钻头用含硫XGML40Cr钢的开发及其切削性能的改善

特殊钢 ›› 2017, Vol. 38 ›› Issue (4): 60-63.

钻头用含硫XGML40Cr钢的开发及其切削性能的改善

黄翠环^1,2，秦树超^1,2，郭明仪^1,2，孔维涛^1,2

1邢台钢铁有限责任公司技术中心，邢台054027 ；
2河北省线材工程技术研究中心，邢台054027

收稿日期:2017-02-09 出版日期:2017-08-01 发布日期:2022-07-22
作者简介:黄翠环(1985-)，女，硕士(2010年东北大学)，工程师,2008年东北大学(本科)毕业,冷镦钢研究和开发。

Development of Bearing Sulfur Steel XGML40Cr for Drill Bit and Improvement of Its Cutting Performance

Huang Cuihuan^1,2, Qin Shuchao^1,2, Guo Mingy^1,2 ，Kong Weitao^1,2

1 Technology Center, Xingtai Iron and Steel Corp Ltd, Xingtai 054027；
2 Hebei Province Wire Engineering Technical Research Center, Xingtai 054027

Received:2017-02-09 Published:2017-08-01 Online:2022-07-22

摘要/Abstract

摘要： 邢钢开发的0.020%0.060%S钻头用XGMI40Cr钢（/%:0.38~0.44C,0.170~.30Si,0.60~0.80Mn,≤0.035P,0.020~0.060S,0.90~1.10Cr,≤0.01Al）的生产流程为50 t BOF-LF-285 mm×320 mm坯连铸-热轧成Φ12 mm线材。对0.027%S的XGML40Cr和0.006%S的ML40Cr盘条试样进行进刀量0.015 mm/r,切削深度0.1 mm,切削速度1230 m/min的切削试验。试验结果表明,XGML40Cr断屑性能优于ML40Cr,其切削长度为ML40Cr钢1/53/5,XGML40Cr切削过程产生更低的切削热,蓝色切屑比例为10%,ML40Cr钢为70%,XGML40Cr切屑变形系数低于ML40Cr,XGML40Cr表面粗糙度（Ra 10.2μm）优于ML40Cr（Ra 22.4μm）。含硫XGML40Cr钢的力学性能与ML40Cr相当,870℃淬火和500℃回火后的力学性能为抗拉强度1 082 MPa,断面收缩率70%,HRC硬度值40,冲击功A_k_v272 J。

Abstract: The production flowsheet of developed 0. 020% ~ 0. 060% S steel XGML40Cr (/% : 0. 38 ~ 0. 44C, 0. 17 ~0. 30Si, 0.60 ~0. 80Mn, ≤0. 035P, 0. 020 ~0. 060S, 0. 90 〜1.1OCr, ≤ 0. 01A1) for drill bit at Xingsteel is 50 t BOF-LF-285 mm x320 mm bloom casting-hot-rolling to Φ12 mm wire rod. The cutting test on 0. 027% S steel XGML40Cr and 0. 006% S steel ML40Cr with cutting feed rate 0. 015 mm/r, depth of cut 0. 1 mm and cutting speed 12 〜30 mm/min has been carried out. Test results show that the cutting performance of steel XGML40Cr is better than that of steel ML40Cr, i. e. its turning chip length is 1/5 ~ 3/5 that of steel ML40Cr； the heat productivity of steel XGML40Cr during cutting process is lower than that of steel ML40Cr, its blue turning chip ratio is 10% but that of steel ML40Cr is up to 70% ； and the cutting deformation coefficient of steel XGML40Cr is lower than that of steel ML40Cr and its surface roughness ( Ra 10. 2μm) is better than that of steel ML40Cr (Ra 22. 4μm). The mechanical properties of steel XGML40Cr is about equal to that of steel ML40Cr, its mechanical properties quenched at 870 °C and tempered at 500 ℃ are tensile strength 1 082 MPa, reduction of area 70% , HRC hardness value 40 and impact energy A_kv2 72 J.

黄翠环, 秦树超, 郭明仪, 孔维涛. 钻头用含硫XGML40Cr钢的开发及其切削性能的改善[J]. 特殊钢, 2017, 38(4): 60-63.

Huang Cuihuan, Qin Shuchao', Guo Mingyi, Kong Weitao, . Development of Bearing Sulfur Steel XGML40Cr for Drill Bit and Improvement of Its Cutting Performance[J]. Special Steel, 2017, 38(4): 60-63.

参考文献

[1]夏云进，王福明,王金龙，等.氧含量对易切削钢中硫化物生成行为的影响[J].北京科技大学学报,2010,32(10):1271-1276.
[2]王妮燕，蒋仕军，罗军，等,Y45S20易切削钢的工艺优化[J]. 钢铁,2002,37(10):48-51.
[3]戴永刚.精炼渣组分对硫易切削钢夹杂物含量和形态的影响 [J].特殊钢,2016,37(1):60-63.
[4]刘洋，王文军，王新华，等.低硫微合金钢中硫化锭析出规律分析[C] //2010年全国炼钢-连铸生产技术会议论文集.河北迁安：中国金属协会,2010:390-394.
[5]高建伟.转炉生产易切削钢45BS工艺技术[J].辽宁科技学院学报,2012,14(1):1-3.
[6]袁武华，王峰.国内外易切削钢的研究现状和前景[J].钢铁研究,2008,36(5):56-62.
[7]段飞虎，朱荣，林腾昌.硫系易切削钢中氧含量对硫化物形成的影响[J].钢铁研究学报,2012,24(1) =36-39.
[8]陈明，刘钢，张晓辉，等.新型低碳硫系易切削钢切削性能试验[J].机械工程学报,2007,43(9):161-166.
[9]王继梅，于军华，管旭.不锈钢1Cr18Ni9Ti切屑形态研究[J]. 铸造技术,2015,36(4) ： 1084-1087.
[10]郝春水，吴凤春.稀土硬质合金刀片切削性能[J].东北大学学报,1994,15(5) ：499-5。2.
[11]刘华.刀屑接触长度对切削变形的影响[J].包头钢铁学院学报,1998,17(1):36-39.
[12]段春争，王敏杰，于海洋.高速切削淬硬钢切屑变质层微结构及形成机理[J].材料科学与工艺,2012,20(3):127-131.
[13]陈锡渠，彭晓南.金属切削原理与刀具[M].北京:中国林业出版社,2006.
[14]侯书林，朱海.机械制造基础(下册)：机械加工工艺基础 [M],北京:中国林业出版社,2006.
[15]陆剑中，孙家宁.金属切削原理与刀具[M].北京:机械工业版社,2005.