Quality Defects of H Section Steel Continuous Casting and Numerical Simulation for Structure Optimization of Submerged Nozzle

李小明; 史雷刚; 崔雅茹; 李文峰

您当前的位置：

首页 >

文章列表页 >

Quality Defects of H Section Steel Continuous Casting and Numerical Simulation for Structure Optimization of Submerged Nozzle

更新时间：2026-01-21

- Quality Defects of H Section Steel Continuous Casting and Numerical Simulation for Structure Optimization of Submerged Nozzle
- Special Steel Vol. 34, Issue 5, Pages: 9-12(2013)
- 作者机构：
  
  西安建筑科技大学冶金学院,西安,710055
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：13 April 2013，
  
  Online First：19 September 2022，
  
  Published：19 September 2013
- 稿件说明：
移动端阅览
李小明, 史雷刚, 崔雅茹, et al. Quality Defects of H Section Steel Continuous Casting and Numerical Simulation for Structure Optimization of Submerged Nozzle[J]. Special Steel, 2013, 34(5): 9-12.
DOI：

李小明, 史雷刚, 崔雅茹, et al. Quality Defects of H Section Steel Continuous Casting and Numerical Simulation for Structure Optimization of Submerged Nozzle[J]. Special Steel, 2013, 34(5): 9-12. DOI：

摘要

研究的H型钢Q235(/%:0.06c，0.30si，1.60Mn，0.010P，0.003S，0.025Mo，0.40Ni，0.017Ti，0.15Cu)由80 t LD-LF-喂硅钙线-28 t中间包-430 mm×300 mm×85 mm H型连铸一热轧工艺生产。由于H型铸坯易产生纵裂纹缺陷

根据H型连铸坯采用直通型浸入式双水口浇铸的实际工艺参数建立数学模型

采用流体有限元软件CFD进行结晶器流场和温度场分布汁算

得出直通型双水口浇铸时

熔池冲击深度大

不利夹杂上浮;液面得不到足够热量补充

导致坯壳过早凝固

不利于化渣。数值模拟结果表明

改用三侧孔水口进行浇铸

避免了直通型水口的不利因素

流场和温度场分布合理

可降低漏钢事故和裂纹发生的机率。

Abstract

The tested H section steel Q235 (/% : 0.06C

0.30Si

1.60Mn

0.010P

0.003S

0.025Mo

0.40Ni

0.017Ti

0.15Cu) is produced by 80 t LD-LF-feeding silicon-calcium wire-28 t tundish-430 mm x 300 mm x 85 mm H section CC bloom-hot rolling process. Due to the longitudinal crack easily occurred on surface of H section steel bloom

based on real process parameters of through type double submerged nozzle for H section casting bloom

a mathematical model is established and the calculation of distribution of flow field and temperature field in mold is carried out by using fluid finite element simulation software CFD. It is obtained that with using through type double submerged nozzle the impact depth in pool is large that is unfavorable to inclusions floating off； and the liquid surface can't get enough heat supply led to bloom shell more earlier solidification and unfavorable to slag melting. The results of numerical simulation show that as casting by using modified three side nozzle

the unfavorable factors with using through nozzle are avoided

the distribution of flow field and temperature field is reasonable

and the possibility of bleeding trouble and occurrence of crack decreases.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Numerical Simulation of Fluid Flowing in Concasting Mould for Wide Slab

Numerical Simulation of Control Devices of Flow in a Two-Strand T-Shape 23 t Tundish and Structure Optimization

Numerical Simulation on Optimization of Inclination of Submerged Nozzle for 220mm x 1600mm Slab Casting and Application

Numerical Simulation of 80 mm Extra-thick Plate Stacking Slow Cooling for EH420 Marine Steel

Numerical Simulation of Solidification Structure for 4J36 Invar Alloy Ingot

Related Author

沈巧珍

朱必炼

王俊杰

杨运超

刘艳贺

贺铸

刘双

李黎

Related Institution

武汉科技大学钢铁冶金及资源利用省部共建教育部重点实验室

武汉钢铁(集团)公司第三炼钢厂

首钢技术研究院

绿色可循环钢铁流程北京市重点实验室

User Application Technology Research Institute， Citic Pacific Special Special Steel Group Co.，Ltd.， Jiangyin

⁰