1.25C-1.5Cr-5Al轴承钢中合金元素扩散对κ碳化物不均匀形核的影响

doi:10.20057/j.1003-8620.2022-00129

特殊钢 ›› 2022, Vol. 43 ›› Issue (6): 21-27.DOI: 10.20057/j.1003-8620.2022-00129

1.25C-1.5Cr-5Al轴承钢中合金元素扩散对κ碳化物不均匀形核的影响

庞佳琛, 王国栋, 易红亮

东北大学轧制技术及连轧自动化国家重点实验室，沈阳110189

收稿日期:2022-09-07 出版日期:2022-12-01 发布日期:2022-11-17
通讯作者: 易红亮
作者简介:庞佳琛(1990-),女,博士
基金资助:
国家自然科学基金(52101128)；国家重点研发计划(2018YFE0306102);中国博士后科学基金(2022 M710021)

Effect of Alloying Elements Diffusion on Heterogeneous Nucleation of κ-Carbide in 1.25C-1.5Cr-5Al Bearing Steel

Pang Jiachen, Wang Guodong, Yi Hongliang

The State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110189

Received:2022-09-07 Published:2022-12-01 Online:2022-11-17

摘要/Abstract

摘要： 采用组织观察、成分检测、热力学计算及结构分析等方法研究了1.25C-1.5Cr-5Al轴承钢离异共析相变过程中Al对κ碳化物不均匀形核的影响，并验证了混合碳化物组成的粒状珠光体对该钢最终硬化热处理组织及性能的影响。结果表明：退火温度由850℃降低至800℃过程中部分未溶解渗碳体溶解入奥氏体基体，未溶解渗碳体含量(体积分数)由(3.1±0.5)vol.%降低至(2.8±0.6)vol.%。高退火温度下的高扩散速度使Al能够在奥氏体中均匀分布，θ/γ界面附近不存在Al偏聚。铁素体中的高Al含量为κ碳化物形核提供成分需求。铁素体中高浓度Al有助于κ碳化物在渗碳体表面成核。

关键词: 低密度；1.25C-1.5Cr-5Al轴承钢, 离异共析相变, Al偏聚

Abstract: Through microstructure observation, chemical composition detection, thermodynamic calculation and structure analysis, the effect of Al on the heterogeneous nucleation of K-carbide during the divorced-eutectoid transformation process of 1.25C-1.5Cr-5Al bearing steel is studied, and the influence of spheroidal pearlite consisting of a mixture of carbides on the final quenched treatment^ microstructure and hardness of steel is investigated. The results shows that when the annealing temperature decreases from 850 ℃ to 800 °C , a small amount of undissolved cementite dissolves into austenite, and the non-dissolved cementite content (volume fraction) decreases from (3. 1 ±0.5) vol. % to (2.8 ±0. 6) vol. %. There is no segregation of Al in austenite along the θ/γ interface due to its high diffusion rate at high annealing temperature. The κ-carbide nucleation at the cementite interface is facilitated by ferrite' s high Al concentration.

Key words: 1.25C-1.5Cr-5Al Bearing Steel , Divorced Eutectoid Transformation , Al Segregation

庞佳琛, 王国栋, 易红亮. 1.25C-1.5Cr-5Al轴承钢中合金元素扩散对κ碳化物不均匀形核的影响[J]. 特殊钢, 2022, 43(6): 21-27.

Pang Jiachen, Wang Guodong, Yi Hongliang. Effect of Alloying Elements Diffusion on Heterogeneous Nucleation of κ-Carbide in 1.25C-1.5Cr-5Al Bearing Steel[J]. Special Steel, 2022, 43(6): 21-27.

