Effect of Inclusion Characteristics on Impact Toughness of 10CrNi3Mo Steel

更新时间：2026-01-21

- Effect of Inclusion Characteristics on Impact Toughness of 10CrNi3Mo Steel
- Special Steel Vol. 43, Issue 5, Pages: 33-38(2022)
- 作者机构：
  
  宝武集团中央研究院,武汉,430080
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Online First：28 September 2022，
  
  Published：28 September 2022
- 稿件说明：
移动端阅览
杨治争, 严翔, 熊玉影, et al. Effect of Inclusion Characteristics on Impact Toughness of 10CrNi3Mo Steel[J]. Special Steel, 2022, 43(5): 33-38.
DOI：

杨治争, 严翔, 熊玉影, et al. Effect of Inclusion Characteristics on Impact Toughness of 10CrNi3Mo Steel[J]. Special Steel, 2022, 43(5): 33-38. DOI：

摘要

基于200 t BOF-LF-RH-板坯连铸的10CrNi3Mo钢冶金生产流程，分别通过向钢液喂入硅钙包芯线和钙镁复合包芯线，对夹杂物进行变性处理，之后通过4300厚板轧机轧制35 mm板并进行热处理。利用等电位溶液电解、扫描电镜与能谱、夹杂物分析仪等设备和方法对试验钢的夹杂物进行定量、定性分析，获得夹杂物的特性参数，主要表现为变性后夹杂物单位面积数量减少约40%

平均间距增加近1倍。结合夏比冲击试验结果，得出夹杂物变形处理对冲击韧性特别是低温冲击韧性有明显改善的结论。

Abstract

Based on 200 t BOF-LF-RH-CC slab metallurgical process to produce 10CrNi3Mo steel

silicon-calcium cored wire and calcium-magnesium composite cored wire are injected respectively into liquid steel to modify inclusions

and the slabs are rolled to 35 mm plates with 4 300 mm heavy plate rolling mill then to carried out heat treatment. The inclusions of test steel are analyzed quantitatively and qualitatively by means of SPEED

SEM & EDS and INCA etc. The obtained main performance is that the number of inclusions per unit area is reduced by about 40% and the average distance is nearly doubled after modification. Combined with the Charpy impact test results

it is concluded that the inclusion deformation treatment is obviously improve to the impact toughness

especially the low-temperature impact toughness.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Effect of Nioblum on Microstructure and Properties of 65Mn High Carbon Cutting Tool Steel

Effect on Fatigue Failure Behavior Induced by Inclusions in GCr15 Bearing Steel Under Different Metallurgical Processes

Effects of Ti Microalloying on the Microstructure and Mechanical Properties of a Novel GH1059 Alloy for Nuclear Applications

High Temperature Mechanical Properties and Fracture Mechanism of 9Cr-2W-3Co Martensitic Heat-resistant Steel

Effect Mechanism of Curling Temperature on the Toughness of Titanium Microalloyed High-strength Steel GCL700

Related Author

Yang Yu

Wang Tianxiao

Song Xiaoming

Xu Cheng

Wang Runqi

Wang Zheng

Chen feng

Shi Tao

Related Institution

State Key Laboratory of Metallic Materials for Marine Equipment and Applications

Angang Steel Co.， Ltd.

School of Materials Science and Engineering， Dalian University of Technology Liaoning

Jiangying Xingcheng Special Steel Works Co.， Ltd.， Jiangying

Daye Special Steel Co.， Ltd.

⁰