Mechanical Properties of Casting Slab of High Strength Cold-Rolled Steel 1500MS for Auto at High Temperature

更新时间：2026-01-21

- Mechanical Properties of Casting Slab of High Strength Cold-Rolled Steel 1500MS for Auto at High Temperature
- Special Steel Vol. 39, Issue 1, Pages: 54-56(2018)
- 作者机构：
  
  1. 中国钢研集团,北京,100081
  2. 邯钢集团公司,邯郸,056000
  3. 北京科技大学钢铁冶金新技术国家重点实验室,北京,100083
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：01 August 2017，
  
  Online First：01 July 2022，
  
  Published：01 July 2018
- 稿件说明：
移动端阅览
邓建军, 王睿. Mechanical Properties of Casting Slab of High Strength Cold-Rolled Steel 1500MS for Auto at High Temperature[J]. Special Steel, 2018, 39(1): 54-56.
DOI：

邓建军, 王睿. Mechanical Properties of Casting Slab of High Strength Cold-Rolled Steel 1500MS for Auto at High Temperature[J]. Special Steel, 2018, 39(1): 54-56. DOI：

摘要

试验用1500MS钢（/%:0.20C

0.31Si

1.39Mn

0.011P

0.001S

0.028Als

0.26Cr

0.028Ti

0.0018B

0.0048N）240mm板坯的生产流程为250t BOF-LF-RH-板坯连铸。通过Gleeble-1500热模拟试验机

测试了试验钢1350~600℃的力学性能

得出该钢第Ⅰ脆性区为1350~1250℃

第Ⅲ脆性区为650~750℃在800~1200℃铸坯具有良好的热塑性;建立了板坯凝固传热数学模型和计算了铸坯凝固过程的表面温度。1500MS钢铸坯矫直区域的温度应控制在800~1150℃。

Abstract

The production flowsheet of 240 mm slab of tested steel 1500MS (/% : 0.20C

0.31Si

1.39Mn

0.011P

0.001S

0.028Als

0.26Cr

0.028Ti

0.0018B

0.0048N) is 250t BOF-LF-RH-slab CC process. The mechanical properties of tested steel at 1350 ~600°C have been measured by using Gleeble-1500 thermal simulation machine to get I-bnttle zone at 1350 ~ 1250°C

and Ⅲ-brittle zone at 650〜750°C，and at 800〜1200 °C the tested steel has better hot plasticity ； and the mathematical model of slab solidification heat transfer is established and the surface temperature of casting slab in solidification process is calculated. The temperature of tested steel of steel 1500MS at straightening zone should be controlled at 800〜1150°C.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

A Study on High Temperature Mechanical Properties of GCr15 Bearing Steel

Effect of Nickel on Mechanical Properties of Weathering Steel 09CuPCrNi at High Temperature

Study and Application of a Casting Bloom Micro Segregation Model during Solidification Process of Bearing Steel GCrl5

Elevated Temperature Mechanical Properties of High Strength Weathering Steel Q450NQR1 in Thermal Cycle Process

Effect of Carbon and Boron Content on Mechanical Properties of Casting Bloom of Low Carbon Cold Heading Steel at Elevated Temperature

Related Author

路文刚

朱立光

吴浩方

万兰凤

黄绪传

张晖

张龙

武佳毅

Related Institution

河北理工大学冶金与能源学院

上海梅山钢铁股份有限公司技术中心

安徽工业大学

重庆大学材料科学与工程学院

邢台钢铁有限责任公司，河北省线材工程技术研究中心

⁰