High   temperature   mechanical   properties   of grain-oriented   silicon   steel(0.027%C

3.06%Si) melting   by a  30 kg vacuum induction furnace  in lab and simulating 50mm thin slab casting and rolling process have been tested by Gleeble- 1500D   stress/strain   thermal   simulation   machine.Results   show   that   with   strain   rate   1×10

-3

s

-1

there   are   two  brittle  temperature zones for  the  test  steel

i.e.  I  brittle  zone-  melting  point  to  1300  ℃  and  Ⅲ  brittle  zone-  800～600 ℃. 1390~1410  ℃ is  crack  sensitive  range  of the  test  steel.  In  I brittle  zone  the  dentritic  crystal boundary  surrounded by liquid  film  of  rich  solute  is  main  reason  to  produce  brittlement.And  in  Ⅲ  brittle  zone

γ→α  transformation

y

α  and  Fe

3

C triple phase coexistence at about 760 ℃ and precipitates at grain boundary are main cause

of deterioration in ductility.