Rare Earth Inoculation Process Practice of Electroslag  Remelting M42 High Speed Steel

Wang Kai1,2, Wang Zhenyu1, Xie Zhibin1,2, Liang Jingbin1,2 ， Zhang Xuyang1   

  1. 1 Heye Science and Technology Co Ltd, Shijiazhuang 052165;
    2 Hebei High Speed Tool Steel Engineering and Technology Research Center, Shijiazhuang 052165
  • Received:2021-03-25 Online:2021-12-23 Published:2022-01-03

电渣重熔M42高速钢稀土孕育处理工艺实践

王凯1,2,王振宇1,谢志彬1,2,梁敬斌1,2,张旭阳1   

  1. 1 河冶科技股份有限公司，石家庄052165；
    2 河北省高速工具钢工程技术研究中心，石家庄052165
  • 作者简介:王 凯(1986-),男，工程师，2009年华北理工大学(本科)毕 业，工模具钢冶炼工艺研究。

PDF

Abstract: he morphology of carbides and the thermoplasticity of high speed steel can be improved by inoculating with   rare   earth.   Test   and   batch   production   results   show   that   by   20t   MIF+25tLF+25tVD+4tESR   process,as   Al 0. 12%  in  steel  in  VD  process  adding  0. 1%  lanthannm-cerium  mixed  RE  alloy  and  using  6%  REO2  slag  series  in  ESR process,the  RE  content  in  M42  steel  is  0.027%～0.038%  stably  to  obviously  improve  inclusions  morphology  and  hot plastisity  of steel.

摘要： 使用稀土对高速钢进行孕育处理可改变高速钢碳化物形貌和提高高速钢热塑性。通过20 t MIF+25 t LF+25 t VD+4 t ESR工艺试验和批量生产结果表明， 采用VD过程在钢中Al 0.12%时加0.1%镧铈混合稀土合金及ESR过程用6%REO2渣系，M42钢RE含量稳定在0.027%~0.038%，夹杂物形貌和钢的热塑性都得到明显改善。