Effect of Primary Recrystallization Annealing Process on Structure and Texture of 3%Si Oriented Silicon Steel

更新时间：2026-01-21

- Effect of Primary Recrystallization Annealing Process on Structure and Texture of 3%Si Oriented Silicon Steel
- Special Steel Vol. 35, Issue 3, Pages: 62-64(2014)
- 作者机构：
  
  武汉科技大学钢铁冶金及资源利用省部共建教育部重点实验室,武汉,430081
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：09 December 2013，
  
  Online First：02 September 2022，
  
  Published：02 September 2014
- 稿件说明：
移动端阅览
唐刚, 赵刚, 鲍思前, et al. Effect of Primary Recrystallization Annealing Process on Structure and Texture of 3%Si Oriented Silicon Steel[J]. Special Steel, 2014, 35(3): 62-64.
DOI：

唐刚, 赵刚, 鲍思前, et al. Effect of Primary Recrystallization Annealing Process on Structure and Texture of 3%Si Oriented Silicon Steel[J]. Special Steel, 2014, 35(3): 62-64. DOI：

摘要

试验研究了0.3 mm取向硅钢冷轧板(/%:0.046C

3.07Si

0.09Mn

0.029P

0.004S

0.005Al)的退火温度(760~880℃7 min)和退火时间(820℃3~9 min)对该钢的晶粒尺寸

再结晶和织构的影响。结果表明

最佳初次再结晶退火工艺为820℃5 min

该钢的平均晶粒尺寸为14.20μm

完全再结晶率为92%

不利{111}<110>结构含量为3.16%

有利织构{111}<112>

{012}<001>和高斯织构含量分别0.40%

4.73%和2.46%。

Abstract

The effect of annealing temperature (at 760 ~ 880 ℃ for 7 min) and time (at 820 ℃ for 3 ~ 9 min) on grain size

recrystallization rate and texture of 0. 3 mm cold-rolled sheet of oriented silicon steel (/% : 0. 046C

3.07Si

0. 09Mn

0. 029P

0. 004S

0. 005Al) has been tested and studied. Results show that with optimum recrystallized annealing at 820 ℃ for 5 min

the silicon steel average grain size is 14. 20 the complete recrystallization rate is 92%

the unfavourable-texture {111} < 110 > content in steel is 3.16%

the favourable-texture {111} < 112 >

{012}<001 > and Gauss texture content in steel are respectively 0.40%

4.73% and 2.46%.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Effect of Hot-Rolled Plate Normalization Process on Structure and Properties of Annealed Cold-Rolled Sheet of Oriented Silicon Steel

Effect of Annealing Process and Cold Rolling Reduction on Texture of CSP Thin Sheet of Ultra-low Carbon Steel

Effect of Rare Earth Element on Structure and Magnetic Performance of Cold Rolled Non-Oriented Electrical Steel Products

Microstructure and Texture of Yttrium Bearing 3% Si Oriented Silicon Steel Fabricated by Thin Strip Casting Rolling Process

Influence of Cold Rolling Reduction and Annealing Temperature on Texture and Formability of Ti-IF Steel

Related Author

李黎

李方方

刘海霞

王宝昆

金自力

光红兵

张文康

辛宪诚

Related Institution

内蒙古科技大学材料与冶金学院

太原钢铁(集团)有限公司技术中心

河北科技大学材料科学与工程学院，河北省材料近净成形技术重点实验室

广西冶金研究院

武汉科技大学材料加工工程系

⁰