高品质压路机振轮用耐磨钢NM360的开发

特殊钢 ›› 2021, Vol. 42 ›› Issue (2): 24-27.

高品质压路机振轮用耐磨钢NM360的开发

姚宙¹,刘红艳^1,2,邓想涛²,于光远¹,许伟¹

1河钢集团邯郸公司技术中心，邯郸056000；2东北大学轧制技术及连轧自动化国家重点实验室，沈阳110819

收稿日期:2020-08-17 出版日期:2021-04-01 发布日期:2022-04-15
作者简介:姚宙(1986-),男，硕士生(武汉科技大学)，高级工程师， 2009年太原理工大学(本科)毕业，低合金耐磨产品研发和应用.

Development of High Quality NM360 Wear-Resistant Steel for Vibration Wheel of Roller

Yao Zhou¹ , Liu Hongyan^1,2, , Deng Xiangtao ², Yu Guangyuan¹ Xu Wei¹

1 Technical Center of HBIS Group Han Steel, Handan 056000；2 State key laboratory of Rolling Technology and Automation,Northeastern University,Shenyang 110819

Received:2020-08-17 Published:2021-04-01 Online:2022-04-15

摘要/Abstract

摘要： 设计和开发了压路机振轮用耐磨钢NM360(/%:0.10～0.15C,0.50～1.50Mn,≤0.001P,≤0.008S,0.20～0.50Mo,0.015～0.03Nb,0.018～0.15Ti,≥0.035Als,0.0012～0.003 0B,≤0.008N,≤0.0003 H,≤0.003O)32 mm板。900℃淬火+200℃回火后,该钢组织为回火马氏体;抗拉强度1150～1182 MPa,延伸率15%～17.5%;冲击功150～226 J;表面HBW布氏硬度值385～402;冷弯直径为32 mm,冷弯角度45°、90°、150°和180°冷弯试验全部合格;采用GM120焊丝焊接后,焊接接头抗拉强度为1 052 MPa,焊缝冲击功为58～63 J,焊缝HV硬度值390～396。

关键词: NM360钢, 振轮, 焊接性, 冷弯性

Abstract: The wear-resistant steel NM360 (/% : 0. 10 〜0. 15C, 0. 50 〜1. 50Mn, W 0. 001P, 0.008S, 0. 20 〜 0. 50Mo ,0.015 ~ 0. 03Nb,0.018 ~ 0.15Ti, ' 0.035Als, 0,001 2 ~ 0.003 0B, w 0.008N, W 0.000 3 H, W 0.0030) 32 mm plate for vibration wheel of roller are designed and developed. After quenching at 900℃ . + tempering at 200 ℃, the structure of steel is tempered martensite with tensile strength 1 150 ~ 1 182 MPa,elongation 15% - 17. 5% ; impact energy 150 ~226 J surface HBW brinell hardness value 385 -402. With cold bending diameter 32 mm,and bending center angles 45°, 90°, 150° and 180° ,the bending test is all qualified. After welding with GM120 welding wire, the tensile strength of the welded joint is 1 052 MPa,the impact energy of the weld is 58 ~63 J,and the HV hardness value of the weld is 390 ~396.

Key words: NM360 Steel, Vibration Wheel, Weld-Ability, Cold Bending Performance ,

姚宙, 刘红艳, 邓想涛, 于光远, 许伟. 高品质压路机振轮用耐磨钢NM360的开发[J]. 特殊钢, 2021, 42(2): 24-27.

Yao Zhou , Liu Hongyan, , Deng Xiangtao, Yu Guangyuan Xu Wei. Development of High Quality NM360 Wear-Resistant Steel for Vibration Wheel of Roller[J]. Special Steel, 2021, 42(2): 24-27.

[1]	杨亚倩, 马帅, 王惠生, 杨晓东, 梁田, 马颖澈. Mn含量对Inconel718板材焊接接头组织性能的影响[J]. 特殊钢, 2024, 45(3): 96-104.
[2]	刘红艳, 陈子刚, 邓想涛, 王昭东. 奥氏体化温度对辗压圈圆成型NM360-YLJ耐磨钢组织与性能的影响[J]. 特殊钢, 2022, 43(4): 88-94.
[3]	张卫攀刘红艳徐桂喜王青云孙电强. 高品质自卸车厢体用NM450耐磨钢板的开发[J]. 特殊钢, 2022, 43(3): 39-42.
[4]	熊刚, 夏文斌, 李端正, 田研. X65QO φ457 mm x 25.4 mm大口径深海海底无缝钢管的开发和应用[J]. 特殊钢, 2021, 42(5): 41-45.
[5]	赵国昌, 张海军, 刘生, 石莉, 林明新, 张萌, 程含文. 500 MPa级S500QL调质高强钢板在线直接淬火(DQ)工艺研究及应用[J]. 特殊钢, 2021, 42(3): 57-62.
[6]	方磊, 左秀荣, 姜金星, 刘帅, 翟冬雨. 深海Nb-Ti微合金化X65MO管线板管强度和韧性研究[J]. 特殊钢, 2021, 42(1): 86-90.
[7]	刘丽华. 低焊接裂纹敏感性低碳贝氏体高强度钢板Q800CFE的研发[J]. 特殊钢, 2014, 35(2): 51-53.
[8]	邹勇. TTS443高铬铁素体不锈钢的开发[J]. 特殊钢, 2012, 33(1): 51-53.
[9]	陈妍, 齐殿威, 吴美庆. 国内外高强度船板钢的研发现状和发展[J]. 特殊钢, 2011, 32(5): 26-30.