Effect of Annealing Temperature on Texture and Mechanical Properties of Stainless Steel 06Cr13 Cold-Rolled Sheet

田华; 刘有鹏; 薛润东; 李显龙; 袁凯; 刘谨; 赵志毅; 吴潮荣

您当前的位置：

首页 >

文章列表页 >

Effect of Annealing Temperature on Texture and Mechanical Properties of Stainless Steel 06Cr13 Cold-Rolled Sheet

更新时间：2026-01-21

- Effect of Annealing Temperature on Texture and Mechanical Properties of Stainless Steel 06Cr13 Cold-Rolled Sheet
- Special Steel Vol. 38, Issue 6, Pages: 56-59(2017)
- 作者机构：
  
  1. 北京科技大学材料科学与工程学院,北京,100083
  2. 广东宝嘉不锈钢实业有限公司,揭阳,515500
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：17 June 2017，
  
  Online First：15 July 2022，
  
  Published：15 July 2017
- 稿件说明：
移动端阅览
田华, 刘有鹏, 薛润东, et al. Effect of Annealing Temperature on Texture and Mechanical Properties of Stainless Steel 06Cr13 Cold-Rolled Sheet[J]. Special Steel, 2017, 38(6): 56-59.
DOI：

田华, 刘有鹏, 薛润东, et al. Effect of Annealing Temperature on Texture and Mechanical Properties of Stainless Steel 06Cr13 Cold-Rolled Sheet[J]. Special Steel, 2017, 38(6): 56-59. DOI：

摘要

06Cr13不锈钢（/%:0.03C

0.45Si

0.22Mn

0.020P

0.002S

12.20Cr）3.5mm热轧板经11道次冷轧成0.375mm冷轧板。利用CCT-AV-Ⅱ模拟退火实验机研究了800~925℃退火对06Cr13不锈钢冷轧板的织构组分和力学性能的影响。结果表明

随着退火温度的升高

深冲性能有利的{111}织构组分含量上升

而不利组分{001}<110>

{114}<110>

{112}<110>

{112}<111>和{110}<110>含量总和下降;在875℃退火时

{111}<110>与{111}<112>织构组分含量的差值最大

{111}织构的均匀性最差;06Cr13不锈钢的强度和延伸率在875℃退火后表现出很明显的各向异性。综合分析

该06Cr13不锈钢冷轧板的适合退火温度为（850±10）℃。

Abstract

The 3.5mm hot-rolled plate of stainless steel 06Cr13 (/%：0.03C

0.45Si

0.22Mn

0.020P

0.002S

12.20Cr) cold-rolls down to 0.375mm cold-rolled sheet by 11 passes. The effect of 800~925℃ annealing on texture ingredient and mechanical properties of stainless steel 06Cr13 cold-rolled sheet has been studied by using CCT-AV-Ⅱ simulation continuous annealing unit. Results show that with increasing annealing temperature the amount of {111} fiber texture being favourable for deep drawability increases

while the sum of amounts of {001}<110>

{114}<111>

{112}<110>

{112}<111> and {110}<110> texture being unfavourable for deep drawability decreases；as annealing at 875°C

difference between{111}<110> and {111}<112> texture ingredient is largest and the uniformity of {111} fiber texture is poorest；and the obvious anisotropy of strength and elongation of stainless steel 06Cr13 cold-rolledtor sheet annealed at 875℃ occurs. Based on comprehensive analysis the suitable annealing temperature for stainless steel 06Cr13 cold-rolled sheet is (850土10)℃.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Influence of Cold Rolling Reduction and Annealing Temperature on Texture and Formability of Ti-IF Steel

Effect of Annealing Process and Cold Rolling Reduction on Texture of CSP Thin Sheet of Ultra-low Carbon Steel

Effect of Austempering on Mechanical Properties of 700 MPa Cold Rolled TRIP Steel 0.15C-1.5Mn-l. 4Si-0. 03Nb-0.03Ti-0.005N

Effect of Primary Recrystallization Annealing Process on Structure and Texture of 3%Si Oriented Silicon Steel

Effect of Continuous Annealing Temperature on Structure Texture and Mechanical Properties 390 MPa IF Steel

Related Author

罗海燕

肖欢

赵刚

余冲

孙宏云

魏俊杰

樊雷

刘海霞

Related Institution

广西冶金研究院

武汉科技大学材料加工工程系

广西柳州钢铁(集团)公司

内蒙古科技大学材料与冶金学院

钢铁研究总院

⁰