参考文献

[1]王全山，焦作光，樊邯生.钢的球化退火机理的研究[J].特殊钢，1982, 3(3)： 3-12.
[2]柳萍，李博鹏，郑文超，等.20CrNiMo钢球化退火工艺研究 [J].特殊钢，2022, 43(3): 69-73.
[3]Hwang H, De Cooman B C. Influence of the Initial Microstructure on the Spheroidization of SAE 52100 Bearing Steel [ J ]. Steel Research International, 2016 , 87(1) ： 112-125.
[4]Verhoeven J D, Gibson E D. The divorced eutectoid transformation in steel [J]. Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science, 1998, 29(4) ： 1181-1189.
[5]Verhoeven J D. The role of the divorced eutectoid transformation in the spheroidization of 52100 steel [ J ]. Metallurgical and Materials Transactions A, 2000, 31 (10) : 2431-2438.
[6]Pandit A S, Bhadeshia H K D H. Divorced pearlite in steels[ J]. Proceedings of the Royal Society A, 2012, 468(2145) : 2767-2778.
[7 ] Wang B, Song X, Peng H. Design of a spheroidization processing for ultrahigh carbon steels containing Al [ J ]. Materials and Design, 2007, 28(2)： 562-568.
[8]Chen P, Xiong X C, Wang G D, et al. The origin of the brittleness of high aluminum pearlite and the method for improving ductility[ J]. Scripta Materialia, 2016, 124 ： 42-46.
[9]Yi H L, Hou Z Y, Xu Y B, et al. Acceleration of spheroidization in eutectoid steels by the addition of aluminumL J] . Scripta Materialia, 2012, 67(7-8) ：645-648.
[10]Pang J C, Wang G D, Yi H L. Effect of isothermal annealing on microstructure and hardness of low-density bearing steel [ J ]. Journal of Iron & Steel Research, 2020, 32(12) : 61-67.
[11]Qian D S, Wang K W, Liu Q L, et al. Effect of annealing parameters on microstructure and mechanical property of hot-rolled 100C16 bearing ring [ J ]. Materials Science and Technology, 2016, 32 (11): 1-8.
[12]Oyama T, Sherby 0 D, Wadsworth J, et al. Application of the divorced eutectoid transformation to the development of fine-grained, spheroidized structures in ultralight carbon steels [ J ]. Scripta Metallurgica, 1984, 18(8)： 799-804.
[13]Cree A M, Faulkner R G, Lyne A T. Cementite particle coarsening during spheroidisation of bearing steel SAE 52100 [ J ]. Materials Science and Technology, 1995, 11 (6) : 566-571.
[14]Luzginova N V, Zhao L, Sietsma J. The Cementite Spheroidization Process in High-Carbon Steels with Different Chromium Contents [J]. Metallurgical & Materials Transactions A, 2008, 39 (3)： 513-521.
[15]Kim K H, Lee J S, Lee D L. Effect of silicon on the spheroidization of cementite in hypereutectoid high carbon chromium bearing steels [J]. Metals And Materials International, 2010, 16(6) : 871-876.
[16]Yin Z X, Bhadeshia H. The Divorce Eutectoid Transformation in the Higher Mn Bearing Steel [ J ] . Advanced Materials Research, 2013,634038： 1798-1802.
[17]Luo D, Peet M J, Ooi S W, et al. Spheroidisation of hypereutectoid state of nanostructured bainitic steel [ J ]. Materials Science and Technology, 2014, 30(11)： 1282-1286.
[18]Pang J C, Yang W F, Wang G D, et al. Divorced eutectoid transformation in high-Al added steels due to heterogenous nucleation of K-carbide[J]. Scripta Materialia, 2022 , 209： 114395.
[19]Xiong H H, Zhang H H, Zhang H N, et al. Effects of alloying elements X (X =Zr, V, Cr, Mn, Mo, W, Nb, Y) on ferrite/TiC heterogeneous nucleation interface: first-principles study [ J ]. Journal of Iron and Steel Research( International) , 2017 , 24(3) : 328- 334.
[20]Lipchin N N, Shubin V N. Influence of the initial structure on the formation of austenite in NO. 40 steel [ J ]. Metal Science & Heat Treatment, 1966 , 8(6)： 506-507.
[21]Yi H L, Cai H L, Hou Z Y, et al. Low density steel 1.2C-1.5Cr- 5Al designed for bearings[ J ]. Materials Science and Technology, 2014 , 30(9) : 1045-1049.
[22]Zhang G H, Chae J Y, Kim K H, et al. Effects of Mn, Si and Cr addition on the dissolution and coarsening of pearlitic cementite during intercortical austenitization in Fe-1 mass%C alloy[J]. Materials Characterization, 2013, 81: 56-67.
[23 ] Ghosh S. Kinetic study on the coarsening behaviour of equilibrium phases in Nb alloyed ferritic stainless steels at 700°C[ J . Materials Chemistry and Physics, 2010, 124( 1) : 13-16.
[24 ] Razik N A, Lorimer GW, Ridley N. Chromium partitioning during the austenite-pearlite transformation [J] . Metallurgical Transactions A, 1976, 7(2): 209-214.
[25]Chance J, Ridley N. Chromium partitioning during isothermal transformation of a eutectoid steel [ J ]. Metallurgical Transactions A, 1981, 12(7)： 1205-1213.
[26]Khare S, Mahajan P. Effect of Al on Growth Kinetics of Cementite in Fe-C-Al Alloys[ J]. National Academy of Science Letters, 2016, 39(6) : 441444.
[27]Cheng W C, Song Y S, Lin Y S, et al. On the Eutectoid Reaction in a Quaternary Fe-C-Mn-Al Alloy: Austenite—► Ferrite + Kappa- Carbide + M23C6 Carbide[J]. Metallurgical and Materials Transactions A, 2013, 45(3)： 1199-1216.
[28 ] Sadhan G. Equilibrium Versus Paraequilibrium Precipitation of Cementite in Ternary Alloys: Thermodynamic and Kinetic Interpretations[ J]. Transactions Of The Indian Institute Of Metals, 2018, 71 (5) : 1265-1278.

1.25C-1.5Cr-5Al轴承钢中合金元素扩散对κ碳化物不均匀形核的影响

Effect of Alloying Elements Diffusion on Heterogeneous Nucleation of κ-Carbide in 1.25C-1.5Cr-5Al Bearing Steel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 0

编辑推荐

Metrics

本文评价