Simulation Calculation on 250 ~ 320 mm Casting Slab during Stacking Slow Cooling Process

王卫华; 王文军; 刘洋; 陈霞

您当前的位置：

首页 >

文章列表页 >

Simulation Calculation on 250 ~ 320 mm Casting Slab during Stacking Slow Cooling Process

更新时间：2026-01-21

- Simulation Calculation on 250 ~ 320 mm Casting Slab during Stacking Slow Cooling Process
- Special Steel Vol. 34, Issue 1, Pages: 13-15(2013)
- 作者机构：
  
  首钢技术研究院,北京,100043
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：25 August 2012，
  
  Online First：13 September 2022，
  
  Published：13 September 2013
- 稿件说明：
移动端阅览
王卫华, 王文军, 刘洋, et al. Simulation Calculation on 250 ~ 320 mm Casting Slab during Stacking Slow Cooling Process[J]. Special Steel, 2013, 34(1): 13-15.
DOI：

王卫华, 王文军, 刘洋, et al. Simulation Calculation on 250 ~ 320 mm Casting Slab during Stacking Slow Cooling Process[J]. Special Steel, 2013, 34(1): 13-15. DOI：

摘要

L245、D36、X70等钢种连铸板坯生产流程为铁水预处理-100 t转炉-LF-RH-250～320 mm×2000 mm板坯连铸。当铸坯人炉温度为650～700℃

因AlN在晶界析出

在轧制过程钢板易出现爪裂

当铸坯入炉温度控制在500～550℃则可避免钢板爪裂。通过ANSYS有限元软件

对板坯堆垛温度场和降温速率进行数值模拟。模型计算结果表明

250 mm和320 mm厚铸坯分别堆垛12 h和24 h后

可使堆垛中心铸坯表面温度达到600℃以下

现场实测值与模拟结果相同。

Abstract

The casting flow sheet for slab of L245

D36 and X70 etc steel grades is metal pretreatment-100 t converter-LF-RH-250 ~320 x 2 000 mm slab casting. As temperature of charging casting slab is 650 〜700 °C

because of AIN precipitates at grain boundary the claw-cracks of steel plate easily occur

and as the temperature of charging slab is controlled at 500 ~ 550 V. the claw-cracks of steel plate are avoided. The numerical simulation on temperature field and temperature dropping rate of staking slab has been carried out by ANSYS finite element method software. The model calculation results show that as 250 mm slab and 320 mm slab are respectively stacked for 12 h and 24 h

the surface temperature of slab at centre of stacking is less than 600 ℃

and the measured value at production situation conforms to the simulation result.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Finite Element Numerical-Simulation and Analysis on BD2 Blooming Process of Heavy Rail Steel U75V

Nu merical Simulation of Temperature Field of 304 Stainless Steel Rod and Wire Hot Continuous Rolling

Numeric Simulation of Three-Dimensional Flow Field of Molten Steel in a Mould with High Efficiency Inner and Outer Couple Cooling

Numerical Simulation of Fluid Field of Molten Steel in Mold for 280 mm×380 mm Billet Concasting

Physical and Mathematical Study on Flow Control Device of Tundish for 5-Strand billet Casting at Chongqing Steel

Related Author

陈林

孙盛志

廖舒纶

于永泗

张立文

原思宇

江国栋

甑玉

Related Institution

内蒙古科技大学材料与冶金学院

太原科技大学工程力学系

辽宁科技大学材料学院

鞍山钢铁集团技术中心

重庆大学材料科学与工程学院

⁰