Quality Control of SWRH82B Steel Coil for Prestressed Wire at Xiangtan Steel

王贵容; 薛正良

您当前的位置：

首页 >

文章列表页 >

Quality Control of SWRH82B Steel Coil for Prestressed Wire at Xiangtan Steel

更新时间：2026-01-21

- Quality Control of SWRH82B Steel Coil for Prestressed Wire at Xiangtan Steel
- Special Steel Vol. 26, Issue 5, Pages: 44-47(2005)
- 作者机构：
  
  1. 湘潭钢铁集团公司,湘潭,411101
  2. 湖北省钢铁冶金重点实验室，武汉科技大学,武汉,430081
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：22 April 2005，
  
  Online First：04 April 2023，
  
  Published：04 April 2005
- 稿件说明：
移动端阅览
王贵容, 薛正良. Quality Control of SWRH82B Steel Coil for Prestressed Wire at Xiangtan Steel[J]. Special Steel, 2005, 26(5): 44-47.
DOI：

王贵容, 薛正良. Quality Control of SWRH82B Steel Coil for Prestressed Wire at Xiangtan Steel[J]. Special Steel, 2005, 26(5): 44-47. DOI：

摘要

湘钢采用铁水预处理-80t顶底复吹转炉-90 t LF-150 mm ×150 mm方坯连铸机-高速线材轧机成功开发出Φ11~13mm的预应力钢丝和钢绞线用钢SWRH82B(%:0.79~0.83C

0.70~0.80Mn

0.17~0.22Cr

≤0.020S

≤0.025P)盘条。实践表明

中间包钢水过热度控制在15~25(30)℃

拉坯速度2.6~2.9m/min

拉坯速度波动值≤0.2m/min

二冷水量1.95~2.10L/kg

可使铸坯中心碳偏析比(铸坯中心碳含量/钢水碳含量)≤1.04

盘条索氏体率≥85%

实际拉拔和捻股过程中10

m的断丝率≤1次。

Abstract

The φ11~13 mm SWRH82B steel coil(0.79~0.83C

0.70～0.80Mn

0. 17~0.22Cr

≤0.020S

≤0.025P) for prestressed steel wire and stranded wire has been successfully developed by hot metal pretreatment - 80 t top and bottom combined blown converter - 150 mm×150 mm billet concasting-high speed wire-rod mill process at Xiangtan Steel.The production practice with overheating temperature of liquid steel in tundish controlled between 15 ℃ and 25(30) ℃

casting speed 2.6~2.9 m/min

vibrated value of casting speed ≤ 0.2 m/min

and amount of secondary water cooling between 1.95 L/kg and 2.10 L/kg

the centre carbon segregation ratio of billet(carbon content at centre of billet / carbon content of liquid steel) shall be ≤ 1.04

the sorbite proportion of SWRH82B steel coil ≥ 85%

and during 10000 m drawing and stranding procedure the wire broken ratio ≤ one time.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Quality Control of Bar Products of Bearing Steel Produced by Consteel EAF-LF(VD)-CC Process at Wuhan Iron and Steel

Development and Application of Premelted Slag for Electroslag Remelting Process

Forming Reason and Process Improvement of Seab Defects Rolled Boron-bearing Cold Heading Steel 10B21

Production Practice of Improving Surface Quality of Corrosion Resistant Steel G7624 by Optimizing Concasting Parameters and Chemical Composition

Related Author

张贤忠

陈庆丰

谈知良

韦泽宏

徐冠宇

熊玉彰

姜周华

董艳伍

Related Institution

武钢研究院

武钢鄂钢公司

东北大学材料与冶金学院

邯郸钢铁集团有限责任公司冷轧厂

邯郸钢铁集团有限责任公司一炼钢厂

⁰