Optimizing Continuous Casting Process to Improve SWRH82A Steel 150 mm x 150 nun Billet Center Carbon Segregation

毕胜; 宫哲; 王鑫; 何金泽; 陈修君

您当前的位置：

首页 >

文章列表页 >

Optimizing Continuous Casting Process to Improve SWRH82A Steel 150 mm x 150 nun Billet Center Carbon Segregation

更新时间：2026-01-21

- Optimizing Continuous Casting Process to Improve SWRH82A Steel 150 mm x 150 nun Billet Center Carbon Segregation
- Special Steel Vol. 43, Issue 4, Pages: 24-27(2022)
- 作者机构：
  
  1. 东北特殊钢集团股份有限公司1总工办
  2. 技术中心,大连,116000
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Online First：12 August 2022，
  
  Published：12 August 2022
- 稿件说明：
移动端阅览
毕胜, 宫哲, 王鑫, et al. Optimizing Continuous Casting Process to Improve SWRH82A Steel 150 mm x 150 nun Billet Center Carbon Segregation[J]. Special Steel, 2022, 43(4): 24-27.
DOI：

毕胜, 宫哲, 王鑫, et al. Optimizing Continuous Casting Process to Improve SWRH82A Steel 150 mm x 150 nun Billet Center Carbon Segregation[J]. Special Steel, 2022, 43(4): 24-27. DOI：

摘要

为了减轻SWRH82A钢150 mm x 150 mm铸坯中心碳偏析，进行了拉速(1. 9 ~2. 3 m/min)、二冷比水量(0. 75 ~ 1.24 L/kg)、过热度(25 ~38 °C )、结晶器电磁搅拌强度(300 - 350 A)和末端电磁搅拌强度(300 - 470 A) 连铸工艺参数试验。结果证明

合理控制拉速1.9-2.0 m/min

钢水过热度25°C 左右、比水量为1. 01 I7kg、结晶器电磁搅拌强度为350 A/3 Hz、末端电磁搅拌强度为400 A/7 Hz时，铸坯中心碳偏析指数可以得到大幅改善，由原来的1.21降为1.05。

Abstract

In order to reduce the center carbon segregation of SWRH82A steel 150mm x 150 mm cast billet

the experiments with different continuous casting processes including casting speed (1. 9 ~ 2. 3 m/min)

water ratio in secondary cooling zone (0. 75 ~ 1.24 L/kg)

degree of liquid superheat (25 - 28 °C )

mold electromagnetic stirring intensity (300 ~ 350 A) and end electromagnetic stirring intensity (300 ~ 470 A) have been carried out. The results prove that when the casting speed is 1. 9 ~2. 0 m/min

the liquid superheat is about 25 °C

the water ratio is 1. 01 L/kg

the mold electromagnetic stirring intensity is 350 A/3 Hz

and the end electromagnetic stirring intensity is 400 A/7 Hz

the billet center carbon segregation index can be large improved decreasing from original 1. 21 to 1. 05.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

A Study on Decarburization Trend of New High Strength and Toughness Spring Steels 40T and 44T

Control of Chemical Composition and Quality of LZ50 Steel Billet for Vehicle Axle Produced by 120 t Converter -LF + RH-TB Process

Practice of GCr15 Bearing Steel Production by 50 t EBT EAF-LF(VD)- CC Process

Process Practice of GCr15 Bearing Steel With 60 t Consteel EAF-LF(VD)- CC Flow Sheet at Guiyang Steel

Advance in Research on Evolution of Structure in TRIP Steels during TMP and Heat Treatment

Related Author

尹钟大

徐德祥

刘德富

许家彦

王荣武

李法兴

兰新哲

宋永辉

Related Institution

哈尔滨工业大学

本溪钢铁集团公司

西安建筑科技大学

莱芜钢铁股份有限公司

贵阳特殊钢有限责任公司

⁰