An Analysis on Surface Temperature of Concasting Profiled Beam Blank of Nb Microalloying Steel

刘建华; 包燕平; 张军; 杜松林; 汤寅波; 李建中

您当前的位置：

首页 >

文章列表页 >

An Analysis on Surface Temperature of Concasting Profiled Beam Blank of Nb Microalloying Steel

更新时间：2026-01-21

- An Analysis on Surface Temperature of Concasting Profiled Beam Blank of Nb Microalloying Steel
- Special Steel Vol. 26, Issue 3, Pages: 51-53(2005)
- 作者机构：
  
  北京科技大学冶金与生态工程学院，北京100083 马鞍山钢铁股份有限公司,马鞍山,243003
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：29 November 2004，
  
  Online First：29 May 2023，
  
  Published：29 May 2005
- 稿件说明：
移动端阅览
刘建华, 包燕平, 张军, et al. An Analysis on Surface Temperature of Concasting Profiled Beam Blank of Nb Microalloying Steel[J]. Special Steel, 2005, 26(3): 51-53.
DOI：

刘建华, 包燕平, 张军, et al. An Analysis on Surface Temperature of Concasting Profiled Beam Blank of Nb Microalloying Steel[J]. Special Steel, 2005, 26(3): 51-53. DOI：

摘要

采用CIT-M型红外测温线性化传感器测定了马钢Nb 微合金化钢 SM490YB(%:0.09～0. 13C

1.35～1.50Mn

0.04～0.06Nb)异型坯在连铸过程中的表面温度，结果表明异型坯横向表面温度不均匀；在二冷区测量位置和矫直区，铸坯表面温度基本处于SM490YB钢的低温脆性区(650～750℃);在二冷2段由于支撑棍间间隔喷水冷却，温度回复大于冶金规则允许的最大限度100 ℃/m。SM490YB异型坯浇铸应采用弱冷工艺，同时调整冷却喷嘴的布置，以提高异型坯表面质量。

Abstract

The surface temperature of profiled beam blank of Nb microalloying steel SM490YB-0.09～0. 13C

1.35 ~1.50Mn

0.04～0.06Nb during concasting by CIT-M Infrared Pyrometer. The results showed that the traverse surface temperature of beam blank was uneven

the surface temperature of beam at measured location in secondary cooling and straightening area were generally in the brittle low temperature range between 650 ℃ and 750℃ of steel SM490YB; and due to interval water spraying cooling between supporting rollers

the re-rise rate of temperature of beam surface between some supporting rollers in secondary cooling area was higher than 100 ℃/m the limits of metallurgical rules. It shall be to adopt weakening cooling process during casting profiled beam and adjust distribution of spraying nomles in order to increase the surface quality of profiled beam.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Math Model and Application for Heat Transfer during Solidification of Concasting Round Bloom

Related Author

唐海燕

李京社

韩丽敏

温德松

Related Institution

北京科技大学冶金与生态工程学院

天津钢管集团有限公司炼钢厂

⁰