Abstract:  Precipitated     phases,precipitated     temperature     and     each     phase     content     in     SA508-3     steel     -0. 19C,0.01~  0.22Si,1.40~1.58Mn,0.65~0.76Ni,0.50～0.55Mo       have       been       calculated       by       using       Thermo-Calc       thermodynamic       soft- ware,and   effect   of   Si   and   Mn-Ni-Mo   content   on   precipitated   phases   in   the   steel   was   studied.   The   calculated   results   show that   main    equilibrium   precipitates    in    SA508-3    steel    are    alloying    cementite,M,C₃    and   Mo    carbide.    There    is   no    obvious effect   of   Si   content   change   on   precipitated   temperature   and   precipitated   amount   of  each   phase.   With   increasing   Mo   content the   brittle   precipitated   phases   decreased   while   there   is   not   obvious   effect   on   alloying   cementite   precipitates.   The   optimum tempering    temperature    for    SA508-3    steel    is    643~678℃.

摘要： 采用Thermo-Calc热力学软件计算了SA508-3钢(％:0．19C、0．01-0．22Si、1．40-1．58Mn、0．65- 0．76Ni、0．50-0．55Mo)的析出相、析出温度和各相的含量,并研究了Si和Mn-Ni-Mo含量对该钢析出相的影响。计算结果表明,SA508-3钢平衡态的析出相主要为合金渗碳体、M7C3及Mo的碳化物。Si含量变化对钢中各相析出温度和析出量无显著影响。随Mo含量降低,钢中脆性相析出减少,但对合金渗碳体析出无显著影响。SA508-3钢最佳回火温度为643-678℃。

关键词: SA508-3 钢, 析出相, 热力学计算