回火工艺对热轧U20Mn2SiCrNiMo贝氏体钢轨组织性能的影响

特殊钢 ›› 2021, Vol. 42 ›› Issue (6): 68-71.

回火工艺对热轧U20Mn2SiCrNiMo贝氏体钢轨组织性能的影响

杨维宇¹,何建中²,梁正伟²,李智丽²

1内蒙古包钢金属制造有限责任公司研发中心，包头 014010;
2内蒙古包钢钢联股份有限公司技术中心，包头014010

收稿日期:2021-04-02 出版日期:2021-12-23 发布日期:2022-01-03
通讯作者: 何健中
作者简介:杨维宇(1982-),男，硕士(2009年中北大学),高级工程师， 2006年中北大学(本科)毕业，新产品开发和失效分析。
基金资助:
国家重点研发计划资助(2017YFB0304504)

Effect of Tempering Process on Microstructure and Properties of Hot rolled U20Mn2SiCrNiMo Bainitic Rail Steel

Yang Weiyu¹，He Jianzhong²，Liang Zhengwei² ， Li Zhili²

1 Research Center of Metal Manufacture Co Ltd of Inner Mongolia Baotou Steel Union，Baotou 014010;
2 Technical Center of Inner Mongolia Baotou Steel Union Co Ltd,Baotou 014010

Received:2021-04-02 Published:2021-12-23 Online:2022-01-03

摘要/Abstract

摘要： U20Mn2SiCrNiMo贝氏体钢轨的生产流程为150 t 转炉-LF-VD-280 mm×380 mm铸坯轧制，终轧930~980 ℃,空冷-340 ℃ 4 h两次回火，空冷。U20Mn2SiCrNiMo钢热轧态(终轧930~980 ℃空冷）和(320 ℃一、二次回火)组织均由贝氏体、马氏体和残余奥氏体组成。力学性能试验结果表明：U20Mn2SiCrNiMo钢轨最佳回火工艺为320 ℃ 4 h空冷+320 ℃ 4 h空冷二次回火，其性能为：屈服强度1242 MPa，抗拉强度1393 MPa，HBW硬度值417，伸长率15.0%，断面收缩率60%，冲击吸收功K_U2 98 J，轨底纵向残余应力+180 MPa。

Abstract: The flowsheet process of U20Mn2SiCrNiMo bainitic rail steel is 150 t BOF-LF-VD-280 mm×380 mm cast bloom-rolling,finishing at 930～980℃,air cooling -340℃ 4 h,air cooling,double tempeing.The microstructure of hotrolled(end rolling at 930～980℃ air cooling)and tempered(320 ℃once-and double-tempering)of U20Mn2SiCrNiMo steel is composed of bainite, martensite and retained austenite.Mechenical properties test results show that the optimum tempering process of U20Mn2SiCrNiMo steel rail is 320℃4 h air cooling+320℃4 hair cooling,double tempeing,its yield strength is 1242 MPa,tensile strength 1393 MPa,HBW hardness 417,elongation 15.0%,reduction of area 60%,impact absorption work K_u2 is 98 J,and longitudinal residual stress of rail bottom +180 MPa.

杨维宇, 何建中, 梁正伟, 李智丽. 回火工艺对热轧U20Mn2SiCrNiMo贝氏体钢轨组织性能的影响[J]. 特殊钢, 2021, 42(6): 68-71.

Yang Weiyu, He Jianzhong, Liang Zhengwei , Li Zhili. Effect of Tempering Process on Microstructure and Properties of Hot rolled U20Mn2SiCrNiMo Bainitic Rail Steel[J]. Special Steel, 2021, 42(6): 68-71.