Effect of Acid-Soluble Alirniinium Content on Characteristics of Inclusions in Silicon Killed Steel and Nozzle Clogging

郑万; 沈星; 李光强; 朱诚意; 吴振华; 屠浩; 卢凯

您当前的位置：

首页 >

文章列表页 >

Effect of Acid-Soluble Alirniinium Content on Characteristics of Inclusions in Silicon Killed Steel and Nozzle Clogging

更新时间：2026-01-21

- Effect of Acid-Soluble Alirniinium Content on Characteristics of Inclusions in Silicon Killed Steel and Nozzle Clogging
- Special Steel Vol. 35, Issue 1, Pages: 36-39(2014)
- 作者机构：
  
  1. 武汉科技大学钢铁冶金及资源利用省部共建教育部重点实验室,武汉,430081
  2. 武汉钢铁股份有限公司炼钢总厂,武汉,430083
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：28 August 2013，
  
  Online First：06 September 2022，
  
  Published：06 September 2014
- 稿件说明：
移动端阅览
郑万, 沈星, 李光强, et al. Effect of Acid-Soluble Alirniinium Content on Characteristics of Inclusions in Silicon Killed Steel and Nozzle Clogging[J]. Special Steel, 2014, 35(1): 36-39.
DOI：

郑万, 沈星, 李光强, et al. Effect of Acid-Soluble Alirniinium Content on Characteristics of Inclusions in Silicon Killed Steel and Nozzle Clogging[J]. Special Steel, 2014, 35(1): 36-39. DOI：

摘要

通过500 g MoSi

电阻炉熔炼试验考察了酸溶铝Als含量对硅镇静钢中夹杂物形貌、组成、数量及熔点的影响

并对KR铁水预处理-BOF-吹Ar-LF-CC流程现场水口残留物进行微观观察

探讨了夹杂物堵塞水口的机理

提出了硅镇静钢中铝含量的合理控制范围。结果表明

随Als含量增加硅镇静钢的夹杂物熔点升高

夹杂物数量减少;观察水口残留物为低熔点夹杂物镶嵌高熔点夹杂物

高Als钢中固态夹杂物以熔融态夹杂物为粘结剂聚集而粘附水口;钢液中Als含量控制在0.0030%~0.007 5%不会生成皮下气孔、不易水口堵塞。

Abstract

The effect of acid-soluble aluminium Als content in steel on morphology

ingredient

number and melting point of inclusions in silicon killed steel has been studied by 500 g MoSi

electric resistance furnace melting trial

and the micro-observation on residue of nozzle clogging at situ of KR metal pretreatment-BOF-Ar blowing-LF-CC process is carried out to explore the mechanism of nozzle clogging by inclusions and propose a reasonable control range of Als content in silicon killed steel. Results show that with increasing Als content in steel the melting point of inclusions in silicon killed steel increases and the number of inclusions decreases ； the observation on residue in nozzle gets that the high melting point inclusions are embedded in low melting point inclusions

it is indicated the solid inclusions in high Als steel are accumulated and adhered at nozzle

by molten inclusions which are coherent agent； the subskin blowhole shall not occurred and nozzle is not easily clogging as Als content in liquid is controlled in 0.003 0% ~0. 007 5%.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Process Practice to Control of Precipitation of TiN in ER70S-G Welding Wire Steel Containing Titanium and Prevent Nozzle Clogging

Analysis on Nozzle Clogging during Continuous Casting of Steel 38CrMoAl and Process Improvement

Related Author

杨咏阶

王郢

徐建飞

何西

王昆鹏

万文华

孙光涛

Related Institution

青岛钢铁控股集团有限责任公司炼钢总厂

中天钢铁集团有限公司技术中心

⁰