Effect of Heat Treatment  and Hot Deformation on Carbide in High Speed Steel M2 Cast-Strip

张彩东; 丁培道; 周守则; 杨春楣

您当前的位置：

首页 >

文章列表页 >

Effect of Heat Treatment and Hot Deformation on Carbide in High Speed Steel M2 Cast-Strip

更新时间：2026-01-21

- Effect of Heat Treatment and Hot Deformation on Carbide in High Speed Steel M2 Cast-Strip
- Special Steel Vol. 27, Issue 6, Pages: 18-20(2006)
- 作者机构：
  
  重庆大学材料科学与工程学院,重庆,400044
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：16 May 2006，
  
  Online First：01 March 2023，
  
  Published：01 March 2006
- 稿件说明：
移动端阅览
张彩东, 丁培道, 周守则, et al. Effect of Heat Treatment and Hot Deformation on Carbide in High Speed Steel M2 Cast-Strip[J]. Special Steel, 2006, 27(6): 18-20.
DOI：

张彩东, 丁培道, 周守则, et al. Effect of Heat Treatment and Hot Deformation on Carbide in High Speed Steel M2 Cast-Strip[J]. Special Steel, 2006, 27(6): 18-20. DOI：

摘要

用定量金相法研究了Gleeble1500D自动热模拟机1200℃热处理和1050～950℃40%～60%热变形对3mmM2(W6Mo5Cr4V2)高速钢铸带中碳化物直径

体积分数的影响。研究结果表明

高温热处理和热变形可细化M2钢铸带中的碳化物尺寸

改善碳化物分布;1200℃40min热处理+50%热变形可得到较细的碳化物(0.96μm)和均匀的分布。

Abstract

The effect of 1200 ℃ heat treatment and 40%～60% hot deformation at 1050~950℃ on diameters and volume fraction of carbide in 3 mm cast-strip of high speed steel M2(W6Mo5Cr4V2)using Gleeble 1500D auto thermo- simulation machine have been studied by quantitative metallographic examination. The studied results showed that the car bide size in steel M2 was fined and distribution of carbide was improved in cast-strip by high temperature heat treatment and hot deformation

and 1200 ℃ 40 min heat treatment + 50% hot deformation was available to get fine carbide(0.96 μm) and homogeneous distribution.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Grain Growth Behavior of Nickel-based Superalloy GH3230

The As-Cast Microstructure and Solidification Segregation Behavior of GH5188 Alloy Produced by VIM+ESR Dual Melting Process

Hot Deformation Behavior and Microstructure Evolution of Fe-Mn-Al-C Lightweight Steel Containing Ni

Control of Carbides and Process Optimization in the Direct Rolling Process of Cr12MoV Flat Steel

Development Process of Cutter Ring for Shield Machine/Tunnel Boring Machine （TBM） Hob

Related Author

Zhen Xingmin

Kou Jinfeng

Bai Yaguan

Nie Yihong

Shang Shuming

Zhang Bingbing

Zhang Xin

Zhou Yun

Related Institution

Capital Aerospace Machinery Co.， Ltd.

China First Heavy Industries

Tianjin Heavy Industries Research & Development Co.， Ltd.

Heilongjiang Provincial Key Laboratory of Intelligent Manufacturing for Advanced Nuclear Power Equipment

School of Materials and Metallurgy， University of Science and Technology Liaoning

⁰