Process Practice of Deep Dephosphorization Technology of 200t Top and Bottom Combined Blowing Converter with Semi-Steel

陈均; 江南红; 龚洪君; 张彦恒; 曾建华

您当前的位置：

首页 >

文章列表页 >

Process Practice of Deep Dephosphorization Technology of 200t Top and Bottom Combined Blowing Converter with Semi-Steel

更新时间：2026-01-21

- Process Practice of Deep Dephosphorization Technology of 200t Top and Bottom Combined Blowing Converter with Semi-Steel
- Special Steel Vol. 38, Issue 6, Pages: 40-44(2017)
- 作者机构：
  
  1. 攀钢集团研究院有限公司，钒钛资源综合利用国家重点实验室,攀枝花,617000
  2. 攀钢集团西昌钢钒有限公司，西昌,615000
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：05 June 2017，
  
  Online First：12 July 2022，
  
  Published：12 July 2017
- 稿件说明：
移动端阅览
陈均, 江南红, 龚洪君, et al. Process Practice of Deep Dephosphorization Technology of 200t Top and Bottom Combined Blowing Converter with Semi-Steel[J]. Special Steel, 2017, 38(6): 40-44.
DOI：

陈均, 江南红, 龚洪君, et al. Process Practice of Deep Dephosphorization Technology of 200t Top and Bottom Combined Blowing Converter with Semi-Steel[J]. Special Steel, 2017, 38(6): 40-44. DOI：

摘要

针对转炉终点钢水磷含量高且波动大的问题

对钢水深脱磷控制难点及影响脱磷的因素进行了分析

提出了采用"双渣高拉碳放渣"的深脱磷工艺路线;通过优化造渣制度、供氧和底吹气制度、枪位控制和终点控制等脱磷工艺

9炉34CrMo4钢的冶炼结果表明

钢水脱磷率达84.6%

终点渣-钢磷分配比Lp达到90.1

实现了转炉终点钢水[P]≤0.006%的稳定控制

并通过采用滑板挡渣及顶渣改制等减少回磷的技术措施

具备了批量生产磷含量小于0.010%的低磷钢种的能力。

Abstract

According to the issue of high phosphorus content in liquid with great fluctuation at end-point of converter

the difficult points for control of deep dephosphorization of liquid and the influence factors on dephosphorization are analyzed

and to use the deep dephosphorization process scheme of “double slagging catch carbon method” is proposed. With the dephosphorization measures including optimizing slagging

oxygen supplying

bottom gas blowing and lance level and end point control

the results of 9 heats of steel 34CrMo4 steelmaking shows that the dephosphorization rate of liquid is up to 84.6%

the end slag-steel phosphor partition ratio Lp is up to 90.1 to realize the stable control on converter liquid end [P]≤0.006%

and with using the technology measures of skateboard and reformed top slag to reduce rephosphorization

the ability of batch steelmaking low phosphorus steel with phosphorus content less than 0. 010% is qualified.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Process Practice for Production of Caterpillar Track Steel 35MnBM by 90 t EAF-LF(VD)-CC-CR Flow Sheet

Operation Practice of High Carbon Chromium Bearing Steel Produced by LD-LF+VD Process

Practice of Process for Steel 38CrMoAl Produced by 100 t EBT Arc Furnace-LF-CC Flow Sheet

Process Practice of Non-Aluminum Deoxidation for Spring Steel Steelmaking Production by 100 t DC EAF-LF -VD Flow Sheet

Development of Tire Cord Steel XLX72A by 80 t Top and Bottom Combined Blown Converter-LF Nol-LF No2-VD-CC Flow Sheet

Related Author

朱志欣李艾王秀兰

林纲

李士琦

郁健

曹立国

余国松

杜建新

Related Institution

东北特钢集团北满特殊钢有限责任公司

北京科技大学冶金与生态工程学院

石家庄钢铁有限贲任公司炼钢厂

中咨工程建设监理公司总工办

杭州钢铁集团公司技术中心

⁰