The    effect    of    quenching    temperature1025~1125℃+570℃4    h    air    cooling    +    720    ℃    2    h    air    cooling  and    secondary    tempering    temperature    680~780    ℃    after1050~1075    ℃    quenching    on    mechanical    properties    of    martensite  heat                     resistant                     steel                     X12CrMoWVNbN10- 1- 1(%:0. 11C

10.28Cr

0.77Ni

1.0Mo

0.96W

0. 18V

0.04Nb

0.053N)  has    been    studied.    Results    show    that    with    increasing    quenching    temperature

the    strength    of   steel    increases

of   which    the  plasticity    has    no    appreciable    change

but    the    impact    toughness    obviously    decreases;    with    increasing    tempering    temperature

  the   strength   of   steel   decreases

while   the   plasticity   and   impact   toughness   of   steel   increase.   The   optimizing   heat   treatment   of the     steel     is1050~1075℃1~2h     oil     cooling     +570℃4h     air     cooling     +715~725     ℃     2     h     air     cooling.