Effect of Product Thickness on Texture and Magnetic Properties of Non-Oriented Silicon Steel

董爱锋; 苗晓; 申毅; 张文康

您当前的位置：

首页 >

文章列表页 >

Effect of Product Thickness on Texture and Magnetic Properties of Non-Oriented Silicon Steel

更新时间：2026-01-21

- Effect of Product Thickness on Texture and Magnetic Properties of Non-Oriented Silicon Steel
- Special Steel Vol. 30, Issue 5, Pages: 42-44(2009)
- 作者机构：
  
  太原钢铁(集团)冇限公司技术中心,太原,030003
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：10 March 2009，
  
  Online First：18 November 2022，
  
  Published：18 November 2009
- 稿件说明：
移动端阅览
董爱锋, 苗晓, 申毅, et al. Effect of Product Thickness on Texture and Magnetic Properties of Non-Oriented Silicon Steel[J]. Special Steel, 2009, 30(5): 42-44.
DOI：

董爱锋, 苗晓, 申毅, et al. Effect of Product Thickness on Texture and Magnetic Properties of Non-Oriented Silicon Steel[J]. Special Steel, 2009, 30(5): 42-44. DOI：

摘要

研究了成品板厚度(0.35～0.65 mm)对0.003%C-2.40%Si-0.32%Al无取向硅钢织构演变、磁感和铁损的影响。结果表明

随着钢板厚度的减薄

成品中对磁性不利的织构组分增加

有利织构组分减少

磁感降低。在化学成分和晶粒尺寸一定的情况下

影响铁损的主要因素是钢板厚度

钢板厚度从0.65 mm减薄至0.35 mm时

铁损显著降低。

Abstract

The effect of product thickness (0.35 ~0.65 mm) of sheet on texture

magnetic induction and core less of 0. 003% C-2.40% Si-0.32% Al non-oriented silicon steel sheet have been studied. Results showed that with decreasing the thickness of sheet

the component of unfavorable texture in products to magnetic properties increased

the component of favorable texture decreased led to decreasing magnetic induction； in conditions of definite chemical composition and grain size of steel

the major factor to influence core loss was thickness of steel sheet

as the thickness decreased from 0.65 mm to 0.35 mm

the core loss decreased obviously.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Effect of Aging Rolling Temperature on the Microstructure， Texture and Magnetic Properties of Low-temperature Grain-oriented Silicon Steel

Evolution of Asynchronous Cold Rolling Texture in Thickness Direction of Non-Oriented Silicon Electric Steel

Effect of Cr on Magnetic Properties of Non-Oriented Silicon Steel

Effect of Original Structure of Hot Rolled Plate on Texture Evolution of Cold Rolled Non-Oriented Silicon Steel

Impact of the Annealing Temperature on the Magnetic and Mechanical Characteristics of Thin-gauge Non-oriented Electrical Steel

Related Author

Liu Huidan

Yin Licheng

Zhu Jiqiao

Liu Jing

Cheng Zhaoyang

Dai Huilei

张正贵

刘沿东

Related Institution

Hongwang Holding Group， Hunan Hongwang New Material Technology

The State Key Laboratory of Refractories and Metallurgy， Wuhan University of Science and Technology

College of Material Science and Engineering， Shenzhen University

沈阳大学机械工程学院材料系

东北大学材料与冶金学院

⁰