Abstract: The production flow sheet of Φ110 〜Φ280 mm hot rolled round steel 12Crl MoVG for boiler tube (/%: 0. 08 〜0. 15C, 0. 17~0. 35Si, 0. 40 -0. 70Mn, ≤0.015P, ≤0.010S, 0. 90 〜1. 20Cr, 0. 25 ~0. 35Mo, 0. 15 -0. 30V, ≤0. 015 [Alt]) is 120 t top and bottom combined blown con verter-LF-RH-CC-Rolling process. With the process measures including to control hot metal [ As], [ Sn], [ Sb], [ Pb] and [ Bi], control converter end point [C]0. 04% 〜0. 080%, [P] ≤0. 010% and [ S] ≤0. 010%, deoxidize by aluminum iron during tapping, feed Al wire in ladle to control [ Alt] ≤0. 015%, refine by compound refining slag and some aluminum shot in LF process, control tundish liquid superheating extent 20 ~ 35 ℃, whole-shielding-cast etc, the [As] + [ Sn] + [ Sb] + [ Pb] + [ Bi] is W 0. 029%, the [P], [ S] and [Als] are respectively ≤0.011%, ≤0. 008% and ≤0. 010%, and the rating of each series inclusion is ≤1.0 to meet the technical requirement of user.

摘要： Φ110～Φ280 mm锅炉管用热轧圆钢12Crl MoVG(/%:0.08～0.15C、0.17～0.35Si、0.40～0.70Mn、≤0.015P、≤0.010S、0.90～1.20Cr、0.25～0.35Mo、0.15～0.30V、≤0.015[Alt])的生产工艺流程为120 t顶底复吹转炉-LF-RH-CC-轧制。通过控制铁水[As]、[Sn]、[Sb]、[Pb]、[Bi],控制转炉终点[C]0.04%～0.08%、[P]≤0.010%、[S]≤0.010%,出钢过程铝铁脱氧,钢包喂铝线控制[Alt]≤0.015%并用复合精炼渣和少量铝丸终脱氧,控制中间包钢水过热度20～35℃,全程保护浇注等工艺措施,使试验钢的[As]+[Sn]+[Sb]+[Pb]+[Bi]≤0.029%、[P]≤0.011%、[S]≤0.008%、[Alt]≤0.011%,各类夹杂物级别均≤1.0,满足用户的技术要求。

关键词: 高压锅炉管, 12Cr1MoVG钢, 120 t BOF-LF-RH-CC, 热轧圆钢