Development of Direct Quenching 800 MPa High Strength Low Alloy Steel Plate

王世森; 余宏伟; 张云燕; 李德发; 熊涛

您当前的位置：

首页 >

文章列表页 >

Development of Direct Quenching 800 MPa High Strength Low Alloy Steel Plate

更新时间：2026-01-21

- Development of Direct Quenching 800 MPa High Strength Low Alloy Steel Plate
- Special Steel Vol. 34, Issue 4, Pages: 53-55(2013)
- 作者机构：
  
  1. 武汉钢铁集团研究院,武汉,430080
  2. 武汉钢铁集团鄂城钢铁有限责任公司技术中心,鄂州,436002
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：21 February 2013，
  
  Online First：11 September 2022，
  
  Published：11 September 2013
- 稿件说明：
移动端阅览
王世森, 余宏伟, 张云燕, et al. Development of Direct Quenching 800 MPa High Strength Low Alloy Steel Plate[J]. Special Steel, 2013, 34(4): 53-55.
DOI：

王世森, 余宏伟, 张云燕, et al. Development of Direct Quenching 800 MPa High Strength Low Alloy Steel Plate[J]. Special Steel, 2013, 34(4): 53-55. DOI：

摘要

开发的20 mm低成本铌钛硼微合金化低碳钢板(/%:0.06C、0.40Si、1.60Mn、0.010P、0.005S、0.050Nb、0.012Ti、0.002B)的生产流程为130 t顶底复吹转炉-LF-RH-250 mm板坯连铸-4300轧机轧制-直接淬火-回火工艺。通过终轧≥900℃

以≥20℃/s冷却速度直接淬火

500℃回火

20 mm钢板抗拉强度R

为855 MPa

屈服强度R

0.2771 MPa

延长率A 16%

0℃冲击功A

kv2

217～238J

-40℃ A

kv2

137～181J。该钢的回火组织为细小的贝氏体板条

宽度为0.5～1.0μm

并有较多弥散分布的30～90 nm Nb+Ti碳氮化物析出。

Abstract

The production flow sheet for developed 20 mm low-cost niobium-titanium-boron microalloying low carbon steel plate (/% : 0. 06C

0. 40Si

1. 60Mn

0. 010P

0. 005S

0. 050Nb

0. 012Ti

0. 002B) is 130 t top and bottom combined blown converter-LF-RH-250 mm slab casting-4300 mill rolling-direct quenching-tempering process. With end rolling ≥ 900 °C

>20 °C./s direct quenching and tempering at 500 ℃ the tensile strength R

of the 20 mm steel plate is 855 MPa

yield strength R

0.2771 MPa

elongation A 16% impact energy A

KV2

at 0 °C 217 〜238 J and impact energy 4KV2 at -40

°C

137 〜181 J. Tempered structure of the steel is fine bainite lath with width 0. 5 ~ 1. 0μm and there are lots of dispersed 30 ~90 nm Nb + Ti carbo-nitride precipitates.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Structure Feature and Strength-Toughness of High Grade Pipeline Steels

A Test for Optimization of Heat Treatment Process of High Strength Spring Steel 60Si2CrVAT

Research and Development of Low Welding Sensitiveness Low Carbon Bainite High Strength Steel Q800CFE Plate

Development of Material of Stainless Steel Die for New Environmental Protection Pulp Mold Products

Effect of Cooling Rate on Structure and Cold-Heading Crack of Ф6.5〜12mm Coil of Steel SCM435

Related Author

庄传晶

吉玲康

冯耀荣

赵文轸

霍春勇

张小立

李秋志

高国华

Related Institution

中国石油天然气集团公司管材研究所，石油管力学和环境行为重点实验室

西安交通大学材料科学与工程学院

北京科技大学材料科学与工程学院.

湖北新冶钢有限公司技术中心

广西职业技术学院机械系

⁰