A Study on Austenite Grain Growth Behaviour of High Strength 23MnNiMoCr54 Link-Chain Steel for Mining

赵海东; 刘佳兴; 张朝磊; 苗红生; 刘雅政

您当前的位置：

首页 >

文章列表页 >

A Study on Austenite Grain Growth Behaviour of High Strength 23MnNiMoCr54 Link-Chain Steel for Mining

更新时间：2026-01-21

- A Study on Austenite Grain Growth Behaviour of High Strength 23MnNiMoCr54 Link-Chain Steel for Mining
- Special Steel Vol. 42, Issue 2, Pages: 10-13(2021)
- 作者机构：
  
  1. 西宁特殊钢股份有限公司,西宁,810005
  2. 2北京科技大学材料科学与工程学院,北京,100083
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：30 August 2020，
  
  Online First：13 April 2022，
  
  Published：13 April 2021
- 稿件说明：
移动端阅览
赵海东, 刘佳兴, 张朝磊, et al. A Study on Austenite Grain Growth Behaviour of High Strength 23MnNiMoCr54 Link-Chain Steel for Mining[J]. Special Steel, 2021, 42(2): 10-13.
DOI：

赵海东, 刘佳兴, 张朝磊, et al. A Study on Austenite Grain Growth Behaviour of High Strength 23MnNiMoCr54 Link-Chain Steel for Mining[J]. Special Steel, 2021, 42(2): 10-13. DOI：

摘要

研究结果表明:链环钢23MnNiMoCr54奥氏体晶粒的粗化温度为900

℃

为避免“混晶现象”的发生，最佳奥氏体化工艺在850℃下保温30 min。在相同保温时间下

奥氏体晶粒随着加热温度在850-1100℃内升高呈指数关系长大。在相同加热温度下，平均奥氏体晶粒尺寸与保温时间的关系符合Beck模型

晶粒长大指数n随着加热温度的升高先降低后升高。依据Arrhenius公式拟合得到了链环钢23MnNiMoCr54在950 - 1250℃内的奥氏体晶粒长大模型 D=2. 105 xl0

0.138

exp( -5.18 x 10

/RT)。

Abstract

The research results show that the coarsening temperature of austenite grains of 23MnNiMoCr54 link-chain steel is 900℃

in order to avoid “mix grain phenomena" occured

the opitmum austenitizing temperature of steel is 850 ℃ for 30 min. Austenite grains grow exponentially with the increase of heating temperature from 850

℃

to 1100℃ for same holding time. The relationship between the average austenite grain size and holding time conforms to Beck model at the same heating temperature

the grain growth index (n) first decreases and then increases with increase of temperature. The austenitic grain growth model D=2.105 xl0

0.138

exp( -5.18 x 10

/RT)。 for 23MnNiMoCr54 link-chain steel at 950 ~ 1250 °C is obtained by fitting in Arrhenius formula.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

No data

Related Author

No data

Related Institution

No data

⁰