Abstract: The macrosegregation law  of  C,S,P  and  Al  in  240  mm×240  mm  cast  billet  of  steel  40Cr(0.38  ~ 0.40C,0.90~0.91Cr,0.015～0.029P,0.009~0.014S)has    been    studied    by  the    technology    of   original    position statistic  distribution  analysis(OPA).The  study  indicated  that  with  45%～63%  equiaxial  crystal  rate  in  billet, there  has not  any  effect  of overheating temperature(5~32  ℃)of molten  steel  in tundish  on macrosegregation  of C, but there has  an obvious effect on macrosegregation of S and P. The S presents center positive segregation, P presents center negative segregation, and  low  overheating  temperature(5℃)could  not  decreases  S  and  P  segregation.Al₂O₃  inclusions  concentrated  at center of cast billet leads to Al element center positive segregation.

摘要： 应用金属原位统计分布分析技术研究了40Cr钢(%:0.38～0.40C、0.90~0.91Cr、0.015～0.029P、 0.009~0.014S)240 mm×240 mm连铸坯中C、S、P和Al的宏观偏析规律。研究表明，在铸坯45%～63%等轴晶率下中间包钢水过热度(5~32 ℃)对C的宏观偏析没有显著影响，但对S、P宏观偏析产生明显影响。S呈中心正偏析，P呈中心负偏析，低过热度(5℃)不能减轻S和P的偏析程度。Al元素中心正偏析主要是Al₂0₃夹杂向连铸坯中心聚集所致。

关键词: 连铸坯,凝固偏析, 原位统计分布分析