渣料中石灰活性度对铁水脱硫的影响

特殊钢 ›› 2017, Vol. 38 ›› Issue (2): 16-18.

渣料中石灰活性度对铁水脱硫的影响

郝素菊¹，兰吉然¹，蒋武锋¹，张玉柱^1,2，郝华强²

1. 华北理工大学冶金与能源学院，现代冶金技术教育部重点实验室，唐山 063009；
2. 东北大学冶金学院，沈阳 110004;

收稿日期:2016-10-26 出版日期:2017-04-01 发布日期:2022-07-20
作者简介:郝素菊(1966-)，女，博士(2010年东北大学)，教授,1989年东北大学(大学)毕业，钢铁冶金研究。
基金资助:
国家自然基金项目(51174075,51274084);
河北省自然科学基金项目(E2014209157);
华北理工大学培育基金项目(GP201507)资助;

Effect of Activity of Lime in Slagging Materials on Desulfurization of Hot Metal

Hao Suju¹ , Lan Jiran¹ , Jiang Wufeng¹ , Zhang Yuzhu^1,2 , Hao Huaqiang²

1. Ministry of Education Key Laboratory of Modern Metallurgy Technology, College of Metallurgy and Energy,North China University of Science and Technology, Tangshan 063009 ；
2. School of Metallurgy,Northeastern University, Shenyang 110004;

Received:2016-10-26 Published:2017-04-01 Online:2022-07-20

摘要/Abstract

摘要： 煅烧石灰石制备260,401,397,383 mL四种活性度的石灰。试验铁水脱硫渣成分为（/%）:35.18~44.84CaO，13.80~23.46SiO₂，18.98Al₂O₃，9.49MgO，1.89Fe₂O₃，11.00CaF₂，碱度为1.5~3.25，铁水成分为（/%）:4.53C，0.16Si，0.107S，0.099P。试验渣-铁比为7:100~15:100于电磁感应炉中在1330~1390℃进行脱硫实验。用荧光仪检测坩埚铁水中硫含量，并用全自动压汞仪测量石灰的比表面积和孔径分布。实验采用单一变量的方法，研究了石灰活性度，渣料碱度,熔炼温度，渣铁比对铁水脱硫的影响。实验表明,活性为397 mL的石灰比表面积较大，孔分布均匀,脱硫效果最好。在1390℃、碱度为2.25、渣铁比为15:100的条件下，活性度为397 mL的石灰，铁水脱硫率可达到97.2%。

关键词: 铁水, 脱硫, 石灰, 活性度

Abstract: The lime with 260, 401, 397 and 383 mL four kinds of activity is manufactured by calcined limestone. The ingredient of tested slag for desulphurization of hot metal is (/% :) 35.18〜44.84CaO, 13.80〜23.46SiO₂, 18.98Al₂O₃, 9. 49MgO, 1.89Fe₂O₃, 11.00CaF₂ with basicity 1.5~3.25, and the chemical composition of hot metal is (/% :) 4.53C, 0.16Si, 0.107S, 0.099P. The tested slag-metal ratio is 7：100 to 15：100 and the desulphurization test is in an induction furnace at 1330〜1390 °C. The sulphur content in metal in crucible is analyzed by a fluorescence analyzer, and the distribution of specific surface area and size of pore of lime are measured by an automate pressure mercury analyzer. The experiment is carried out by a single variable method to study the effect of slag basicity, melting temperature, slag-metal ratio and activity of lime on desulphurization of hot metal. The test results show that the lime with activity 397 mL is larger specific surface area and more uniform pore distribution, it has best desulphurization effect. With slag basicity 2.25, slagmetal ratio 15：100 and at 1390℃, by using lime with activity 397 mL the desulphurization ratio of metal is up to 97.2%.

郝素菊, 兰吉然, 蒋武锋, 张玉柱, 郝华强. 渣料中石灰活性度对铁水脱硫的影响[J]. 特殊钢, 2017, 38(2): 16-18.

Hao Suju , Lan Jiran , Jiang Wufeng , Zhang Yuzhu , Hao Huaqiang. Effect of Activity of Lime in Slagging Materials on Desulfurization of Hot Metal[J]. Special Steel, 2017, 38(2): 16-18.

[1]	陈君, 苏春阳, 姜亚清. 基于多元线性回归的转炉石灰加入量计算模型[J]. 特殊钢, 2024, 45(1): 42-47.
[2]	甄先锋, 宋永涛, 吴志敏, 胡建新. KR脱硫喷粉工艺实践[J]. 特殊钢, 2023, 44(4): 54-57.
[3]	徐小伟. KR-BOF-RH流程高牌号无取向硅钢W310超低硫冶炼研究与实践[J]. 特殊钢, 2023, 44(1): 55-60.
[4]	潘宏伟, 张仕骏, 单庆林, 路博勋, 张贺君, 肖鹏程, 邝霜. 唐钢新区铁水KR高效脱硫的工业试验研究[J]. 特殊钢, 2023, 44(1): 25-29.
[5]	梁娜, 刘永昌, 王升. 汽车零部件用45Mn2R硫系易切削钢的开发[J]. 特殊钢, 2022, 43(5): 51-54.
[6]	高琦, 智建国, 吴伟, 张志兵, 张晓峰, 关键. 100t 转炉留渣双渣法冶炼高硅高磷铁水试验[J]. 特殊钢, 2020, 41(6): 41-45.
[7]	翟勇强, 王建伟, 张毅, 夏朝开, 王琳松, 高长益. 100t转炉用含钛铁水冶炼高碳钢的留渣+单渣操作实践[J]. 特殊钢, 2020, 41(5): 29-33.
[8]	赵世杰, 轩振博, 冯文甫, 刘学强, 范建英, 霍立国. 80 t BOF-LF-RH流程GCrl5钢超深脱硫的生产实践[J]. 特殊钢, 2020, 41(5): 42-44.
[9]	张天旭, 宋劲松, 苏浩男, 周东东. 100t铁水罐下KR搅拌法脱硫流场的数值模拟[J]. 特殊钢, 2020, 41(3): 5-9.
[10]	刘锦文, 铁占鹏, 郭路召, 张硕, 张家泉, 唐海燕. SiCaBa合金对55SiCr弹簧钢的脱氧脱硫及夹杂物控制研究[J]. 特殊钢, 2020, 41(3): 20-24.
[11]	尚大军. 20Cr13不锈钢25 t VOD-LF硅脱氧精炼工艺的生产试验[J]. 特殊钢, 2019, 40(2): 13-16.
[12]	刘兵. 40%铁水-50 t EAF-LF-VD-CC流程16MnCr5齿轮钢的开发[J]. 特殊钢, 2019, 40(2): 42-45.
[13]	吴明, 杨芳, 吕鸣. 复合喷吹石灰与镁粉配比对铁水脱硫效果的影响[J]. 特殊钢, 2018, 39(5): 18-20.
[14]	张彦恒, 周海龙, 喻林, 卓钧. 钒钛铁水冶炼提升废钢比的探索与实践[J]. 特殊钢, 2018, 39(5): 21-23.
[15]	李德军, 许孟春, 李晓伟, 刘祥, 于赋志. 170 ~190tLF精炼过程脱硫影响因素分析[J]. 特殊钢, 2018, 39(5): 32-35.