Effect of Boron on Structure and Mechanical Properties of 780 MPa Low Carbon Bainite Steel

赵燕青; 孙力; 刘宏强; 王九清; 安会龙; 罗应明; 车金锋

您当前的位置：

首页 >

文章列表页 >

Effect of Boron on Structure and Mechanical Properties of 780 MPa Low Carbon Bainite Steel

更新时间：2026-01-21

- Effect of Boron on Structure and Mechanical Properties of 780 MPa Low Carbon Bainite Steel
- Special Steel Vol. 39, Issue 2, Pages: 65-67(2018)
- 作者机构：
  
  1. 河钢集团钢研总院,石家庄,050023
  2. 河钢集团舞钢公司,平顶山,462500
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：30 October 2017，
  
  Online First：04 July 2022，
  
  Published：04 July 2018
- 稿件说明：
移动端阅览
赵燕青, 孙力, 刘宏强, et al. Effect of Boron on Structure and Mechanical Properties of 780 MPa Low Carbon Bainite Steel[J]. Special Steel, 2018, 39(2): 65-67.
DOI：

赵燕青, 孙力, 刘宏强, et al. Effect of Boron on Structure and Mechanical Properties of 780 MPa Low Carbon Bainite Steel[J]. Special Steel, 2018, 39(2): 65-67. DOI：

摘要

试验低碳贝氏体钢（/%:0.08C

0.11~0.13Si

1.10~1.20Mn

0.008~0.009P

0.002S

0.21~0.23Ni

0.020~0.021Ti

0.003~0.004Nb

0~0.0010B

0.000 7~0.0008O

0.0031~0.0033N）由50kg真空感应炉熔炼

轧成45mm钢板

并经930℃淬火

610℃回火。研究了0.0010%硼对780 MPa低碳贝氏体钢45mm板组织和力学性能的影响。结果表明

硼可显著提高试验钢的淬透性

不含硼试验钢淬火后得到粒状贝氏体

0.0010%硼试验钢淬火后得到板条贝氏体。硼明显改善试验低碳贝氏体钢的力学性能

含0.0010%硼试验钢淬、回火后的抗拉强度834MPa和屈服强度771MPa远高于不含硼试验钢的抗拉强度702MPa和屈服强度591MPa

实际生产中应加入适量硼可使低碳贝氏体钢得到板条贝氏体。

Abstract

The tested low carbon bainite steel (/%: 0.08C

0.11~0.13Si

1.10~1.12Mn

0.008〜0.009P

0.002S

0.21~0.23Ni

0.020~0.021Ti

0.003〜0.004Nb

0~0.0010B

0.0007~0.0008O

0.0031~0.0033N) is melted by a 50kg vacuum induction furnace

rolled to 45mm plate

quenched at 930℃ and tempered at 610°C. The effect of 0.0010% boron on structure and mechanical properties of 45mm plate of 780MPa low carbon bainite steel has been studied. Results show that boron can remarkably improve the hardenability of tested steel

the structure of quenched tested steel without bearing boron is granular bainite

and the structure of quenched 0.0010% boron tested steel is lath bainite. The boron can obviously improve the mechanical properties of tested low carbon bainite steel

the tensile strength 834MPa and yield strength 771MPa of quenched-tempered bearing 0.0010% boron tested steel is higher than the tensile strength 702MPa and yield strength 591MPa of quenched-tempered without bearing boron tested steel. Adding suitable boron in steel in practical production the low carbon bainite steel can get lath bainite structure.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Effect of Quenching and Partitioning(Q & P)Process on Structure and Mechanical Properties of Steel 25Si2Ni3

Influence of Niobium Content on Structure and Mechanical Properties of Steel Cr8WMo2V2SiNb

Effect of Si Content on Structure and Mechanical Properties of Ultra Supercritical Steam Turbine Rotor Steel 30Cr2Ni4MoV

Effect of Solution Treatment on Structure and Mechanical Properties of Nickel Base Alloy 690

Effect of Quenching Cooling Rate on Structure and Mechanical Properties of Heat-Resistant Steel lCrl2Ni3Mo2VN

Related Author

解西强

高文涛

时捷

王存宇

张方

刘建华

马党参

张占普

Related Institution

昆明理工大学机电学院

钢铁研究总院结构材料研究所.

鞍山钢铁集团公司

钢铁研究总院

河冶科技股份有限公司

⁰