Study on Homogenization Process of Super Austenitic Stainless Steel 254SMo

史咏鑫; 李青; 钟庆元; 田伟; 叶强

doi:10.20057/j.1003-8620.2022-00094

您当前的位置：

首页 >

文章列表页 >

Study on Homogenization Process of Super Austenitic Stainless Steel 254SMo

更新时间：2026-01-21

- Study on Homogenization Process of Super Austenitic Stainless Steel 254SMo
- Special Steel Vol. 44, Issue 2, Pages: 12-16(2023)
- 作者机构：
  
  1. 中航上大高温合金材料股份有限公司,邢台,054800
  2. 河北省特种合金再生工程技术研究中心,邢台,054800
- 作者简介：
- 基金信息：
- DOI：10.20057/j.1003-8620.2022-00094
  CLC：
- Received：19 August 2022，
  
  Online First：23 March 2023，
  
  Published：23 March 2023
- 稿件说明：
移动端阅览
史咏鑫, 李青, 钟庆元, et al. Study on Homogenization Process of Super Austenitic Stainless Steel 254SMo[J]. Special Steel, 2023, 44(2): 12-16.
DOI：

史咏鑫, 李青, 钟庆元, et al. Study on Homogenization Process of Super Austenitic Stainless Steel 254SMo[J]. Special Steel, 2023, 44(2): 12-16. DOI： 10.20057/j.1003-8620.2022-00094.

摘要

试验用超级奥氏体不锈钢254SMo(/%:0.011C

0.30Si

0.46Mn

20.25Cr

17.75Ni

6. 13Mo

0.64Cu

0.212N)采用20 t电弧炉+AOD+LF 精炼的工艺冶炼，研究了254SMo钢的铸态组织，发现枝晶间存在大量的析出相，其临近冒口钢锭头部中心的析出相尺寸最大，且呈网状分布。钢锭经1240℃ 8～40 h均质化处理后，锻造成 φ204 mm棒材，检验其析出相数量和点腐蚀速率。试验结果表明：随着均质化时间的延长，其析出相尺寸减小，数量减少，钢的点腐蚀性能提高；均质化12h+镦粗拔长+均质化12 h为最优均质化工艺。

Abstract

The tested super austenitic stainless steel 254SMo(/%:0.011C

0.30Si

0.46Mn

20.25Cr

17.75Ni

6.13Mo

0.64Cu

0.212N) is melted by 20 t electric arc furnace + AOD +LF refining

the as-cast microstructure of 254SMo steel has been studied. It is found that there are a large number of precipitates between dendrites

and the precipitates in the center of ingot head near hot top are the largest and distributed in a network. After homogenization treatment at 1240℃ for 8-40 h

the ingots are forged to φ204 mm bar

the quantity of precipitated phase and pitting corrosion rate are inspected. The experimental results show that with the prolongation of homogenization time

the size and quantity of precipitates decrease

and the pitting corrosion performanceof steel improves; Homogenization for 12 h + Upsetting and Stretching + homogenization for 12 h is the optimal homogenization process.

关键词

Keywords

references

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Effect of SiO₂ on Precipitation Phases and High-temperature Structures of Slags for Drawing-ingot-type Electroslag Remelting

The Effect of Rare Earth on the Precipitated Phases During Aging Process of T91 Heat-resistant Steel

High Temperature Mechanical Properties and Fracture Mechanism of 9Cr-2W-3Co Martensitic Heat-resistant Steel

The Effect of Nb on Microstructure and Properties of GH4169 Alloy Pipe

Thermodynamic Simulation of Equilibrium Solidification and Precipitation of CW12MW and CW6MC Cast Nickel-based Alloys

Related Author

Jiang Zhouhua

Dong Yanwu

Yao Yudong

Zhou Weiji

Cao Junze

Wang Xinwei

Sun Xin

Li Gen

Related Institution

School of Metallurgy， Northeastern University

Dongbei Special Steel Group Co.， Ltd.

State Key Laboratory of Advanced Metallurgy， University of Science and Technology Beijing

Research Institute of Special Steel， Central Iron and Steel Research Institute Co. Ltd.

Daye Special Steel Co.， Ltd.

⁰