两流板坯连铸58t中间包过滤器的水模型试验和应用

特殊钢 ›› 2018, Vol. 39 ›› Issue (2): 13-16.

两流板坯连铸58t中间包过滤器的水模型试验和应用

钟巍^1,2, 赵丹婷^1,3, 帅勇^1,2, 罗仁辉², 仇圣桃¹

1钢铁研究总院连铸技术国家工程研究中心，北京100081;
2新余钢铁集团有限责任公司，新余338001；
3北京科技大学冶金与生态工程学院，北京100083

收稿日期:2017-11-23 出版日期:2018-04-01 发布日期:2022-06-27
作者简介:钟巍(1973-),男，博士研究生，高级工程师,1995年南昌航空工业大学(本科)毕业，设备技术和管理。

Water Model Test of 58t Tundish with Channel Filter for Two Strands Slab Casting and Application

Zhong Wei^1,2, Zhao Danting^1,3, Shuai Yong^1,2, Luo Renhui², Qiu Shengtao¹

1 National Engineering and Research Center of Continuous Casting Technology, Central Iron and Steel Research Institute, Beijing 100081；
2 Xinyu Iron and Steel Co Ltd, Xinyu 338001;
3 School of Metallurgical and Ecological Engineering, Beijing University of Science and Technology, Beijing 100083

Received:2017-11-23 Published:2018-04-01 Online:2022-06-27

摘要/Abstract

摘要： 通过几何相似比0.29:1的水模型试验了湍流抑制器+挡墙+挡坝和湍流抑制器+挡墙+过滤器两种控流装置的钢液流动,研究了通道式过滤器对58t中间包钢液流场的影响。结果表明,原中间包（湍流抑制器+挡墙+挡坝）活塞区体积小,死区体积高达29.53%,优化中间包加入过滤器后（湍流抑制器+挡墙+过滤器）短路流基本消失,钢液的实际平均停留时间延长,死区体积由29.53%减小至13.52%。50t中间包,230mm×1100mm连铸板坯,拉速1.25~1.30m/min工业生产结果表明,使用过滤器后,中间包浇注区的夹杂物尺寸明显小于冲击区,中间包浇注区T[O]由原86×10^-6降至30×10^-6,连铸坯大多数夹杂物尺寸≤10μm,没有发现≥30μm夹杂物。

关键词: 58t中间包, 通道式过滤器, 水模型, 流场, 夹杂物

Abstract:

The effect of channel filter on fluid field of liquid in a 58t tundish has been studied by using geometric similarity 0.29 : 1 water model to test liquid flow by both control flow devices- turbulence controller + retaining wall + dam and turbulence controller + retaining wall + channel filter. Results show that in original tundish with turbulence controller + retaining wall + dam the plug flow area is relatively small and the dead area is up to 29.53% , while in optimized tundish adding channel filter with turbulence controller + retaining wall + channel filter the short circuit flow basically disappears, the real resident time of liquid increases and the dead area decreases from original 29.53% to 13.52%. The results of commercial production with 50t tundish, casting 230mm x 1100mm slab and casting speed 1.25~1.30 m/min show that after using channel filter the size of inclusions in liquid at casting area in tundish is obvious less than that in impact zone, the T[O] in liquid at casting area in tundish decreases from original

86x10^-6 to 30x10^-6 and the size of most inclusions in casting slab is≤10μm and the ≥30μm inclusions are not found.

钟巍, 赵丹婷, 帅勇, 罗仁辉, 仇圣桃. 两流板坯连铸58t中间包过滤器的水模型试验和应用[J]. 特殊钢, 2018, 39(2): 13-16.

Zhong Wei, Zhao Danting, Shuai Yong, Luo Renhui, Qiu Shengtao. Water Model Test of 58t Tundish with Channel Filter for Two Strands Slab Casting and Application[J]. Special Steel, 2018, 39(2): 13-16.

[1]	倪卓文, 朱红春, 李花兵, 姜周华, 孙正鑫, 何志禹. H13模具钢电渣锭中夹杂物的类型以及分布规律分析[J]. 特殊钢, 2024, 45(6): 48-52.
[2]	王利, 刘成宝, 李浩秋, 王毅, 孙宗辉, 刘春伟, 杨超云, 付志豪. 稀土对20CrMnTi齿轮钢夹杂物和疲劳性能的影响[J]. 特殊钢, 2024, 45(6): 117-124.
[3]	谢康, 莫金强, 张威, 王丽君. 稀土Ce对441铁素体不锈钢碳氮化物析出的影响与控制[J]. 特殊钢, 2024, 45(6): 1-7.
[4]	郑安民, 樊轩宇, 黄增鑫, 毛旺旺, 于彦冲, 张金玲, 王社斌. 稀土Ce对20MnTiB冷镦钢中夹杂物演变的影响[J]. 特殊钢, 2024, 45(6): 37-47.
[5]	赵昊乾, 张育明, 马博, 巩延杰, 孟耀青. LF精炼结束后软吹时间对帘线钢LX82 A夹杂物控制的影响[J]. 特殊钢, 2024, 45(6): 53-56.
[6]	杨建华, 巨银军, 杨俊. 帘线钢XLX72 A中氧化物夹杂的演变解析与去除[J]. 特殊钢, 2024, 45(5): 66-71.
[7]	刘泳, 张雲飞, 赵英利, 赵楠, 赵峥嵘, 樊明强, 田志强. 改善模具钢洁净度与抛光性能的冶炼工艺实践[J]. 特殊钢, 2024, 45(5): 47-52.
[8]	袁麟, 胡小强, 刘洋, 李殿中, 谢晶, 陈伟. 稀土精炼与电渣重熔3%Cr轧辊钢对比分析[J]. 特殊钢, 2024, 45(5): 1-7.
[9]	李琦, 邱国兴, 王恭亮, 高鹏, 李荣祥. 130 t钢包底吹氩工艺数值模拟[J]. 特殊钢, 2024, 45(5): 59-65.
[10]	王冰杰, 王宇, 项淼苗, 施晓芳, 常立忠. 低频电渣重熔过程电流强度对电渣锭洁净度的影响[J]. 特殊钢, 2024, 45(4): 77-82.
[11]	杨曙磊, 王曦伟, 田强, 王田田, 杨树峰. GH4742合金真空自耗铸锭中夹杂物分布特征[J]. 特殊钢, 2024, 45(4): 61-67.
[12]	周杨, 朱红春, 李花兵, 姜周华, 何志禹, 倪卓文. 基于相场法模拟VAR强迫流场中柱状晶生长[J]. 特殊钢, 2024, 45(4): 41-46.
[13]	孙中豪, 李强, 张明亮, 马程款, 夏志斌, 钟云波. 磁控电渣重熔对M2高速钢凝固组织及力学性能的影响[J]. 特殊钢, 2024, 45(4): 68-76.
[14]	赵朋, 桂凯璇, 曲敬龙, 杨树峰. ϕ690 mm大尺寸GH4738合金真空自耗重熔数值模拟与工业实验[J]. 特殊钢, 2024, 45(4): 55-60.
[15]	任吉, 燕云, 田家龙, 王礼超, 蒋成钢, 王琳, 姜周华. La处理对H13热作模具钢中夹杂物的影响[J]. 特殊钢, 2024, 45(4): 117-123.