An Analysis on Cleanliness of Die Steel H13 Steelmaking by 40 t EBT EAF-LF-VD-Ingot Casting Process

庞永刚; 侯明山; 胡建成; 李士琦; 刘润藻; 王玉刚

您当前的位置：

首页 >

文章列表页 >

An Analysis on Cleanliness of Die Steel H13 Steelmaking by 40 t EBT EAF-LF-VD-Ingot Casting Process

更新时间：2026-01-21

- An Analysis on Cleanliness of Die Steel H13 Steelmaking by 40 t EBT EAF-LF-VD-Ingot Casting Process
- Special Steel Vol. 34, Issue 5, Pages: 61-63(2013)
- 作者机构：
  
  1. 北京科技大学冶金与生态工程学院,北京,100083
  2. 中原特钢股份有限公司,济源,454685
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：07 May 2013，
  
  Online First：22 September 2022，
  
  Published：22 September 2013
- 稿件说明：
移动端阅览
庞永刚, 侯明山, 胡建成, et al. An Analysis on Cleanliness of Die Steel H13 Steelmaking by 40 t EBT EAF-LF-VD-Ingot Casting Process[J]. Special Steel, 2013, 34(5): 61-63.
DOI：

庞永刚, 侯明山, 胡建成, et al. An Analysis on Cleanliness of Die Steel H13 Steelmaking by 40 t EBT EAF-LF-VD-Ingot Casting Process[J]. Special Steel, 2013, 34(5): 61-63. DOI：

摘要

试验用热作模具钢H13(/%:0.36~0.38C、0.36~0.38Mn、0.89~0.91Si、0.007~0.010P、0.006~0.011s、5.10~5.15Cr、1.12~1.18Mo、0.84~0.89V)的冶炼工艺流程为40 t偏心炉底出钢电弧炉-钢包炉精炼-VD处理4.65 t铸锭工艺。通过对各冶炼工序钢水的总氧和氮含量-T[O

]

和[N

]

的分析以及钢中夹杂物的形貌和组成的分析

研究了该工艺流程生产的H13钢的洁净度。结果表明

经LF-VD精炼后H13钢中的平均总氧含量-T[O

]

为22×10

-6

平均氮含量-[N

]

为95×10

-6

Φ200 mm锻坯中夹杂主要以脱氧产物氧化铝为主

同时含有硫化锰等硫化物和偏析产生的氮化物;夹杂物尺寸集中在5μm左右

较大尺寸的夹杂物为10μm左右。采用该流程冶炼的H13钢可以满足对该钢种洁净度的要求。

Abstract

The steelmaking process for test hot working die steel H13 (/% : 0.36-0.38C

0.36-0.38Mn

0.89-0.91Si

0.007-0.010P

0.006-0.011S

5.10-5.15Cr

1.12-1.18Mo

0.84-0.89V) is 40 t eccentric bottom tapping arc furnace-ladle furnace refining-VD treatment-4. 65 t ingot casting process. With analysis on total oxygen and nitrogen content in liquid- T [O

]

and [ N

]

and analysis on morphology and ingredient of inclusions in steel

the cleanliness of steel H13 produced by this process flow sheet has been studied. Results show that after refining by LF-VD process the average total oxygen content in steel H13- T[O

]

is 22 x 10

-6

and the average nitrogen- [N

]

is 95 x 10

-6

the main inclusions in Φ200 mm forging are deoxidation products- alum

inium oxide with sulHdes including manganese sulfide and nitride formed by segregation ； the sizes of inclusions are mainly about 5 μm

the sizes of some inclusions can come up to about 10 μm. The steel H13 steelmaking by this flow sheet could meet the requirement for cleanliness of that steel grade.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Effect of Refining Slag Basicity on the Molten Steel Cleanliness of GCr15SiMn Bearing Steel

Effect of Adding Direct Reduced Iron to EAF on Steelmaking

Effect of Current on the Cleanliness of Electroslag Ingots During Low Frequency Electroslag Remelting

Effect of La-Ce Rare Earth on Inclusions and Impact Properties of Q345D Steel

Research on the Production Practice of 09CuPCrNi Weather Resistant Steel

Related Author

Zhang Guolei

Guo Yunfei

Qiu Mian

Chen Gang

Cheng Guoguang

Zhang Tao

Nian Baoguo

Liu Chong

Related Institution

State Key Laboratory of Advanced Metallurgy， University of Science and Technology Beijing

Shanxi Taizhong Intelligent Equipment Co.， Ltd.

State Key Laboratory of Intelligent Mining Equipment Technology

HBIS Group Zhangxuan Technology，Xuanhua

HBIS Material Technology Research Institute

⁰