低钛高炉渣应用于HRB400E螺纹钢100t LF精炼的工业试验

特殊钢 ›› 2018, Vol. 39 ›› Issue (1): 28-33.

低钛高炉渣应用于HRB400E螺纹钢100t LF精炼的工业试验

王宝华^1,2，宫永煜²，张明博^1,2，黄世平³，宁树博²

1.北京科技大学冶金与生态工程学院，北京 100083；
2.河钢股份有限公司承德分公司，承德 067102；
3.河钢集团钢研总院，石家庄 050023 ；

收稿日期:2017-08-17 出版日期:2018-02-01 发布日期:2022-06-30
作者简介:王宝华(1973-)，男，高级工程师，博士研究生(北京科技大学),1996年河北理工大学(专科)毕业,炼钢工艺技术研究。

Commercial Pilot Production of Threading Steel HRB400E 100t LF Refining by Using Low Titanium Blast Furnace Slag

Wang Baohua^1,2 , Gong Yongyu² , Zhang Mingbo^1,2 , Huang Shiping³ ， Ning Shubo²

1.School of Metallurgical and Ecological Engineering, University of Science and Technology, Beijing 100083 ；
2.Chengde Branch,Hesteel Co Ltd, Chengde 067102 ；
3.Central Iron and Steel Research Institute, Hesteel Group, Shijiazhuang 050023；

Received:2017-08-17 Published:2018-02-01 Online:2022-06-30

摘要/Abstract

摘要： 采用喷吹CO₂法对低钛高炉渣进行脱硫处理，低钛高炉渣中硫的脱除率为66.59%~78.01%，渣中残硫含量为0.137%~0.283%，所制备的低硫低钛高炉渣中硫含量基本满足HRB400E钢LF精炼渣要求。低硫低钛高炉渣LF精炼终渣成分为/%:37.40~46.50CaO，12.30~15.10MgO，21.70~26.70SiO_2，5.74~17.00Al₂O_3，2.44~3.39TiO_2，0.36~1.42MnO，0.75~1.62Fe₂O_3，0.200~0.597S，钢水脱硫率为10.0%~41.5%，HRB400E钢终点[S]为0.008%~0.029%，与现工艺精炼渣（折渣和钢包渣终渣成分/%:34.30~42.90CaO，13.60~18.10MgO，24.00~26.50SiO_2，4.88~11.00Al₂O_3，0.71~1.12TiO_2，0.47~1.47MnO，0.81~1.72Fe₂O_3，0.245~1.132S）的脱硫效果相当（HRB400E钢终点[S]0.027%~0.032%）。

关键词: 低钛高炉渣, 喷吹CO₂法髙炉渣脱硫, HRB400E螺纹钢, LF精炼

Abstract: With desulphurizing treatment on low titanium blast furnace slag by blowing CO₂ method, the rate of removing sulfur from low titanium blast furnace slag is 66.59% ~78.01 % and the residual sulfur content in blast furnace slag is 0.137% ~0.283% , therefore the sulfur content in prepared low sulfur and low titanium blast furnace basically meets the requirements of LF refining slag for steel HRB400E. By using low sulfur and low titanium blast furnace slag the ingredient of end slag of LF refining is /% : 37.40 ~46.50 CaO, 12.30 ~15.10 MgO, 21.70〜26.70 SiO₂，5.74~17.00 Ag , 2.44~3.39 TiO₂, 0.36~1.42 MnO, 0.75~1.62 Fe₂O₃, and 0.200〜0.597 S, the desulphurized rate of liquid is 10.0% ~41.5% , and the end [S] of steel HRB400E is 0.008% ~0.029% , it is about equal to the effect of desulphurization by using present process refining slag-ladle slag and drained hot slag ( LF refining end slag ingredient /% : 34.30 〜42.90 CaO, 13.60 〜18.10 MgO, 24.00 〜26.50 SiO_2， 4.88 -11.00 A1₂O₃, 0.71 ~1.12 TiO₂ 0.47~1.47 MnO, 0.81~1.72 Fe₂O₃, 0.245〜1.132 S； end [S] of steel HRB400E 0.027% ~0.032% ).

王宝华, 宫永煜, 张明博, 黄世平, 宁树博. 低钛高炉渣应用于HRB400E螺纹钢100t LF精炼的工业试验[J]. 特殊钢, 2018, 39(1): 28-33.

Wang Baohua , Gong Yongyu , Zhang Mingbo , Huang Shiping , Ning Shubo. Commercial Pilot Production of Threading Steel HRB400E 100t LF Refining by Using Low Titanium Blast Furnace Slag[J]. Special Steel, 2018, 39(1): 28-33.

参考文献

[1] Liu X H,Gai G S and Yang Y F,et al. Kinetics of the Leaching of TiO₂ from Ti-bearing Blast Furnace Slag[J]. Journal of China University of Mining & Technology, 2008,18(2)：276-278.
[2] 刘晓华，隋智通.含Ti高炉渣的加压酸解[J].中国有色金属学报,2002,12(6)：1281-1284.
[3] 李玉海，娄太平,隋智通.含钛高炉渣中钛组分选择性富集及钙钛矿结晶行为[J] .中国有色金属学报,2000,10(5)：721-724.
[4] 张悦，王思佳,薛向欣.氨水沉淀法由含钛滤液提取二氧化钛[J].化工学报,2012,63(10)：3346-3349.
[5] 付念新，张力，曹洪杨，等.添加剂对含钛高炉渣中钙钛矿相析出行为的影响[J].钢铁研究学报,2008,20(4)：13-17.
[6] 韩兆慧，赵化侨.半导体多相光催化应用研究进展[J].化学进展,1992,11(1):1-10.
[7] Bellmann F and Stark J. Activation of Blast Furnace Slag by a New Method [J], Cement and Concrete Research ,2009,39(8)：644-650.
[8] 杨合,薛向欣，左良，等.含钛和稀土高炉渣光催化降解活性艳红 X-3B [J].硅酸盐学报,2003,31(9)：896-899.
[9] 卢正希.含钛矿物光催化降解硝基苯废水[D].沈阳：东北大学材料与冶金学院,2010.
[10] 王微.利用含钛高炉渣制备陶瓷的试验研究及其抗菌性的探讨[D].沈阳：东北大学材料与冶金学院,2010.
[11] 张悦，杨合，王丽，等.用含钛高炉渣制备肥料[J].东北大学学报(自然科学版)，2010,31(8):1161-1164,1169.
[12] 张悦，杨合,薛向欣.含钛高炉渣合成复合肥料及大豆栽培实验研究[J].环境工程,2012,30(5)：96-99.
[13] 徐楚韶，刘天福.用高炉钛渣冶炼复合铁合金[J].矿业工程. 1988,8(2):4145.
[14] 李祖树，徐楚韶,李在妙，等.用高炉钛渣冶炼钛硅合金的研究[J].重庆大学学报(自然科学版),1996,19(4) ：82-86.
[15] 李祖树，徐楚韶.钛矿渣电热法制取钛硅合金时直流电作用的试验研究[J].化工冶金,1995,16(1):6-11.
[16] 侯世喜，柯昌明,李有奇.金属热还原含钛高炉渣制取合金及残渣的研究[J] .铁合金,2007,196(5) ：20-23.