Influence of 120 t LF Stirring Intensity on Amount of Large Size Inclusions in Low Carbon Q195 Steel during Refining

蒋鲤平; 徐建飞; 于飞

您当前的位置：

首页 >

文章列表页 >

Influence of 120 t LF Stirring Intensity on Amount of Large Size Inclusions in Low Carbon Q195 Steel during Refining

更新时间：2026-01-21

- Influence of 120 t LF Stirring Intensity on Amount of Large Size Inclusions in Low Carbon Q195 Steel during Refining
- Special Steel Vol. 42, Issue 4, Pages: 47-50(2021)
- 作者机构：
  
  中天钢铁集团有限公司第三炼钢厂,常州,213011
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：19 January 2021，
  
  Online First：09 March 2022，
  
  Published：09 March 2021
- 稿件说明：
移动端阅览
蒋鲤平, 徐建飞, 于飞. Influence of 120 t LF Stirring Intensity on Amount of Large Size Inclusions in Low Carbon Q195 Steel during Refining[J]. Special Steel, 2021, 42(4): 47-50.
DOI：

蒋鲤平, 徐建飞, 于飞. Influence of 120 t LF Stirring Intensity on Amount of Large Size Inclusions in Low Carbon Q195 Steel during Refining[J]. Special Steel, 2021, 42(4): 47-50. DOI：

摘要

采用"120 t BOF→LF→Ca处理→160 mm × 160 mm CC"工艺生产的Q195钢。示踪检验得出

当LF精炼过程氩气流量在300～600 L/min时

50 × 400 mm

检验面积中

铸坯中≥27 μm大尺寸夹杂物31个

主要来源于LF精炼渣卷渣、钙处理生成的CaS、水口内壁材质剥落和钢中内生大尺寸钙铝酸盐夹杂物

其中由LF精炼渣卷渣形成的大尺寸夹杂物所占比例为29.1%。通过精炼全程将氩气流量由300～600 L/min降低至100 L/min

发现可以显著降低精炼渣卷渣形成的大尺寸夹杂物数量

同样的检测面积≥27 μm夹杂物降至19个。

Abstract

The Q195 steel is produced by M120 t BOF→LF→Ca addition→160 mm x 160 mm CC” process. It was found by tracing test that the number of ≥27μm large size inclusions at test area 50 x 400 mm

in the billet is 31 and generated by LF top slag entrapped during gas stirring

calcium treatment formed CaS

submerged entry nozzle material stripped and formed endogenous large size calcium-aluminate inclusion in steel as the flow rate of argon is in the range of 300～600 L/min. The proportion of LF top slag entrapped is about 29. 1% in all the large size inclusions. As the flow rate of argon decreases from 300～600 L/min to 100 L/min

it is found that the LF top slag entrapped could be significantly decreased

at some test area the ≥27μm inclusions number decreases to 19.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

No data

Related Author

No data

Related Institution

No data

⁰