Influence of Annealing Temperature on Structure,Texture and Magnetic Properties of Cold Rolled Non-Oriented Silicon Steel

张文康; 毛卫民; 白志浩

您当前的位置：

首页 >

文章列表页 >

Influence of Annealing Temperature on Structure,Texture and Magnetic Properties of Cold Rolled Non-Oriented Silicon Steel

更新时间：2026-01-21

- Influence of Annealing Temperature on Structure,Texture and Magnetic Properties of Cold Rolled Non-Oriented Silicon Steel
- Special Steel Vol. 27, Issue 1, Pages: 15-17(2006)
- 作者机构：
  
  1. 太原钢铁(集团)有限公司技术中心,太原,030003
  2. 北京科技大学材料科学系,北京,100083
  3. 上海电大南汇分校,上海,201300
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：28 July 2005，
  
  Online First：01 February 2006，
  
  Published：01 February 2006
- 稿件说明：
移动端阅览
张文康, 毛卫民, 白志浩. Influence of Annealing Temperature on Structure,Texture and Magnetic Properties of Cold Rolled Non-Oriented Silicon Steel[J]. Special Steel, 2006, 27(1): 15-17.
DOI：

张文康, 毛卫民, 白志浩. Influence of Annealing Temperature on Structure,Texture and Magnetic Properties of Cold Rolled Non-Oriented Silicon Steel[J]. Special Steel, 2006, 27(1): 15-17. DOI：

摘要

研究了成分为0.003%C- 1.6%Si的0.5mm无取向冷轧板850～1000℃退火后的晶粒、织构、铁损和磁感应强度。试验结果表明，随退火温度增高，晶粒的平均尺寸由850 ℃23μm 增加至1000℃115 pm

铁损由850℃4.36 W/kg降低至1000℃3.35W/kg

磁感应强度在920℃退火达到最大值1.732 T。随退火温度继续升高，磁感应强度逐渐降低至1000℃1.717 T

Abstract

The grain size

texture

iron loss and magnetic induction of 0.5 mm 0.003C- 1.6Si non-oriented silicon steel cold rolled sheet annealed at 850~1000 ℃ have been studied.The test results showed that with annealing temperature increasing the average grain size increased from 23 μm at 850 ℃ to 115 pm at 1000 ℃

the iron loss decreased from 4.36 W/kg at 850 ℃ to 3.35 W/kg at 1000 ℃;and the magnetic induction was up to maximum value 1.732 T at 920℃

with annealing temperature further increasing the magnetic induction gradually decreased to 1.717 T at 1000 ℃

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

A Study on Decarburization Trend of New High Strength and Toughness Spring Steels 40T and 44T

A Study on Oxygen Contamination from Crucible Material on Molten Steel during Vacuum Induction Melting

Metallurgy Technology for Ultra-Low Carbon and UItra- Low Nitrogen Steel

Effect of Heat Treatment on Properties of High Strength Spring Steel 60SiCrV7

Practice of Free Cutting Steel 35MnVS Steelmaking by 30t EAF-40t LF

Related Author

尹钟大

徐德祥

刘德富

薛正良

高俊波

齐江华

李正邦

张家雯

Related Institution

哈尔滨工业大学

武汉钢铁(集团)公司技术中心

东北特钢集团北满特殊钢有限责任公司

新疆八一钢铁股份公司板带指挥部

本溪钢铁集团公司

⁰