Control Technology of Aluminum Content and Inclusion Composition in High-silicon and Aluminum-controlled Steel

Zhai Wanli; Zhang Hongcai; Xiao Mengxuan; Xu Zhengzhou

doi:10.20057/j.1003-8620.2024-00208

您当前的位置：

首页 >

文章列表页 >

Control Technology of Aluminum Content and Inclusion Composition in High-silicon and Aluminum-controlled Steel

Smelting and Solidification | 更新时间：2025-05-09

- Control Technology of Aluminum Content and Inclusion Composition in High-silicon and Aluminum-controlled Steel
- Special Steel Vol. 46, Issue 2, Pages: 67-71(2025)
- 作者机构：
  
  江苏沙钢集团淮钢特钢股份有限公司，淮安 223002
- 作者简介：
- 基金信息：
- DOI：10.20057/j.1003-8620.2024-00208
  CLC： TF769.2
- Received：19 August 2024，
  
  Published：30 March 2025
- 稿件说明：
移动端阅览
翟万里,张洪才,肖梦旋等.高硅控铝钢中铝含量与夹杂物成分控制[J].特殊钢,2025,46(02):67-71.

Zhai Wanli,Zhang Hongcai,Xiao Mengxuan,et al.Control Technology of Aluminum Content and Inclusion Composition in High-silicon and Aluminum-controlled Steel[J].Special Steel,2025,46(02):67-71.
翟万里,张洪才,肖梦旋等.高硅控铝钢中铝含量与夹杂物成分控制[J].特殊钢,2025,46(02):67-71. DOI： 10.20057/j.1003-8620.2024-00208.

Zhai Wanli,Zhang Hongcai,Xiao Mengxuan,et al.Control Technology of Aluminum Content and Inclusion Composition in High-silicon and Aluminum-controlled Steel[J].Special Steel,2025,46(02):67-71. DOI： 10.20057/j.1003-8620.2024-00208.

摘要

通过工业试验研究了高硅控铝钢中Al含量、非金属夹杂物化学成分控制工艺，结果表明，采用碱度在1.5以下的低碱度渣系可将钢中

［Al］控制在0.004%以内，采用碱度2.5～3.5的高碱度渣系钢液

［Al］＞0.006%。渣中Al

含量降低有利于抑制冶炼过程钢液增Al量。低碱度渣系钢中氧化物夹杂物成分为SiO

-MnO-Al

-MgO-CaO系，达到夹杂物塑性化的控制目的。高碱度渣系钢中氧化物夹杂成分为Al

含量较高的Al

-SiO

-MgO-CaO系，夹杂物塑性变形能力不足。虽然低碱度渣系在LF精炼过程脱氧能力不足，但经过RH真空处理后，仍然能得到

［O］＜0.001 2%、夹杂物尺寸细小的高洁净度钢。

Abstract

In present paper，the control technology of aluminum content and inclusion composition was analyzed for high-silicon and aluminum-controlled steel by technological test. The results showed that content of Al in steel can be controlled within 0.0040% by using low basicity slag with alkalinity below 1.5，while the Al content is higher than 0.006% by using high basicity slag with basicity 2.5 - 3.5. The decrease of Al

content in slag is beneficial to decrease the amount of Al increase in molten steel.The oxide inclusion component in low basicity slag steel is SiO

-MnO-Al

-MgO-CaO series ， which achieves the control of inclusion plasticization. The oxide inclusion component in high basicity slag steel is Al

-SiO

-MgO-CaO series with high Al

content， and the plastic deformation ability of the inclusion material is insufficient. High clean steel with oxygen content less than 0.001 2% and fine inclusions can be obtained after RH control processing， although deoxygenation effect of the steel with low basicity slag is poor in the refining process.

关键词

Keywords

references

Lankford J . Inclusion-matrix debonding and fatigue crack initiation in low alloy steel ［J］. International Journal of Fracture ， 1976 ， 12 （ 1 ）： 155 - 157 .

Lankford J . （E） Effect of oxide inclusions on fatigue failure ［J］. International Metals Reviews ， 1977 ， 22 （ 1 ）： 221 - 228 .

原永良，舒康颖，曹荫之 . 非金属夹杂物对重轨性能的影响［J］. 钢铁， 1989 （ 10 ）： 27 - 32 .

Liu Y B ， Zhang W ， Tong Q ， et al . Effects of temperature and oxygen concentration on the characteristics of decarburization of 55SiCr spring steel ［J］. ISIJ International ， 2014 ， 54 （ 8 ）： 1920 - 1926 .

陈天明，杨素波，王新华，等 . 齿轮钢氧含量及夹杂物控制技术研究［J］. 北京科技大学学报， 2011 （ 33 ）： 165 - 172

刘珍童 . 重轨钢（U71Mn）夹杂物行为研究［D］. 沈阳：东北大学， 2008 .

Bernard G ， Riboud P ， Urbain G . Investigation of the Plasticity of Oxide Inclusions ［J］. Revue de Metallurgie ，Cahiersd Informations Techniques， 1981 ， 78 （ 5 ）： 421 - 433 .

胡　阳，陈伟庆，韩怀宾，等 . 国内外气门簧用弹簧钢线材质量对比［J］. 炼钢， 2015 ， 31 （ 6 ）： 47 - 52 .

周　群，王福明，张　博，等 . 国内外气门弹簧钢54SiCr6中氧化物夹杂控制分析［J］. 炼钢， 2012 ， 28 （ 2 ）： 71 - 74 .

曾溢彬，包燕平，赵家七，等 . 硅锰脱氧55SiCr弹簧钢中镁铝尖晶石的形成及演变［J］. 钢铁， 2022 ， 57 （ 8 ）： 69 - 77 .

黄希祜 . 钢铁冶金原理［M］. 3版 . 北京：冶金工业出版社， 2002 .

唐国章，李俊国，曾亚南，等 . CaO-MgO-Al 2 O 3 -SiO 2 精炼渣组分活度热力学研究［J］. 钢铁钒钛， 2016 ， 37 （ 4 ）： 127 - 132 .

李正邦，薛正良，张家雯，等 . 合成渣处理对弹簧钢脱氧及夹杂物控制的影响［J］. 特殊钢， 2000 ， 21 （ 3 ）： 10 - 13 .

Kawahara J ， Tanabe K ， Banno T ， et al . Advance of Valve Spring Steel ［J］. Wire Journal Intemational（USA）， 1992 ， 25 （ 11 ）： 55 - 61 .

杨俊，王新华 . 超低氧冶炼过程镁铝尖晶石形成的热力学分析与控制［J］. 钢铁， 2018 ， 53 （ 4 ）： 1 - 7

Kiessling R . Non-metallic inclusion in steel ［M］. London ： The Institute of Metals ， 1989 ： 46 - 93 .

Views

下载量

CSCD

CNKI被引量

Alert me when the article has been cited

提交

Tools

Publicity Resources

Practice of 150t BOF Dephosphorizing Slag Control Process

Related Author

宋延成

刘吉刚

Related Institution

江阴兴澄特种钢铁有限公司特板炼钢分厂，江阴

北京科技大学冶金与生态工程学院

⁰