Heat Treatment Process of 245 mm Heavy Plate of Steel S500Q-Z35 for Seat Ring of Hydro-Power Station

唐郑磊; 许少普; 陆岳璋; 李忠波; 高照海; 杨阳

您当前的位置：

首页 >

文章列表页 >

Heat Treatment Process of 245 mm Heavy Plate of Steel S500Q-Z35 for Seat Ring of Hydro-Power Station

更新时间：2026-01-21

- Heat Treatment Process of 245 mm Heavy Plate of Steel S500Q-Z35 for Seat Ring of Hydro-Power Station
- Special Steel Vol. 36, Issue 3, Pages: 34-37(2015)
- 作者机构：
  
  1. 北京科技大学冶金与生态工程学院,北京,100083
  2. 南阳汉冶特钢有限公司钢研所,南阳,474500
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：03 December 2014，
  
  Online First：17 August 2022，
  
  Published：17 August 2015
- 稿件说明：
移动端阅览
唐郑磊, 许少普, 陆岳璋, et al. Heat Treatment Process of 245 mm Heavy Plate of Steel S500Q-Z35 for Seat Ring of Hydro-Power Station[J]. Special Steel, 2015, 36(3): 34-37.
DOI：

唐郑磊, 许少普, 陆岳璋, et al. Heat Treatment Process of 245 mm Heavy Plate of Steel S500Q-Z35 for Seat Ring of Hydro-Power Station[J]. Special Steel, 2015, 36(3): 34-37. DOI：

摘要

S500Q-Z35钢（%:0.13C

0.25Si

0.007P

0.001S

0.010Al

0.39Cr

0.92Ni

0.44Mn

0.02Nb

0.01Ti

0.54Ceq）245 mm板由KR脱硫铁水-120 t转炉-LF-VD-42t模铸-轧制-热处理工艺生产。根据控制钢的晶粒长大原理

测定的CCT曲线和临界厚度

以及工艺试验

得出S500Q-Z35钢245 mm特厚板经快速升温至930℃

保温2.0min/mm

快冷至670℃的预淬火

快速升温至880℃

保温2.4 min/mm

循环水+气体搅拌冷至室温的亚温淬火

620~630℃

保温4 min/mm

空冷至400℃压平的回火处理

钢板表面组织为索氏体

其他部位为回火贝氏体+铁素体

具有良好的综合机械性能

钢板Z向性能良好。

Abstract

245 mm plate of steel S500Q-Z35 (/% : 0. 13C

0. 25Si

0. 007P

0. 001S

0.010Al

0. 39Cr

0. 92Ni

0. 44Mo

0. 02Nb

0. 01Ti

54Ceq) is produced by KR desulphurized hot metal-120 t BOF-LF-VD-42 t ingot castingrolling-heat treatment process. According to principle of control of grain growth

the measuring CCT curves and critical thickness

as well as process test are carried out

it is obtained that with pre-quenching process-rapidly heating to 930 ℃ for 2. 0 min/mm

quickly cooling to 670 °C

the sub-critical quenching-rapidly heating to 880 ℃ for 2. 4 min/mm

with circle water + gas stirring cooling to ambient

and tempering treatment at 620 ~ 630 ℃ for 4 min/mm

air cooling to 400 ℃ and flatting

the surface structure of 245 mm heavy plate of steel S500Q-Z35 is sorbite

the structure in other parts is tempered bainite + ferrite

it has better comprehensive mechanical properties and has better properties of plate Z-direction.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Influence of Phosphorus Microalloying on Molidification， Hot Deformation and Mechanical Properties in Nickel/Nickel Iron-based Alloys

Effect of Heat Treatment on Mechanical Properties of High Strength Free-Cutting Precipitation Hardening Stainless Steel 2Cr16Ni3Mo2CuN

Effect of Quenching and Tempering Process on Mechanical Properties of Spring Steel 60Si2CrVAT

Structure and Mechanical Properties of Linepipe Steel X80

Production Practice of Steel 37CrMnMo for Coupling Sleeve of Petroleum Drill Stem

Related Author

Wu Yunsheng

Wu Hao

Zhao Yong

Pei Yubing

Wang Tianjian

Jiang Lei

Xu Ziyu

Gao Zhenhuan

Related Institution

State Key Laboratory of Clean and Efficient Turbomachinery Power Equipment

Dongfang Turbine Co.，Ltd.， Dongfang Electric Corporation

changxu Innovation Center for Advanced Materials， Institute of Metal Research， Chinese Academy of Sciences

江阴兴澄特种钢铁有限公司，江阴

中国石油天然气集团公司管材研究所

⁰