Influence of Hot Rolling Process on Magnetic Properties of Cold Rolled Non-Oriented  Silicon Steel 50W600

夏兆所; 康永林

您当前的位置：

首页 >

文章列表页 >

Influence of Hot Rolling Process on Magnetic Properties of Cold Rolled Non-Oriented Silicon Steel 50W600

更新时间：2026-01-21

- Influence of Hot Rolling Process on Magnetic Properties of Cold Rolled Non-Oriented Silicon Steel 50W600
- Special Steel Vol. 27, Issue 6, Pages: 47-49(2006)
- 作者机构：
  
  北京科技大学新金属材料国家重点实验室,北京,100083
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：02 June 2006，
  
  Online First：02 March 2023，
  
  Published：02 March 2006
- 稿件说明：
移动端阅览
夏兆所, 康永林. Influence of Hot Rolling Process on Magnetic Properties of Cold Rolled Non-Oriented Silicon Steel 50W600[J]. Special Steel, 2006, 27(6): 47-49.
DOI：

夏兆所, 康永林. Influence of Hot Rolling Process on Magnetic Properties of Cold Rolled Non-Oriented Silicon Steel 50W600[J]. Special Steel, 2006, 27(6): 47-49. DOI：

摘要

试验了180mm铸坯加热温度(1200℃、1180℃)、2.3mm热轧卷轧制道次(7道次、5道次)、精轧终轧温度(780～860℃)和卷取温度(≤710℃)对0.5mm冷轧无取向硅钢50W600的铁损和磁感应强度的影响。结果表明

降低铸坯加热温度

提高终轧温度和卷取温度

有利于改善该冷轧无取向硅钢成品的磁性能;而粗轧道次对成品磁性能无明显影响。

Abstract

The influence of heating temperature(1200 ℃

1180℃)of 180 mm cast slab

rolling passes for 2.3 mm hot coil(7 pass and 5 pass)

finishing rolling temperature(780~860℃)and coil temperature(≤710℃)on iron loss and magnetic intensity of 0.5 mm cold rolled non-oriented silicon steel 50W600 has been tested. The results showed that decreasing heat temperature of cast slab

increasing finishing rolling temperature and coiling temperature were available to improve magnetic properties of the cold rolled non-oriented silicon steel; while the rolling passes had no significant influence on magnetic properties of steel products.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Effect of Forging Process on Microstructure and Properties of Fe10Cr10Co Soft Magnetic Alloy

Effect of Aging Rolling Temperature on the Microstructure， Texture and Magnetic Properties of Low-temperature Grain-oriented Silicon Steel

Preparation of 6.5%Si High Silicon Steel by Pack Rolling Method and its Performance Characteristics

Effect of Normalizing Temperature of Hot Rolled Plate on Structure and properties of 3.0Si Non-Oriented Electric Steel

Effect of Product Thickness on Texture and Magnetic Properties of Non-Oriented Silicon Steel

Related Author

Han Zhongjian

Li Zhu

Ma Jing

Wang Yanmou

Liu Jie

Liu Huidan

Yin Licheng

Zhu Jiqiao

Related Institution

Xi'an Gangyan Special Alloy Co.，Ltd

Hongwang Holding Group， Hunan Hongwang New Material Technology

The State Key Laboratory of Refractories and Metallurgy， Wuhan University of Science and Technology

College of Material Science and Engineering， Shenzhen University

Putian Low-Carbon Industry Research Institute， Wuxi Putian Iron Core Co.， Ltd.

⁰