摘要/Abstract

摘要： 基于200 t BOF-LF-RH-板坯连铸的10CrNi3Mo钢冶金生产流程，分别通过向钢液喂入硅钙包芯线和钙镁复合包芯线，对夹杂物进行变性处理，之后通过4300厚板轧机轧制35 mm板并进行热处理。利用等电位溶液电解、扫描电镜与能谱、夹杂物分析仪等设备和方法对试验钢的夹杂物进行定量、定性分析，获得夹杂物的特性参数，主要表现为变性后夹杂物单位面积数量减少约40%,平均间距增加近1倍。结合夏比冲击试验结果，得出夹杂物变形处理对冲击韧性特别是低温冲击韧性有明显改善的结论。

关键词: 200 t BOF-LF-RH-板坯连铸流程, 10CrNi3Mo钢, 夹杂物, 变性处理, 冲击韧性

Abstract: Based on 200 t BOF-LF-RH-CC slab metallurgical process to produce 10CrNi3Mo steel, silicon-calcium cored wire and calcium-magnesium composite cored wire are injected respectively into liquid steel to modify inclusions, and the slabs are rolled to 35 mm plates with 4 300 mm heavy plate rolling mill then to carried out heat treatment. The inclusions of test steel are analyzed quantitatively and qualitatively by means of SPEED, SEM & EDS and INCA etc. The obtained main performance is that the number of inclusions per unit area is reduced by about 40% and the average distance is nearly doubled after modification. Combined with the Charpy impact test results, it is concluded that the inclusion deformation treatment is obviously improve to the impact toughness, especially the low-temperature impact toughness.

Key words: 200 t BOF-LF-RH-Slab Cast Process, 10CrNi3Mo Steel, Inclusion, Modification Treatment, Impact Toughness

杨治争, 严翔, 熊玉影, 官计生. 夹杂物特性对10CrNi3MoV钢冲击韧性的影响[J]. 特殊钢, 2022, 43(5): 33-38.

Yang Zhizheng , Yan Xiang , Xiong Yuzhang , Guan Jisheng. Effect of Inclusion Characteristics on Impact Toughness of 10CrNi3Mo Steel[J]. Special Steel, 2022, 43(5): 33-38.

参考文献

[1] 黄希祜.钢铁冶金原理[M],北京:冶金工业出版社,2007.
[2] Ye G, Jonsson P, Lund T. Thermodynamics and Kinetics of Modification of Al₂O₃ Inclusions [J]. ISIJ International, 1996, 36(S): 105-111.
[3] Hilty D C, Farrell J W. Modification of Inclusions by Ca[J]. Iron and Steel Maker, 1975, 2(5): 17-22.
[4] Holappa L, Hamalainen M, Liukkonen M, et al. Thermodynamic Examination of Inclusion Modification and Precipitation from Calcium Treatment to Solidified Steel [J]. Iron Making and Steel Making, 2003, 30(2)： 111-115.
[5] Yousef Tabatabaei, Kenneth S. Coley, Gordon A. , et al. Model of Inclusion Evolution During Calcium Treatment in the Ladle Furnace [J]. Metallurgical and Materials Transactions B, 2018, 49B：2022- 2025
[6] 沼田光裕，樋口善彦.Ca・Mg添加時的溶鋼中介在物組成变化[J].鉄与鋼,2011,97(1):1-6
[7] Zhe Yu, Chengjun Liu, Evolution Mechanism of Inclusions in Medium-Mn Steel by Mg Treatment with Different Aluminum Contents [J]. Metallurgical & Materials Transactions B, 2019, 50B：773- 781.
[8] Fu J, Yu Y G, Wang A R, et al. Inclusion Modification with Magnesium Treatment For 35CrNi3MoV Steel [J] , Journal of Materials Science&Technology, 1998, 14(1)：53-56.
[9] Ye G, Jonsson P, Lund T. Thermodynamics and Kinetics of Modification of Al₂O₃ Inclusions [J]. ISIJ Internationa], 1996, 36(S)：105-111.
[10] 张德堂.钢中非金属夹杂物图谱[M].北京：国防工业出版社，1980.
[11] 张毅，都君飞,缪乐德.钢中非金属夹杂物的分析研究进展[J]. 宝钢技术,2008(2):35-40.
[12] 方克明.钢中的夹杂物研究从表征到改性[J].中国稀土学报，2006,24(10)： 439-441.
[13] 陈家祥.炼钢常用图表数据手册[M].北京:冶金工业出版社，2010.
[14] 李晓源，时捷，萤瀚.央杂物特征参数对40CrNi2Mo钢塑性的影响材料研究学报,2002,24(1)：91-96.
[15] 李静媛，章为夷，魏成富，等.钢中夹杂物与钢的性能及断裂 [M ].北京:冶金工业出版社,2012.
[16] 魏成富，李静媛，田继丰，等.分形维数与D₆AC钢的韧化[J]. 材料科学与工程,1995,13(3):35-40.
[17] 叶瑞英，李静媛，马红，等.D₆AC钢冲击断口的分形研究 [J].材料科学与工程,2001,19(4) ：47-51,