Hot Plasticity of Austenite Stainless Steel 15Mn-22Cr-0.56N and Effect of Rolling Process on Properties of Steel

Special Steel ›› 2008, Vol. 29 ›› Issue (1): 22-24.

Previous Articles Next Articles

Hot Plasticity of Austenite Stainless Steel 15Mn-22Cr-0.56N and Effect of Rolling Process on Properties of Steel

Zhou Yong^1，2, Lang Yuping², Rong Fan²， Liu Peiying¹

1 Faculty of Engineering and Science of Materials,Beijing University,Beijing 100083;
2 State Key Laboratory of Advanced Steel Processing and Products,Central Iron and Steel Research Institute,Beijing 100081

Received:2007-08-23 Online:2008-02-01 Published:2022-12-13
Supported by:
“973”二期基金项目(编号：2004CB619103)

奥氏体不锈钢15Mn-22Cr-0.56N的热塑性和轧制工艺对其性能的影响

周勇^1，2，郎宇平² ，荣凡 ² ，刘培英¹

1北京航空航天大学材料科学与工程学院，北京100083;
2先进钢铁流程及材料国家重点实验室钢铁研究总院，北京100081

作者简介:周勇(1982-),男，在读硕士研究生，研究方向为资源节约型不锈钢。

Abstract

Abstract: The high temperature tensile and compressing plasticity of austenite stainless steel 15Mn-22Cr-0.56N and effect of hot rolling process on structure and mechanical properties of steel have been studied by thermal simulated test and single pass 20%~60% deformation hot rolling test. Simulated steel results showed that the optimum hot plasticity zone was 1000~1150 ℃;and the hot rolling test results showed that the optimum rolling parameters of steel 15Mn-22Cr-0.56N was 40% deformation at 1000~1050 ℃ by which the steel could get higher strength and toughness.

Key words: Austenite Stainless Steel 15Mn-22Cr-0.56N, Hot Plasticity, Rolling Process, Mechanical Properties

摘要： 通过热模拟试验和20%～60%单道次变形的热轧试验研究了奥氏体不锈钢15Mn-22Cr-0.56N的高温拉伸和压缩塑性以及热轧工艺对组织和机械性能的影响。模拟试验结果表明,该钢最佳热塑性区为1000～1150℃;热轧试验结果表明,15Mn-22Cr-0.56N钢最佳轧制工艺参数为1000～1050℃、40%变形可得到较高的强韧性。

关键词: 奥氏体不锈钢15Mn-22Cr-0．56N, 热塑性, 热轧工艺, 机械性能

Zhou Yong, Lang Yuping, Rong Fan, Liu Peiying. Hot Plasticity of Austenite Stainless Steel 15Mn-22Cr-0.56N and Effect of Rolling Process on Properties of Steel[J]. Special Steel, 2008, 29(1): 22-24.

周勇, 郎宇平, 荣凡, 刘培英. 奥氏体不锈钢15Mn-22Cr-0.56N的热塑性和轧制工艺对其性能的影响[J]. 特殊钢, 2008, 29(1): 22-24.

[1]	Duan Zhengtao. Effect of Cooling and Temper-Rolling Processes on Mechanical Properties of Hot-Rolled 700 MPa Grade Nb-Ti Micro-Alloying S600MC High Strength Steel Strip [J]. Special Steel, 2022, 43(5): 92-94.
[2]	Zhang Hongliang, Feng Guanghong, Liu Xin, Chen Jilin, Wang Baoshan , Ma Jian. Optimization of Convying Connection of Continuous Casting Billet Queuing Process in Direct Rolling Process of Billet at Casting-Rolling Interface [J]. Special Steel, 2021, 42(5): 1-5.
[3]	Wu Liping , Zhi Jianguo , Liu Qing, Wang Shaobing, Zhang Jiangshan. Research and Industrialization of Hot Rolled Casing TG22 [J]. Special Steel, 2020, 41(1): 21-23.
[4]	Peng Jun, Wan Wuxia, Li Fuhua , Tang Ke. Practice of Rolling Process for Φ 158.75 mm x25.4 mm Heavy Wall Tube of Martensite Stainless Steel 420M [J]. Special Steel, 2018, 39(4): 35-37.
[5]	Xiao Aida, Li Guangqinag , Li zhaodong , Zhang Bo. Analysis on Breaking of 230 mm Casting Slab of High Ti Microalloying Low Carbon Steel and Process Improvement [J]. Special Steel, 2017, 38(1): 31-35.
[6]	Li Xiaolong , Cheng Weiguo , Zhou Lixin , Zhou Dunshi , Zou Hui. Numerical Simulation and Analysis on Hot Continuous Rolling Process of KOCKS Mill for Φ16 mm GCr15 Bearing Steel Bar [J]. Special Steel, 2016, 37(5): 5-9.
[7]	Luo Gang , Wang Huimian. Test and Study on Relative Hot Plasticity of MnS Inclusion in a New Free-Cutting Stainless Steel TBPS [J]. Special Steel, 2016, 37(2): 1-3.
[8]	Zhou Wen , Wu Kaiming , Wang Houxin , Guo Aimin , Zou Dehui , Li Shurui. Hot Plasticity of Casting Slab of Nb-Ti Microalloying High Performance Steel Q370qE-HPS for Bridge Beam at 700-1050 ℃ [J]. Special Steel, 2015, 36(5): 55-58.
[9]	Li Ququan, Yan Huicheng, Zeng Fanzheng , Liu Jian, Tang Guangbo. Effect of Metal Rheology of Gear Steel 20CrMnTiH in Rolling Process on Carbon Segregation of Casting Bloom [J]. Special Steel, 2015, 36(1): 14-16.
[10]	Cao Liqiang , He Yingying, Li Hongyou, Ma Han. Process Practice of Improvement on Cutting Quality of Low-Carbon High-Sulphur Free-Cutting Steel [J]. Special Steel, 2015, 36(1): 21-24.
[11]	Wang Yuling, Wang Zhixiang, Zhang Xiaokun, Cheng Shengwei, Wu Zhonghua. Hot Plasticity, Structure and Mechanical Properties of Steel 0.25C-1. 1Cr-O. 7Mn-0.25Mo-0.05V for High-Speed Train Axle Shaft [J]. Special Steel, 2015, 36(1): 49-51.
[12]	Wang Dongxing, Zhang Lingfeng, Zhou Songhong, Ren Yi, Zhong Rong, Cao Hui. Improvement of Centre Density of 30CrMo Steel Heavy Bar by Finite Element Simulation on Rolling Process [J]. Special Steel, 2013, 34(4): 10-12.
[13]	Wang Xiaoli, Song Bo , Zhi Jianguo, Gao Mingxing, Chen Yuan, An Shengli. Effect of RE on Hot Plasticity of V Microalloying Heavy Rail Steel [J]. Special Steel, 2012, 33(5): 45-46.
[14]	Han Le , Sun Hao , Ren Huiping , Wang Haiyan , Jin Zili. Effect of Rolling Process on Structure, Texture and Properties of X80 Pipeline Steel [J]. Special Steel, 2012, 33(2): 62-64.
[15]	Liu Xia, Shi Fengwu, Wang Xiaoli, Jiao Guoli. Influence of Vanadium on Hot Plasticity of Microalloying Heavy Rail Steel [J]. Special Steel, 2010, 31(4): 26-27.

Hot Plasticity of Austenite Stainless Steel 15Mn-22Cr-0.56N and Effect of Rolling Process on Properties of Steel

奥氏体不锈钢15Mn-22Cr-0.56N的热塑性和轧制工艺对其性能的影响

PDF

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments