常化温度对无取向电工钢50W300热轧板组织、织构和磁性能的影响

特殊钢 ›› 2022, Vol. 43 ›› Issue (4): 82-87.

常化温度对无取向电工钢50W300热轧板组织、织构和磁性能的影响

叶铁¹，高振宇²，卢志文¹，仲志国¹，马春华¹

1南阳师范学院智能制造研究院，南阳473061 ；
2鞍钢股份有限公司技术中心，鞍山114001

收稿日期:2021-12-20 出版日期:2022-08-01 发布日期:2022-08-21
作者简介:叶铁(1974-),男,副教授，博士，电工钢研究。
基金资助:
国家自然科学基金项目(No. 51374132);
河南省自然科学基金项目(NO. 182300410240)；
河南省教育厅项目(212300410377)

Effect of Normalized Temperature on Microstructure、Texture Transformation and Magnetic Properties of Hot Rolled Plate of Electrical Steel 50W300

YE Tie¹, GAO Zhenyu², LU Zhiwen¹, ZHONG Zhiguo¹, MA Chunhua¹

1 Intelligent Manufacturing Research Institute, Nan yang Normal University, Nanyang 473061 ；
2 Technology Centre of Ansteel Co Ltd, Anshan 114001

Received:2021-12-20 Published:2022-08-01 Online:2022-08-21

摘要/Abstract

摘要： 利用电子背散射(EBSD-electron back-scatting diffraction)检测分析技术和磁性能测量技术研究高牌号冷轧50W300无取向电工钢2.3 mm热轧板低温(820℃)和高温(920℃)常化对其组织、织构和电磁性能的影响。研究发现,920℃ 2min(45 m/min)常化时,电工钢成品的铁损最低,磁感最高。此时,电工钢卷外层晶粒组织发生脱碳并快速生长;次表层晶粒生长较为缓慢,晶粒尺寸较小,且均匀。中心层组织晶粒再结晶时,尺寸均匀。同时织构水平降低,表层织构慢散,次表层和中心层织构近似于冷轧织构,有利于电工钢磁性能的织构比例提高。

关键词: 无取向电工钢50W300, , 2.3 mm热轧板, 常化, 组织,织构,磁性能

Abstract: The microstructure, texture and electromagnetic properties of high-grade cold-rolled 50W300 non oriented electrical steel 2. 3 mm hot-rolled plate with normalizing at low temperature ( 820°C ) and high temperature (920 X.) are studied by means of EBSD ( electron back-scatting diffraction) detection etc analysis and magnetic property measurement technology. It is found that when the normalizing treated process is at 920 T for 2 min (45 m/min) , the iron loss of the finished electrical steel is the lowest and the magnetic induction is the highest. Under such process conditions, the grain structure of the outer layer of the electrical steel coil is rapidly decarburized. The grain growth of the subsurface layer is slow, and the grain is small and uniform. When the center layer structure is recrystallized, they are uniform in size. And the texture level reduces, the surface texture is slow, the texture in sub-surface and the central layer are similar to the cold- rolled textures, the texture ratio of the magnetic properties of electrical steel increase.

Key words: Non-Oriented Silicon Steel 50W300, 2. 3 mm Hot Rolled Plate, Normalizing, Microstructure, Texture, Magnetic Properties

叶铁, 高振宇, 卢志文, 仲志国, 马春华. 常化温度对无取向电工钢50W300热轧板组织、织构和磁性能的影响[J]. 特殊钢, 2022, 43(4): 82-87.

YE Tie, GAO Zhenyu, LU Zhiwen, ZHONG Zhiguo, MA Chunhua. Effect of Normalized Temperature on Microstructure、Texture Transformation and Magnetic Properties of Hot Rolled Plate of Electrical Steel 50W300[J]. Special Steel, 2022, 43(4): 82-87.

参考文献

[1]何忠治，赵宇，罗海文.电工钢[M],北京:冶金工业出版社， 2012.
[2]Daem A, Sei^eant P and DuprE L, et al. Modeling Interlocking Effects on Core Losses in Electrical Steel [J]. IEEJ Transactions on Electrical and Electronic Engineering, 2020,15(12) ： 1836-1843.
[3]He Y L, Mehdi M and Liu H, et al. Angular Magnetic Baikhausen Noise of Incline- and Cross-Rolled Non-Oriented Electrical Steel Sheets [J]. Materials Characterization, 2021,177:111200.
[4]Yamamoto and Akihiro. Cold Rolling Mill Technologies for Electrical Steel [J].AISTech-Iron and Steel Technology Conference Proceedings, 2020,2.1196-1203.
[5]Wang Z, Zhang Y L and Zhang D H, et al. Magnetostrictive Characteristics of the Grain-Oriented Electrical Steel in an Epstein Frame Magnetized with a DC Biased Magnetic Field[J]. Journal of Electrical Engineering and Technology, 2020,15(2).749-755.
[6]杨平.电子背散射衍射技术及其应用[M].北京:冶金工业出版社,2007,150-153.
[7]Li Y J, Fu Y and Dou Y, et al. Magnetic Properties Measurement and Analysis of Electrical Steel Sheet Under Cutting Influence [J]. AIP Advances, 2021,11(2).
[8]李长一，黄璞，冯大军，等.冷轧无取向电工钢的点阵畸变能及其对再结晶织构的影响[J].电工材料，2007(4):1043.
[9]吕科，李军，赵宇，等.常化温度对无抑制剂取向硅钢性能影响[J].材料热处理学报,2015,36(4) ： 162-167.
[10]耿京京，于浩,范勇斐.常化温度对热轧无取向硅钢组织与磁性能的影响[J].材料热处理学报,2013,34(Sl)：93-96.
[11]宋中华，欧阳德刚.中、低牌号无取向硅钢热轧卷常化技术[J] .武钢技术,2012,50(5) ：46-51.
[12]董廷亮，岳尔斌,李建军，等.常化温度对TSCR流程制备低碳低硅无取向硅钢组织和性能的影响[J].机械工程材料,2011, 35(3):15-17+21.
[13]董浩.高磁性能冷轧无取向硅钢薄带的研制[D].沈阳：东北大学,2009.
[14]董浩，赵宇,喻晓军，等.常化温度对冷轧无取向硅钢薄带磁性能和织构的影响[J].钢铁研究学报,2008(5) ：45-47 + 51.
[15]Lakkonavar V, Kavi S and Jones P, et al. Edge-Quality Effects on Mechanical Properties of Stamped Non-Oriented Electrical Steel [C] 〃 WCX SAE World Congress Experience, 2020.
[16]谢利，杨平.制备1100｝织构无取向电工钢方法综述[J].材料热处理学报,2013,12:947.
[17]Mazgaj W, Sierzega M and Szular Z. Approximation of Hysteresis Changes in Electrical Steel Sheets [J]. Energies, 2021,14(14)： 1-18.
[18]Ben T, Chen F Y and Chen L, et al. Magnetostrictive Model of Non-Oriented Electrical Steel Sheet Considering Force-Magnetic Coupling Effect] J], Zhongguo Diaiyi Gongcheng Xuebao. Proceedings of the Chinese Society of Electrical Engineering, 2021,41 (15):5361-5370.
[19]Nguyen D T, Ho J R and Tung, P C, et al. An Improved RealTime Temperature Control for Pulsed Laser Cutting of Non-Oriented Electrical Steel[J]. Optics and Laser Technology, 2021,136.
[20]Maeda Y, Urata S and Nakai H, et al. Study on Measuring Method of Magnetic Properties of an Electrical Steel Sheet in Applying Both in-Plane and Out-of-Plane Compressive Stress[J]. IEEJ Transactions on Fundamentals and Materials, 2021,141(5)339-344.