150 t BOF-LF-RH-CC-CR工艺试制石油钻杆连接套用钢SAE4137M

特殊钢 ›› 2012, Vol. 33 ›› Issue (2): 40-42.

150 t BOF-LF-RH-CC-CR工艺试制石油钻杆连接套用钢SAE4137M

卢秉军，董学涛

本钢板材股份有限公司技术中心，本溪 117000

收稿日期:2011-10-31 出版日期:2012-04-01 发布日期:2022-10-14
作者简介:卢秉军(1972-)，男，高级工程师，1993年辽宁工学院毕业，特殊钢产品研究和开发

Pilot Production of Steel SAE4137M for Petroleum Drill Pipe Connecting Sleeve by 150 t BOF-LF-RH-CC-CR Process

Lu Bingjun ， Dong Xuetao

Technology Center, Bengang Steel Plates Co Ltd, Benxi 117000

Received:2011-10-31 Published:2012-04-01 Online:2022-10-14

摘要/Abstract

摘要： 本钢采用铁水预处理-150t复吹转炉-LF-RH-350 mm × 470 mm连铸、M-EMS-连轧工艺生产φ130～170 mm石油钻杆连接套用钢SAE4137M(/%:0.35～0.38C、0.15～0.35Si、0.85～1.00Mn、≤0.015P、≤0.008S、0.90～1.20Cr、0.28～0.33Mo、≤0.005Ca、≤0.0090N)。通过转炉出钢过程加复合脱氧剂,LF扩散脱氧全程吹氩搅拌,RH"软吹氩",严格控制喂钙线量,控制连铸钢水过热度20～30℃,使钢材中氧含量为(13～15)×10^-6,氢含量(0.4～0.5)×10^-6,氮含量为(35～44)×10^-6,残余钙含量(12～18)×10^-6,并保证钢中Al/N≥2,满足石油用钢的要求。

关键词: 150 t BOF-LF-RH-CC流程, 石油钻杆连接套用钢SAE4137M, 试制

Abstract: The Φ130-170 mm bar of steel SAE4137M for petroleum drill pipe connecting sleeve (/% : 0.35-0.38C, 0.15-0.35Si, 0.85-l.00Mn, ≤ 0.015P, ≤ 0.008S, 0.90-1.20Cr, 0.28-0.33Mo，≤ 0.005Ca, ≤ 0.0090N) has been pilot-produced by hot metal pretreatment-150 t top and bottom combined blown converter-LF-RH-350 mm x 470 mm casting with M-EMS-continuous rolling process at Bengang. With adding compound deoxidizer during converter tapping, diffusion deoxidizing with argon stirring in LF refining, soft argon blowing and strict-controlling feeding calcium wire amount in RH refining, and controlling liquid overheating extent within 20-30 ℃ , in steel products the oxygen content is (13-15 ) x 10^-6, hydrogen content (0.4~0.5) x 10^-6 , nitrogen content (35-44) x 10^-6, residual calcium content ( 12-18) x 10^-6 and Al/N is ensured ≥ 2, that all meet the requirement for petroleum steels

Key words: 150 t BOF-LF-RH-CC Flow Sheet, Steel SAE4137M for Petroleum Drill Pipe Connecting Sleeve, Pilot Production

卢秉军, 董学涛. 150 t BOF-LF-RH-CC-CR工艺试制石油钻杆连接套用钢SAE4137M[J]. 特殊钢, 2012, 33(2): 40-42.

Lu Bingjun , Dong Xuetao. Pilot Production of Steel SAE4137M for Petroleum Drill Pipe Connecting Sleeve by 150 t BOF-LF-RH-CC-CR Process[J]. Special Steel, 2012, 33(2): 40-42.

[1]	梁佰战, 郑力宁, 肖波. 链轨节用钢15B36Cr的开发与试制[J]. 特殊钢, 2019, 40(2): 28-30.
[2]	曹燕光, 王毛球, 徐乐, 刘剑辉, 董瀚, 胡芳忠, 孙维. 110 t EAF-LF-RH-CC-连轧流程 Φ110 mm ~ Φ150 mm 22CrMoH齿轮钢的试制[J]. 特殊钢, 2015, 36(3): 27-29.
[3]	王勇, 冉旭, 张敏. 周期轧管工艺生产Φ508 mm x 50 mm WB36钢管的研制[J]. 特殊钢, 2011, 32(5): 60-62.
[4]	李士琦, 王忠诚, 赵宏, 刘润藻, 王玉刚. 50W1300冷轧无取向电工钢带的工业试制[J]. 特殊钢, 2007, 28(4): 45-47.
[5]	谷立功, 肖功业, 王国亮. 天津钢管集团股份有限公司T91高压锅炉钢管材的试制[J]. 特殊钢, 2007, 28(4): 58-59.
[6]	李湘凡, 孙华, 郜书忠. 高强度耐候钢SPA-H的试制[J]. 特殊钢, 2006, 27(1): 53-54.