Abstract: The     precipitated     phase     particles     in     ferrite-martensite     dual     phase     steel(0.08C,0.22Si,1.02Mn, 0.02Nb,0.013Ti,0.034Al)rolled  by  φ450  mill  with  control  rolling  and  cooling  process  in  laboratory  has  been  studied  by using   carbon   extraction-replica   technique.Results   showed   that   there   was(Nb,Ti)(CN)precipitates   with   size   being   doz-  ens nm  at  1200  ℃; with  energy  dispersive X-ray  spectrometer analysis,the Nb  content in  smaller particles was higher than  Ti  content  of which  the  shape  was  irregular,and  in  large  particle  of which  the  shape  was  rectangle,main  content  was  Ti  with   minor   Nb;   and   in   steel   by   control   rolling   and   cooling,the(Nb,Ti)(CN)was   interstitial   precipitated   phase   and  mainly  precipitated  at  grain-boundary.

摘要： 采用萃取复型技术研究了实验室Φ450轧机控轧控冷后铁素体-马氏体双相钢(%:0.08C、0.22Si、1.02Mn、0.02Nb、0.013Ti、0.034Al)中沉淀相粒子。结果表明,该钢在1200℃时就存在尺寸为几十纳米的(Nb,Ti) (CN),经X-射线能谱分析得出,小颗粒中Nb含量大于Ti含量,形状不规则,大颗粒沉淀相主要含Ti,Nb含量较少,呈长方形;经控轧控冷后(Nb,Ti)(CN)为间隙析出,且主要在晶界处析出。

关键词: 双相钢, 铁素体-马氏体, , 沉淀相粒子, , 萃取复型