Commercial Pilot Production of Threading Steel HRB400E 100t LF Refining by Using Low Titanium Blast Furnace Slag

王宝华; 宫永煜; 张明博; 黄世平; 宁树博

您当前的位置：

首页 >

文章列表页 >

Commercial Pilot Production of Threading Steel HRB400E 100t LF Refining by Using Low Titanium Blast Furnace Slag

更新时间：2026-01-21

- Commercial Pilot Production of Threading Steel HRB400E 100t LF Refining by Using Low Titanium Blast Furnace Slag
- Special Steel Vol. 39, Issue 1, Pages: 28-33(2018)
- 作者机构：
  
  1. 北京科技大学冶金与生态工程学院,北京,100083
  2. 河钢股份有限公司承德分公司,承德,067102
  3. 河钢集团钢研总院,石家庄,050023
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：17 August 2017，
  
  Online First：30 June 2022，
  
  Published：30 June 2018
- 稿件说明：
移动端阅览
王宝华, 宫永煜, 张明博, et al. Commercial Pilot Production of Threading Steel HRB400E 100t LF Refining by Using Low Titanium Blast Furnace Slag[J]. Special Steel, 2018, 39(1): 28-33.
DOI：

王宝华, 宫永煜, 张明博, et al. Commercial Pilot Production of Threading Steel HRB400E 100t LF Refining by Using Low Titanium Blast Furnace Slag[J]. Special Steel, 2018, 39(1): 28-33. DOI：

摘要

采用喷吹CO

法对低钛高炉渣进行脱硫处理，低钛高炉渣中硫的脱除率为66.59%~78.01%，渣中残硫含量为0.137%~0.283%，所制备的低硫低钛高炉渣中硫含量基本满足HRB400E钢LF精炼渣要求。低硫低钛高炉渣LF精炼终渣成分为/%:37.40~46.50CaO，12.30~15.10MgO，21.70~26.70SiO

2，

5.74~17.00Al

3，

2.44~3.39TiO

2，

0.36~1.42MnO，0.75~1.62Fe

3，

0.200~0.597S，钢水脱硫率为10.0%~41.5%，HRB400E钢终点[S

]

为0.008%~0.029%，与现工艺精炼渣（折渣和钢包渣终渣成分/%:34.30~42.90CaO，13.60~18.10MgO，24.00~26.50SiO

2，

4.88~11.00Al

3，

0.71~1.12TiO

2，

0.47~1.47MnO，0.81~1.72Fe

3，

0.245~1.132S）的脱硫效果相当（HRB400E钢终点[S

]

0.027%~0.032%）。

Abstract

With desulphurizing treatment on low titanium blast furnace slag by blowing CO

method

the rate of removing sulfur from low titanium blast furnace slag is 66.59% ~78.01 % and the residual sulfur content in blast furnace slag is 0.137% ~0.283%

therefore the sulfur content in prepared low sulfur and low titanium blast furnace basically meets the requirements of LF refining slag for steel HRB400E. By using low sulfur and low titanium blast furnace slag the ingredient of end slag of LF refining is /% : 37.40 ~46.50 CaO

12.30 ~15.10

MgO

21.70〜26.70 SiO

5.74~17.00 Ag

2.44~3.39 TiO

0.36~1.42 MnO

0.75~1.62 Fe

and 0.200〜0.597 S

the desulphurized rate of liquid is 10.0% ~41.5%

and the end [S

]

of steel HRB400E is 0.008% ~0.029%

it is about equal to the effect of desulphurization by using present process refining slag-ladle slag and drained hot slag ( LF refining end slag ingredient /% : 34.30 〜42.90 CaO

13.60 〜18.10 MgO

24.00 〜26.50 SiO

2，

4.88 -11.00 A1

0.71 ~1.12 TiO

0.47~1.47 MnO

0.81~1.72 Fe

0.245〜1.132 S； end [S

]

of steel HRB400E 0.027% ~0.032% ).

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Prediction of Molten Steel End Point Temperature in LF Based on Modified Artificial Neural Network

A Study on Thermodynamics of Dephosphorization and Rephosphorization of Ultra-Low Oxygen Spring Steel

Control of T[O] and Inclusion in Casing Pipe Steel for Petroleum during LF Refining

Effect of Converter-LF Refining and Hot Metal Pretreatment Converter-Ladle Argon Stirring Process on Metallurgical Quality of Weathering- Resisting Steel

Process Practice on Control of Nitrogen Pick-up in Molten Steel during 150 t Ladle Furnace (LF) Refining Process

Related Author

姜茂发

刘承军

陶子玉

王郢

李海波

于会香

周红霞

郭佳

Related Institution

东北大学材料与冶金学院

北京科技大学材料科学与工程学院

钢铁研究总院冶金工艺研究所

唐山建龙钢铁有限公司

钢铁研究总院

⁰