Application of DOE (Design of Experiment) in Enhancing Impact Energy of 30CrNiMo Steel Quenched and Tempered Bar

更新时间：2026-01-21

- Application of DOE (Design of Experiment) in Enhancing Impact Energy of 30CrNiMo Steel Quenched and Tempered Bar
- Special Steel Vol. 43, Issue 5, Pages: 82-85(2022)
- 作者机构：
  
  1. 大冶特殊钢有限公司,黄石,435001
  2. 大冶特殊钢有限公司技术中心,黄石,435001
  3. 高品质特殊钢湖北省重点实验室,黄石,435001
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Received：10 February 2022，
  
  Online First：29 September 2022，
  
  Published：29 September 2022
- 稿件说明：
移动端阅览
蒋乔, 曾云, 胡瑞海, et al. Application of DOE (Design of Experiment) in Enhancing Impact Energy of 30CrNiMo Steel Quenched and Tempered Bar[J]. Special Steel, 2022, 43(5): 82-85.
DOI：

蒋乔, 曾云, 胡瑞海, et al. Application of DOE (Design of Experiment) in Enhancing Impact Energy of 30CrNiMo Steel Quenched and Tempered Bar[J]. Special Steel, 2022, 43(5): 82-85. DOI：

摘要

针对30CrNiMo(/%:0.30C

0.85Mn

0.25Si

0.015P

0.008S

0.96Cr

0.43Mo

0.78Ni

0.025Al)高强度钢调质棒材冲击功不稳定的问题，根据DOE试验设计方法，对运用该钢正火温度(870～910℃)、奥氏体化温度(830～870℃)两项因子、三水平的试验方案快速寻找到提升冲击功的最佳工艺组合。对比检测结果发现30CrNiMo钢正火温度越高，淬火后组织晶粒度级别越小，对应冲击功越小。运用Minitab工具制作出冲击功响应晶粒度的拟合公式即：21℃纵向冲击功(J)=27.11+7.751×晶粒度(级)。30CrNiMo钢最佳工艺组合为870℃正火+850℃奥氏体化，其冲击功为106 J.

Abstract

In view of the unstable impact energy of 30CrNiMo (/% ：0.30C

0.85Mn

0.25Si

0.015P

0.008S

0.96Cr

0.43Mo

0.78Ni

0.025Al) high strength quenched and tempered steel bar

normalizing (870-910 ℃)and austenitizing ( 830-870 °C ) temperature two-factor and three-level DOE test design scheme are used to quickly find die best process combination for improving impact energy. The results show that the higher the normalizing temperature

the bigger the grain size after being normalized and quenched

and the smaller the impact energy in steel 30CrNiMo. The Minitab tool is used to make the fitting formula of impact energy response to grain size： 21 °C longitudinal impact energy (J) = 27.11 +7.751 x grain size (grade). The optimum process combination for 30CrNiMo steel is normalizing at 870 °C + austenitizing at 850 °C. Its impact energy is 106 J.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Process Practice for Microstructure Optimization of UNS N09925 Alloy Forgings in Oilfield Service Industry

The Effect of Nb on Microstructure and Properties of GH4169 Alloy Pipe

Microstructure and High-temperature Mechanical Properties of Different Positions of Turbine Disc Forgings in GH4706 Superalloy

Research on Ultra-high Rotary Bending Fatigue Strength of Flexible Bearing Steels for Robot Harmonic Speed Reducer

Effect of AlN and Zr Microalloying on Thermoplasticity and Grain Size of Carburized Gear Steel

Related Author

Wu Yinhu

Zhang Jiawei

Yang Liang

Yu Jie

Zhu Yuliang

Wang Shucai

Liu Zhengdong

Wang Shaobing

Related Institution

Fushun Special Steel Co.，Ltd.

Central Iron & Steel Research Institute Co.，Ltd.

China Iron & Steel Research Institute Group

Zhejiang Jiuli Metal Materials Research Institute Co.， Ltd.

Zhejiang Jiuli Hi-Tech Metals Co.， Ltd.

⁰