Development and Application of Mold Powder for Free-Cutting Steel X1215 Casting

闫卫兵; 林腾昌; 邢薇; 王成杰; 王宏斌

您当前的位置：

首页 >

文章列表页 >

Development and Application of Mold Powder for Free-Cutting Steel X1215 Casting

更新时间：2026-01-21

- Development and Application of Mold Powder for Free-Cutting Steel X1215 Casting
- Special Steel Vol. 34, Issue 3, Pages: 53-55(2013)
- 作者机构：
  
  1. 河北钢铁集团宣化有限公司炼钢厂，宣化,075100
  2. 北京科技大学冶金与生态工程学院,北京,100083
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：31 December 2012，
  
  Online First：21 September 2022，
  
  Published：21 September 2013
- 稿件说明：
移动端阅览
闫卫兵, 林腾昌, 邢薇, et al. Development and Application of Mold Powder for Free-Cutting Steel X1215 Casting[J]. Special Steel, 2013, 34(3): 53-55.
DOI：

闫卫兵, 林腾昌, 邢薇, et al. Development and Application of Mold Powder for Free-Cutting Steel X1215 Casting[J]. Special Steel, 2013, 34(3): 53-55. DOI：

摘要

根据炼钢厂现有结晶器保护渣FRK-2和FRK-49性能分析的结果

以FRK-2保护渣(/%:32.68SiO

、24.42CaO、3.30MgO、9.52Al

、5.40Na

O、3.10Fe

、3.59F

、12.60C)为基础开发了较高碱度

保温效果好

较低粘度

有一定还原性以降低弯月面处S和O含量

并避免卷渣的X1215易切削钢(/%:0.06～0.09C、≤0.10Si、1.20～1.50Mn、0.08～0.10P、0.30～0.50S)150 mm×150 mm铸坯连铸结晶器保护渣。生产结果表明

保护渣性能达到X1215低碳高硫易切削钢的生产要求;连铸坯合金元素偏析度均为0.90～1.10

S和Mn偏析度分别为0.95～1.05和0.98～1.03

连铸坯内部质量良好。

Abstract

According to the results of analysis on performance of present mold powder FRK-2 and FRK-49 at steel works

based on mold powder FRK-2 (/% ： 32. 68SiO

24.42CaO

3. 30MgO

9. 52Al

5.40Na

3. 10Fe

3. 59F

12. 60C) a mold powder for casting 150 mm x 150 mm billet of free cutting steel X1215 (/% ： 0. 06 ~0. 09C

≤ 0. 10Si

1. 20 ~ 1. 50Mn

0. 08 ~0. 10P

0. 30 ~0. 50S) with higher basicity

nice holding effect

lower viscosity and definite reducing capacity to decrease S and 0 content in liquid at meniscus and avoiding slag entrapment has been developed. Production results show that the performance of mold powder meets the requirement for production of low carbon and high sulfur fre

e cutting steel X1215; the segregation index of alloy elements in steel is 0. 90 ~ 1. 10

the segregation index of S and Mn is respectively 0. 95 - 1. 05 and 0. 98 - 1. 03 ； and the billet has nice internal quality.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

A Study on Mold Powder for High Aluminium Austenite Non-Magnetic Steel 20Mn23Al2V Slab Casting

Production Practice of Avoiding Raw and Supplement Materials on Increase Carbon in MA Ultra-Low Carbon Steel Liquid during KB-150 t BOF-RH-CC Flowsheet

Process Practice of Improvement on Surface Quality of 150 mm x 150 mm Casting Billet of Martensite Stainless Steel 2Cr13

Analysis on Cold Drawing Fracture Cause of B7 Steel Rod Coil and Process Improvement

Related Author

文光华

于雄

唐萍

张宇斌

邓品团

盛喜松

邱雷

宋佳霖

Related Institution

山西太钢不锈钢股份有限公司技术中心

重庆大学材料科学与工程学院

武汉科技大学钢铁冶金及资源利用省部共建教育部重点实验室

武汉钢铁(集团)公司

北京科技大学钢铁冶金新技术国家重点实验室

⁰