A Study on Water Model for Circulation Flow Rate Optimization in RH Degassing Refining

艾新港; 包燕平; 吴华杰; 马鑫; 贾楠

您当前的位置：

首页 >

文章列表页 >

A Study on Water Model for Circulation Flow Rate Optimization in RH Degassing Refining

更新时间：2026-01-21

- A Study on Water Model for Circulation Flow Rate Optimization in RH Degassing Refining
- Special Steel Vol. 30, Issue 3, Pages: 1-3(2009)
- 作者机构：
  
  北京科技大学冶金与生态工程学院,北京,100083
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：26 November 2008，
  
  Online First：22 November 2022，
  
  Published：22 November 2009
- 稿件说明：
移动端阅览
艾新港, 包燕平, 吴华杰, et al. A Study on Water Model for Circulation Flow Rate Optimization in RH Degassing Refining[J]. Special Steel, 2009, 30(3): 1-3.
DOI：

艾新港, 包燕平, 吴华杰, et al. A Study on Water Model for Circulation Flow Rate Optimization in RH Degassing Refining[J]. Special Steel, 2009, 30(3): 1-3. DOI：

摘要

以70 t钢包RH精炼装置为原型建立了1:3.27水模型

用流速法测量RH循环流量。分析了实际工艺条件下钢水的RH循环流量以及上升管吹气量、吹气孔内径、吹气孔高度、浸渍管插入深度等参数对RH循环流量的影响

并得出优化工艺参数。70 t钢包RH精炼实验结果表明

当上升管吹气量1 200 L/min

吹气孔内径3 mm时

轴承钢平均[O

]

比原工艺降低3×10

-6

超低碳钢碳含量可降低到0.002%以下

脱碳时间比优化前明显减少。

Abstract

A water model with linear scale 1 ; 3. 27 for a 70 t ladle RH unit has been established by using flow rale methed to measure RH circulation rate. RH circulation rate of liquid steel in real process condition and effect of parameters such as blow rate in up-gas tube

inner diameter of orifice T blowing up-gas traveling path and dipping depth of leg on RH circulation rate were analyzed to get optimizing process parameters. The commercial test of a 70 t ladle RH degassing refining showed that with blow rate 1 200 L/min in up-gas tube and inner diameter 3 mm of orifice

average [0

]

of bearing steel decreased by 3 X 10

-6

as compared that with original process ； carbon content of extra-low carbon steel might decrease to less than 0. 002% and decarburization time obviously decreased as compared with that before optimization.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Water Modelling for a 85 t Top-Bottom Combined Blown Converter at Chongqing Steel

Preventive Measures of Widmanstatten Structure of 0.45 % C Steel for Automobile Piston Rod and Process Optimization

Water Modelling Test on Interaction between Bottom Injection Gas and Bath for an 180 t Converter#br#

Process Optimization Steel 30CrMnSiA Production by EAF+LF(VD)-ESR Combined Process

Physical and Mathematical Study on Flow Control Device of Tundish for 5-Strand billet Casting at Chongqing Steel

Related Author

鱼洋洋

唐萍

周亮

龙贻菊

陈文满

梁庆

安昌遐

李合意

Related Institution

重庆钢铁公司炼钢厂

重庆大学材料科学与工程学院

河南济源钢铁(集团)有限公司

辽宁科技大学材料学院，鞍山4

大冶特殊钢股份有限公司

⁰