaoxing, Lu Huanxun, Shen Keya ，Huang Yuheng

Jewelry Institute, Guangzhou Panyu Polytechnic College, Guangzhou 511843

Received:2015-06-23 Published:2015-12-01 Online:2022-08-16

摘要/Abstract

摘要： 试验研究了超低碳Cr-Ni-Mo奥氏体不锈钢316L(/%:0.023C,0.55Si,0.86Mn,17.57Cr,11.23Ni,2.03Mo)和抗菌超低碳Cr-Mn-Mo-N-Cu-Ag奥氏体不锈钢HNSAg(0.024C,0.48Si,18.72Mn,18.05Cr,1.96Mo,0.55N,0.48Cu,0.13Ag,0.12Nb)的冷作硬化和耐磨蚀性能。HNSAg钢由10 kg增压感应炉熔炼,锻成15 mm板,再经1 100℃1 h固溶水冷处理。结果表明,固溶状态的HNSAg钢的形变抗力较316L钢高,但仍然保持优良的塑性变形能力。在相同腐蚀磨损条件下,HNSAg钢耐磨蚀性能比316L钢高,其32 h耐磨蚀失重率约为316L钢的1/2。

关键词: 高氮含银无镍抗菌不锈钢HNSAg, 316L不锈钢, 冷作硬化, 耐磨蚀性

Abstract: The cold-work hardening performance and wear-corrosion resistance of ultra-low-carbon Cr-Ni-Mo austenite stainless steel 316L (/%： 0.023C, 0. 55Si, 0. 86Mn, 17. 57Cr, 11. 23Ni, 2. 03Mo) and antibacterial ultra-low-carbon Cr-Mn-Mo-N-Cu-Ag austenite stainless steel HNSAg (0. 024C, 0.48Si, 18.72Mn, 18.05Cr, 1. 96Mo, 0. 55N, 0. 48Cu, 0. 13Ag, 0. 12Nb) have been tested and studied. The steel HNSAg is melted by a 10 kg pressure induction furnace, forged to 15 mm plate and solid-solution-treated at 1 100 ℃ for 1 h, water-cooling. Results show that the deformation resistance of solid-solution-treated steel HNSAg is higher than that of steel 316L, but the steel HNSAg still maintains excellent plastic deformability, and at same wear-corrosion conditions the wear-corrosion resistance of steel HNSAg is better than that of steel 316L, its weight loss rate of wear-corrosion for 32 h is 1/2 that of steel 316L.

袁军平, 王昶, 陈绍兴, 卢焕洵, 申柯娅, 黄宇亨. 含银高氮无镍抗菌不锈钢HNSAg的冷作硬化和耐磨蚀性能[J]. 特殊钢, 2015, 36(6): 59-62.

Yuan Junping, Wang Chang, Chen Shaoxing, Lu Huanxun, Shen Keya , Huang Yuheng. Cold-Work Hardening and Wear-Corrosion Resistance of Silver-Containing High-Nitrogen Nickel-Free Antibacterial Stainless Steel HNSAg[J]. Special Steel, 2015, 36(6): 59-62.

参考文献

[1]Yuan Junping, Li Wei, Wang Chang, et al. Nickel Release Rate of Several Nickel-Containing Stainless Steels for Jewelries[J]. Journal of Iron and Steel Research, International ,2015,22(1) ：72-77.
[2]Yuan Junping,Li Wei. Antibacterial 316L Stainless Steel Containing Silver and Niobium [J]. Rare Metal Materials and Engineering, 2013,42(10) ： 2004-2008.
[3]Yuan Junping,Li Wei,Wang Chang,et al. Effect of the La Alloying Addition on the Antibacterial Capability of 316L Stainless Steel[J]. Materials Science and Engineering C,2013,33( 1) ：446-452.
[4]Ren Yibin, Yang Ke,Zhang Bingchun,et al. Nickel-Free Stainless Steel for Medical Applications [J]. Journal of Materials Science and Technology,2004,20(5) ：571-573.
[5]Sumita M,Hanawa T,Teoh SH. Development of Nitrogen-Containing Nickel-Free Austenitic Stainless Steels for Metallic Biomaterials-Re-view[J]. Materials Science and Engineering C,2004,24(6-8) ：753- 760.
[6]Sreekumari KR,Takao K,Ujiro T, High Nitrogen Stainless Steel as a Preferred Substratum for Bacteria and Other Microfouling Organisms [J].ISIJ International,2004,44(5) ：858-864.
[7]袁军平，李卫，王国智，等.高氮无镍奥氏体抗菌不锈钢 (HNSAg)及其制备方法：中国，专利号.201210585578. 9, [P]. 公开日：2013-04-17.
[8]Bramfitt B. The Effect of Carbide and Nitride Additions on the Heterogeneous Nucleation Behavior of Liquid Iron[J]. Metallurgical and Materials Transactions B ,1970,1(7) ： 1987-1995.
[9]潘宁，宋波,翟启杰，等.钢液非均质形核触媒效用的点阵错配度理论[J].北京科技大学学报,2010,32(2):179-182,190.
[10]王松涛，杨柯,单以银，等.高氮奥氏体不锈钢与316L不锈钢的冷变形行为研究[J ] .金属学报,2007,43(2):171-176.
[11]刘文昌，张静武,郑炀曾.氮强化高锰奥氏体不锈钢的应变硬化行为[J] .金属热处理学报,1995,16(3):33-38.
[12]袁军平.首饰用不锈钢等的镍释放及抗菌改性[D].广州:暨南大学博士学位论文,2012.
[13]Fu Yao,Wu Xinqiang,Han En-Hou,et,al. Effects of Nitrogen on the Passivation of Nickel-Free High Nitrogen and Manganese Stainless Steels in Acidie Chloride Solutions[J]. Electrochimica Acta, 2009,54(16) ：4005-4014.
[14]廖洪军，温继勇,姚长贵，等.Cr-Mn-N奥氏体不锈钢的晶间腐蚀性能研究[J].世界钢铁,2012(2) ：46-49.

含银高氮无镍抗菌不锈钢HNSAg的冷作硬化和耐磨蚀性能

Cold-Work Hardening and Wear-Corrosion Resistance of Silver-Containing High-Nitrogen Nickel-Free Antibacterial Stainless Steel HNSAg

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 6

编辑推荐

Metrics

本文评价

[1]	邢佳, 杜晓建, 张欣杰, 陈保梁, 张利, 刘承志. 喂钙量与软吹氩对316L不锈钢中夹杂物的影响[J]. 特殊钢, 2022, 43(2): 31-35.
[2]	庄迎, 王贵平. 316L 不锈钢冷轧板表面缺陷分析和工艺改进[J]. 特殊钢, 2017, 38(2): 26-29.
[3]	李吉东, 韩培德, 王烽, 任永秀, 贾元伟. 316L不锈钢LF精炼过程夹杂行为热力学分析和工艺优化[J]. 特殊钢, 2017, 38(1): 23-26.
[4]	袁军平, 吴海超, 卢焕洵, 陈绍兴, 薄海瑞, 黄宇亨. 成型和表面处理工艺对316L不锈钢镍释放率的影响[J]. 特殊钢, 2015, 36(5): 59-63.
[5]	时彦林, 包燕平, 董中奇. 非真空吹氮工艺对316L奥氏体不锈钢吸氮行为的影响[J]. 特殊钢, 2011, 32(5): 5-7.
[6]	时彦林, 包燕平, 董中奇. VOD精炼316L不锈钢吹氮合金化的研究[J]. 特殊钢, 2011, 32(1): 16-18.